There is a long-standing puzzle concerning whether polyethylene blends are a suitable substitution for cable-insulation-used crosslinking polyethylene (XLPE) especially at elevated temperatures. In this paper, we investigate temperature dependence of mechanical, electrical properties of blends with 70 wt % linear low density polyethylene (LLDPE) and 30 wt % high density polyethylene (HDPE) (abbreviated as 70 L-30 H). Our results show that the dielectric loss of 70 L-30 H is about an order of magnitude lower than XLPE, and the AC breakdown strength is 22% higher than XLPE at 90 °C. Moreover, the dynamic mechanical thermal analysis (DMA) measurement and hot set tests suggest that the blends shows optimal mechanical properties especially at high temperature with considerable temperature stability. Further scanning electron microscope (SEM) observation and X-ray diffraction (XRD) analysis uncover the reason for the excellent high temperature performance and temperature stability, which can be ascribed to the uniform fine-spherulite structure in 70 L-30 H blends with high crystallinity sustaining at high temperature. Therefore, our findings may enable the potential application of the blends as cable insulation material with higher thermal-endurance ability.

To prepare high-permittivity composite materials for dielectrically functional gradient materials (d-FGMs) by the stereolithographic 3D-printing technique, three ceramic powders (i.e., alumina, barium titanate, and strontium titanate) are selected as functional fillers for a UV-curable resin matrix. The viscosity and UV curing depth of the uncured slurry are tested for feasibility of 3D printing. Comprehensive electrical properties, including volume resistivity, permittivity, dielectric loss, and breakdown strength of the cured composites are measured. The effects of the filler types, morphologies, particle sizes, and volume fractions on the UV curing characteristics of the slurry and dielectric properties of cured composites are systematically analyzed. The experimental results show that spherical fillers with large particle sizes, smooth surfaces, and high permittivity are conducive for reducing the slurry viscosity, increasing curing depth and adjusting the composite’s permittivity over a wide range. We believe that the proposed strategy for material system establishment can improve the 3D printability of high-permittivity composites and promote other applications of the d-FGMs by the stereolithography technique.

Nano-Ag can be prepared through ultraviolet radiation reduction reaction and then the influence on nano-Ag particles by protecting agent, intensity of radiation and mixture ration is studied. The TEM result shows that Ag particles are dispersed evenly and the particle size is about 20 nm. Nano-dielectric with nano-Ag in epoxy resin is prepared successfully. The dielectric property of the composite is discussed. The result is that resistivity (rho_v) and breakdown electric-field intensity (E_b) in room temperature of the composite are improved; the dielectric loss (tandelta) is reduced and the permittivity (epsiv_r) changes little. It can be seen that the dielectric property of base polymer material is improved by adding nano-Ag particles. This phenomenon is explained by Coulomb block effect