Silicon carbide (SiC) is a compound semiconductor, which is considered as a possible alternative to silicon for particles and photons detection. Its characteristics make it very promising for the next generation of nuclear and particle physics experiments at high beam luminosity. Silicon Carbide detectors for Intense Luminosity Investigations and Applications (SiCILIA) is a project starting as a collaboration between the Italian National Institute of Nuclear Physics (INFN) and IMM-CNR, aiming at the realization of innovative detection systems based on SiC. In this paper, we discuss the main features of silicon carbide as a material and its potential application in the field of particles and photons detectors, the project structure and the strategies used for the prototype realization, and the first results concerning prototype production and their performance.

In this review paper, several new approaches about the 3C-SiC growth are been presented. In fact, despite the long research activity on 3C-SiC, no devices with good electrical characteristics have been obtained due to the high defect density and high level of stress. To overcome these problems, two different approaches have been used in the last years. From one side, several compliance substrates have been used to try to reduce both the defects and stress, while from another side, the first bulk growth has been performed to try to improve the quality of this material with respect to the heteroepitaxial one. From all these studies, a new understanding of the material defects has been obtained, as well as regarding all the interactions between defects and several growth parameters. This new knowledge will be the basis to solve the main issue of the 3C-SiC growth and reach the goal to obtain a material with low defects and low stress that would allow for realizing devices with extremely interesting characteristics.

Emerging wide bandgap semiconductor devices such as the ones built with SiC have the potential to revolutionize the power electronics industry through faster switching speeds, lower losses, and higher blocking voltages, which are superior to standard silicon-based devices. The current epitaxial technology enables more controllable and less defective large area substrate growth for the hexagonal polymorph of SiC (4H-SiC) with respect to the cubic counterpart (3C-SiC). However, the cubic polymorph exhibits superior physical properties in comparison to its hexagonal counterpart, such as a narrower bandgap (2.3 eV), possibility to be grown on a silicon substrate, a reduced density of states at the SiC/SiO₂ interface, and a higher channel mobility, characteristics that are ideal for its incorporation in metal oxide semiconductor field effect transistors. The most critical issue that hinders the use of 3C-SiC for electronic devices is the high number of defects in bulk and epilayers, respectively. Their origin and evolution are not understood in the literature to date. In this manuscript, we combine ab initio calibrated Kinetic Monte Carlo calculations with transmission electron microscopy characterization to evaluate the evolution of extended defects in 3C-SiC. Our study pinpoints the atomistic mechanisms responsible for extended defect generation and evolution, and establishes that the antiphase boundary is the critical source of other extended defects such as single stacking faults with different symmetries and sequences. This paper showcases that the eventual reduction of these antiphase boundaries is particularly important to achieve good quality crystals, which can then be incorporated in electronic devices.

This work describes the development of a new method for ion implantation induced crystal damage recovery using multiple XeCl (308 nm) laser pulses with a duration of 30 ns. Experimental activity was carried on single phosphorus (P) as well as double phosphorus and aluminum (Al) implanted 4H-SiC epitaxial layers. Samples were then characterized through micro-Raman spectroscopy, Photoluminescence (PL) and Transmission Electron Microscopy (TEM) and results were compared with those coming from P implanted thermally annealed samples at 1650–1700–1750 °C for 1 h as well as P and Al implanted samples annealed at 1650 °C for 30 min. The activity outcome shows that laser annealing allows to achieve full crystal recovery in the energy density range between 0.50 and 0.60 J/cm². Moreover, laser treated crystal shows an almost stress-free lattice with respect to thermally annealed samples that are characterized by high point and extended defects concentration. Laser annealing process, instead, allows to strongly reduce carbon vacancy (V_C) concentration in the implanted area and to avoid intra-bandgap carrier recombination centres. Implanted area was almost preserved, except for some surface oxidation processes due to oxygen leakage inside the testing chamber. However, the results of this experimental activity gives way to laser annealing process viability for damage recovery and dopant activation inside the implanted area.

In this work, results related to the temperature influence on the homo-epitaxial growth process of 3C-SiC is presented. The seed for the epitaxial layer was obtained by an innovative technique based on silicon melting: after the first step of the hetero-epitaxial growth process of 3C-SiC on a Si substrate, Si melts, and the remaining freestanding SiC layer was used as a seed layer for the homo-epitaxial growth. Different morphological analyses indicate that the growth temperature and the growth rate play a fundamental role in the stacking faults density. In details, X-ray diffraction and micro-Raman analysis show the strict relationship between growth temperature, crystal quality, and doping incorporation in the homo-epitaxial chemical vapor deposition CVD growth process of a 3C-SiC wafer. Furthermore, photoluminescence spectra show a considerable reduction of point defects during homo-epitaxy at high temperatures.