Jung S, et al. J Adv Prosthodont. 2019 Jun;11(3):179-186. https://doi.org/10.4047/jap.2019.11.3.179

Yang H, et al. J Adv Prosthodont. 2018 Jun;10(3):184-190. https://doi.org/10.4047/jap.2018.10.3.184

The development of high-filled 3D printing resin necessitates a bonding protocol for dental indirect restorations to achieve optimal bond strength after cementation. This study evaluates shear bond strengths of high-filler 3D printed materials for permanent restorations with various surface treatments. Rodin Sculpture 1.0 (50% lithium disilicate fillers) and 2.0 Ceramic Nanohybrid (>60% zirconia and lithium disilicate fillers) were tested, with Aelite All-Purpose Body composite resin as control. Samples were prepared, post-cured, and sandblasted with alumina (25 µm). Surface roughness was analyzed using an optical profilometer. Two bonding protocols were compared. First, groups were treated with lithium disilicate silane (Porcelain Primer) or zirconia primer (Z-Prime Plus) or left untreated without a bonding agent. Beam-shaped resin cement (DuoLink Universal) specimens were bonded and stored in a 37 °C water bath. Second, additional sets of materials were coated with a bonding agent (All-Bond Universal), either followed by silane application or left untreated. These sets were then similarly stored alongside resin cement specimens. Shear bond tests were performed after 24 h. SEM images were taken after debonding. One-Way ANOVA and post hoc Duncan were performed for the statistical analysis. Rodin 1.0 exhibited increased adhesive failure with silane or zirconia primer coating, but significantly improved bond strengths with bonding agent application. Rodin 2.0 showed consistent bond strengths regardless of bonding agent application, but cohesive failure rates increased with bonding agent and filler coating. In all groups, except for Rodin 1.0 without bonding agent, silane coating increased cohesive failure rate. In conclusion, optimal shear bond strength for high-filler 3D printing materials can be achieved with silane coating and bonding agent application.

We have investigated the effect of non-thermal atmospheric pressure plasma (NTAPP) treatment and the post process time on the bonding strength and surface sterilization of dental zirconia. Presintered zirconia specimens were manufactured as discs, and then subjected to a 30-min argon treatment (Ar, 99.999%; 10 L/min) using an NTAPP device. Five post-treatment durations were evaluated: control (no treatment), P0 (immediate), P1 (24 h), P2 (48 h), and P3 (72 h). The surface characteristics, shear bonding strength (SBS) with two resin cements, and Streptococcus mutans biofilm formation of these plasma-treated dental zirconia were tested. Plasma did not change the roughness, and caused surface element changes and surface energy increase. Due to this increase in surface energy, SBS increased significantly (p < 0.05) within 48 h when RelyX^TM U200 was used. However, the increase of surface oxygen significantly decreased (p < 0.05) the SBS of Panavia F 2.0 when using plasma immediately (P0). S. mutans adhesion decreased significantly (p < 0.05) for the P0, P1, and P2 groups compared to the control. The P0 group exhibited lower biofilm thickness than the other experimental groups due to the increased hydrophilicity (p < 0.05). Our study suggests that there is a suitable time window for the post NTAPP treatment regarding bonding strength and antimicrobial growth persist.