Nanoparticles of NiLa_xFe_2−xO₄ ferrite spinel incorporated in a SiO₂ matrix were synthesized via a sol-gel method, followed by annealing at 200, 500, and 800 °C. The resulting materials were characterized via XRD, AFM, and BET techniques and evaluated for photocatalytic activity. The XRD diffractograms validate the formation of a single-phase cubic spinel structure at all temperatures, without any evidence of secondary peaks. The size of crystallites exhibited a decrease from 37 to 26 nm with the substitution of Fe³⁺ with La³⁺ ions. The lattice parameters and crystallite sizes were found to increase with the rise in La³⁺ content and annealing temperature. Isotherms were employed to calculate the rate constants for the decomposition of malonate precursors to ferrites and the activation energy for each ferrite. All nanocomposites have pores within the mesoporous range, with a narrow dispersion of pore sizes. The impact of La content on sonophotocatalytic activity was evaluated by studying Rhodamine B degradation under visible light irradiation. The results indicate that the introduction of La enhances nanocomposite performance. The prepared Ni-La ferrites may have potential application for water decontamination.

The electrospun nanosystems containing poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) and 1 wt% Fe doped ZnO nanoparticles (NPs) (with the content of dopant in the range of 0–1 wt% Fe) deposited onto polylactic acid (PLA) film were prepared for food packaging application. They were investigated by scanning electron microscopy (SEM), energy dispersive X-ray (EDX), Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), antimicrobial analysis, and X-ray photoelectron spectrometry (XPS) techniques. Migration studies conducted in acetic acid 3% (wt/wt) and ethanol 10% (v/v) food simulants as well as by the use of treated ashes with 3% HNO₃ solution reveal that the migration of Zn and Fe falls into the specific limits imposed by the legislation in force. Results indicated that the PLA/PHBV/ZnO:Fex electrospun nanosystems exhibit excellent antibacterial activity against the Pseudomonas aeruginosa (ATCC-27853) due to the generation of a larger amount of perhydroxyl (˙OOH) radicals as assessed using electron paramagnetic resonance (EPR) spectroscopy coupled with a spin trapping method.

Our study is focused on the structural and morphological characteristics, optical behaviour and photocatalytic properties of undoped and 5 at% Eu³⁺-, Gd³⁺- and Y³⁺-doped CeO₂ nanoparticles prepared by a green hybrid sol-gel combustion method. Several techniques such as X-ray diffraction powder (XRD), Transmission Electron Microscopy (TEM), UV-Vis spectroscopy, Photoluminescence spectroscopy (PL) and Electron Paramagnetic Resonance (EPR) have been used to investigate the obtained samples. Moreover, the correlation between the characteristics and properties has been studied. The nanoparticles observed by TEM exhibit a pseudo-spherical shape, except for Y³⁺-doped CeO₂, which presents an acicular shape. The average size of undoped and rare-earth-doped CeO₂ nanoparticles is below 10 nm, in good agreement with the calculations performed based on XRD analyses. From UV-Vis analyses it has been deduced that with doping the band gap energy decreases, which shows that additional levels are introduced by doping into the CeO₂ band gap. The EPR spectra evidence similar behaviour for all doped samples. The photocatalytic activity was evaluated by the degradation of rhodamine B (RhB) under UV light irradiation. The photodegradation mechanism has been studied in depth based on the formation of electron-hole pairs, and to evidence the reactive oxygen species, ESR coupled with spin-trapping experiments was performed. In the case of Y-doped CeO₂ nanoparticles, the generation of both •OOH and •${\mathrm{O}}_2^{-}$ radicals involved in RhB photodegradation was highlighted.