Additive manufacturing (AM), also known as three-dimensional (3D) printing, allows the fabrication of complex parts, which are impossible or very expensive to produce using traditional processes. That is the case for dinnerware and artworks (stoneware, porcelain and clay-based products). After the piece is formed, the greenware is fired at high temperatures so that these pieces gain its mechanical strength and aesthetics. The conventional (gas or resistive heating elements) firing usually requires long heating cycles, presently requiring around 10 h to reach temperatures as high as 1200 °C. Searching for faster processes, 3D-printed stoneware were fired using microwave (MW) radiation. The pieces were fired within 10% of the conventional processing time. The temperature were controlled using a pyrometer and monitored using Process Temperature Control Rings (PTCRs). An error of 1.25% was calculated between the PTCR (1207 ± 15 °C) and the pyrometer (1200 °C). Microwave-fast-fired pieces show similar mechanical strength to the references and to the electrically fast-fired pieces (41, 46 and 34 (N/mm²), respectively), presenting aesthetic features closer to the reference. Total porosities of ~4%, ~5% and ~9% were determined for microwave, electrically fast-fired and reference samples. Numerical studies have shown to be essential to better understand and improve the firing process using microwave radiation. In summary, microwave heating can be employed as an alternative to stoneware conventional firing methods, not compromising the quality and features of the processed pieces, and with gains in the heating time.

In fused deposition modeling (FDM), the cooling history impacts the bonding between filaments and layers. The existence of thermal gradients can cause non-homogeneous properties and localized stress points that may affect the individual filaments, resulting in distortion and detachment. Thermal analysis can aid in understanding the manufacturing flaw, providing necessary tools for the optimization of the printing trajectory. The present work is intended to deepen understanding of the thermal phenomena occurring during the extrusion of polymeric materials, aiming at more efficient three-dimensional (3D) printing methods. A one-dimensional (1D) finite differential method was implemented using MATLAB to simulate the temperature evolution of an extruded filament, and the results were compared with two-dimensional (2D) COMSOL Multiphysics simulations, and experimentally validated using infrared thermography. Acrylonitrile–butadiene–styrene (ABS) was used as a test material. The energy dissipation includes forced convection and radiation heat losses to the surrounding medium.