Carbon fibres used as a honeycomb core material (subject to a proper in-depth analysis of their reinforcement patterns) allows solving the thermo-dimensional stability problem of the units for space systems. Based on the results of numerical simulations with the support of finite element analysis, the paper provides an evaluation of the accuracy of analytical dependencies for the determination of the moduli of elasticity of a carbon fibre honeycomb core in tension/compression and shear. It is shown that a carbon fibre honeycomb reinforcement pattern has a significant impact on the mechanical performance of the carbon fibre honeycomb core. For example, for honeycombs measuring 10 mm in height, the maximum shear modulus values corresponding to the reinforcement pattern of ±45° exceed the minimum values for a reinforcement pattern of 0° and 90° by more than 5 times in the XOZ plane and 4 times for the shear modulus in the YOZ plane. The maximum modulus of the elasticity of the honeycomb core in the transverse tension, corresponding to a reinforcement pattern of ±75°, exceeds the minimum modulus for the reinforcement pattern of ±15° more than 3 times. We observe a decrease in the values of the mechanical performance of the carbon fibre honeycomb core depending on its height. With a honeycomb reinforcement pattern of ±45°, the decrease in the shear modulus is 10% in the XOZ plane and 15% in the YOZ plane. The reduction in the modulus of elasticity in the transverse tension for the reinforcement pattern does not exceed 5%. It is shown that in order to ensure high-level moduli of elasticity with respect to tension/compression and shear at the same time, it is necessary to focus on a reinforcement pattern of ±64°. The paper covers the development of the experimental prototype technology that produces carbon fibre honeycomb cores and structures for aerospace applications. It is shown by experiments that the use of a larger number of thin layers of unidirectional carbon fibres provides more than a 2-time reduction in honeycomb density while maintaining high values of strength and stiffness. Our findings can permit a significant expansion of the area of application relative to this class of honeycomb cores in aerospace engineering.

Currently, prefabricated panel structures are typical products made of polymeric composite materials. The integrity of the composite panels, their structure and accuracy of making a contour are largely associated with the manifestation of residual technological stresses. The above phenomena and associated stress-strain behaviour inevitably occur in the process of moulding of the composite products. However, their value, nature, time of occurrence and dynamics of growth can be fully controlled and regulated. The paper deals with the study of the effect of moulding pressure on the quality of a composite product. A dependence is presented that allows us to determine the time for the degassing of the polymeric composite material package at the given temperature and pressure to obtain a monolithic and nonporous structure. It is shown that the peak of the maximum volatile-matter yield for the considered binder types lies in the temperature range where the degree of curing does not exceed 10%; that is, the viscosity values do not prevent the removal of volatile fractions. The effect of moulding pressure on the values of the volume content of the reinforcing material has been studied, and the dependence of the required thickness of the absorbent layer on the parameters of the package of polymer composite material and pressure has been obtained. The dependence of the required thickness of absorbent layer on the parameters of the package of polymeric composite material and pressure has been obtained. The mathematical model developed by us provides an opportunity to predict the stress-strain behaviour of a composite structure at any time during the moulding process. The model is closely related to chemo-viscous and thermal models. It allowed us to synthetize a method for choosing the rational parameters of the moulding process (temperature, pressure, and time), materials of additional layers and equipment. The experiments proved the presence of several defects, such as de-lamination of edges, waviness, swelling and poor adhesion of upper layers in the specimen of the composite panel cooled stepwise in the absence of the vacuum pressure. The surface quality of the specimen of the panel cooled stepwise under vacuum pressure was significantly better, and no visible defects were observed. The obtained theoretical values of deflections, considering the change in physic-mechanical characteristics that depend on the temperature and rheonomic properties of the material, showed an error that did not exceed 7%, compared to the experimental data. Our results can be applied at the enterprises engaged in designing and manufacturing panel structures of polymeric composite materials.

In integrated turbine wheel designs, small deviations, known as mistuning, often occur in the modal properties of individual blades due to manufacturing tolerances and material inhomogeneity. During operation, this mistuning can cause some rotor blades to be subjected to significantly higher loads than predicted for an ideal rotor. The degree of rotor mistuning can only be determined using methods of experimental modal analysis. However, the manual use of the modal hammer cannot ensure precise repeatability of the force impulse’s location and timing, leading to inaccuracies. This article introduces a mechanism that replaces manual modal hammer operations, guaranteeing consistent impact location and timing while eliminating double strikes. The device was verified on bladed discs of various sizes, and its usability is demonstrated in this article on a turbine wheel of a marine engine turbocharger. The developed mechanism automates modal hammer strikes, ensuring precisely repeatable force courses and positioning for each impact. This automation reduces the measurement time and significantly improves the accuracy. The results of this research showed that even with careful manual operation of the modal hammer by an experienced operator, statistically significant differences arise in the repeated measurements of a bladed disc mistuning, whereas with the use of the presented measuring device, the results of the repeated measurements are practically identical.