A smart meta-superconductor Bi(Pb)SrCaCuO (B(P)SCCO) may increase the critical transition temperature (T_C) of B(P)SCCO by electroluminescence (EL) energy injection of inhomogeneous phases. However, the increase amplitude ΔT_C ($\mathsf{\Delta }{T}_C=T_C-T_{C,pure}$) of T_C is relatively small. In this study, a smart meta-superconductor B(P)SCCO with different matrix sizes was designed. Three kinds of raw materials with different particle sizes were used, and different series of Y₂O₃:Sm³⁺, Y₂O₃, Y₂O₃:Eu³⁺, and Y₂O₃:Eu³⁺+Ag-doped samples and pure B(P)SCCO were prepared. Results indicated that the T_C of the Y₂O₃ or Y₂O₃:Sm³⁺ non-luminescent dopant doping sample is lower than that of pure B(P)SCCO. However, the T_C of the Y₂O₃:Eu³⁺+Ag or Y₂O₃:Eu³⁺ luminescent inhomogeneous phase doping sample is higher than that of pure B(P)SCCO. With the decrease of the raw material particle size from 30 to 5 μm, the particle size of the B(P)SCCO superconducting matrix in the prepared samples decreases, and the doping content of the Y₂O₃:Eu³⁺+Ag or Y₂O₃:Eu³⁺ increases from 0.2% to 0.4%. Meanwhile, the increase of the inhomogeneous phase content enhances the ΔT_C. When the particle size of raw material is 5 μm, the doping concentration of the luminescent inhomogeneous phase can be increased to 0.4%. At this time, the zero-resistance temperature and onset transition temperature of the Y₂O₃:Eu³⁺+Ag doped sample are 4 and 6.3 K higher than those of pure B(P)SCCO, respectively.

The smart meta-superconductor MgB₂ and Bi(Pb)SrCaCuO increase the superconducting transition temperature (T_C), but the changes in the transport critical current density (J_C) and Meissner effect are still unknown. Here, we investigated the J_C and Meissner effect of smart meta-superconductor MgB₂ and Bi(Pb)SrCaCuO. The use of the standard four-probe method shows that Y₂O₃:Eu³⁺ and Y₂O₃:Eu³⁺+Ag inhomogeneous phase significantly increase the J_C, and J_C decreases to a minimum value at a higher temperature. The Meissner effect was measured by direct current magnetization. The doping of Y₂O₃:Eu³⁺ and Y₂O₃:Eu³⁺+Ag luminescent inhomogeneous phase causes a Meissner effect of MgB₂ and Bi(Pb)SrCaCuO at a higher temperature, while the non-luminescent dopant reduces the temperature at which samples have Meissner effect. The introduction of luminescent inhomogeneous phase in conventional MgB₂ and copper oxide high-temperature Bi(Pb)SrCaCuO superconductor increases the T_C and J_C, and Meissner effect is exerted at higher temperature. Therefore, smart meta-superconductivity is suitable for conventional and copper oxide high-temperature superconductors.

Superconducting materials exhibit unique physical properties and have great scientific value and vast industrial application prospects. However, due to limitations, such as the critical temperature (T_C) and critical current density (J_C), the large-scale application of superconducting materials remains challenging. Chemical doping has been a commonly used method to enhance the superconductivity of B(P)SCCO. However, satisfactory enhancement results have been difficult to achieve. In this study, we introduce green-light GaN p-n junction particles as inhomogeneous phases into B(P)SCCO polycrystalline particles to form a smart meta-superconductor (SMSC) structure. Based on the electroluminescence properties of the p-n junction, the Cooper pairs were stimulated and strengthened to enhance the superconductivity of B(P)SCCO. The experimental results demonstrate that the introduction of inhomogeneous phases can indeed enhance the critical temperature T_C, critical current density J_C, and complete diamagnetism (Meissner effect) of B(P)SCCO superconductors. Moreover, when the particle size of the raw material of B(P)SCCO is reduced from 30 to 5 μm, the grain size of the sintered samples also decreases, and the optimal doping concentration of the inhomogeneous phases increases from 0.15 wt.% to 0.2 wt.%, further improving the superconductivity.

Increasing and improving the critical transition temperature (T_C), current density (J_C) and the Meissner effect (H_C) of conventional superconductors are the most important problems in superconductivity research, but progress has been slow for many years. In this study, by introducing the p-n junction nanostructured electroluminescent inhomogeneous phase with a red wavelength to realize energy injection, we found the improved property of smart meta-superconductors MgB₂, the critical transition temperature T_C increases by 0.8 K, the current density J_C increases by 37%, and the diamagnetism of the Meissner effect H_C also significantly improved, compared with pure MgB₂. Compared with the previous yttrium oxide inhomogeneous phase, the p-n junction has a higher luminescence intensity, a longer stable life and simpler external field requirements. The coupling between superconducting electrons and surface plasmon polaritons may be explained by this phenomenon. The realization of smart meta-superconductor by the electroluminescent inhomogeneous phase provides a new way to improve the performance of superconductors.

As a highly regarded superconducting material with a concise layered structure, MgB₂ has attracted significant scientific attention and holds vast potential for applications. However, its limited current-carrying capacity under high magnetic fields has greatly hindered its practical use. To address this issue, we have enhanced the superconducting performance of MgB₂ by incorporating inhomogeneous phase nanostructures of p-n junctions with electroluminescent properties. Through temperature-dependent measurements of magnetization, electronic specific heat, and Hall coefficient under various magnetic fields, we have confirmed the crucial role of inhomogeneous phase electroluminescent nanostructures in improving the properties of MgB₂. Experimental results demonstrate that the introduction of electroluminescent inhomogeneous phases effectively enhances the superconducting performance of MgB₂. Moreover, by controlling the size of the electroluminescent inhomogeneous phases and optimizing grain connectivity, density, and microstructural uniformity, we can further improve the critical temperature (T_C) and flux-pinning capability of MgB₂ superconducting materials. Comprehensive studies on the physical properties of MgB₂ superconducting structures added with p-n junction electroluminescent inhomogeneous phases also confirm the general effectiveness of electroluminescent inhomogeneous phases in enhancing the performance of superconducting materials.