This study aims at showing the potential of additive manufacturing as a new processing route for designing future insulators in the building sector. Polycarbonate (PC) is studied as a possible candidate for designing these new insulators. This polymer offers several advantages, among them fire resistance and stability of its physical properties at high temperatures. The 3D printing of PC is attempted using fused deposition modelling technology. The printing temperature and infill rate are varied to achieve optimal mechanical and thermal characteristics. The results show that an optimal printing temperature of 280 °C is needed to achieve high tensile performance. In addition, thermal properties including thermal conductivity and effusivity increase with the increase of the infill rate in opposition to the thermal diffusivity decrease.

This study was aimed at considering the potential of wood-based composites processed using additive manufacturing as insulators in the building sector. A polylactic acid blend with 30% wood particles was used as a feedstock material in fused filament technology. Its thermal and mechanical properties were determined for various processing conditions, including printing temperature and infill rate. The results showed a minor contraction in its tensile performance as a result of the printing process. The printing temperature had a negligible effect on its stiffness and a limited influence on the other engineering constants, such as the tensile strength and ultimate stress. The thermal properties of printed structures have been found to significantly depend on the infill rate. Although the tested 3D printed wood-PLA material exhibited good thermal properties, which were tuneable using the printing conditions, its performance was still 38% to 57% lower compared to insulators such as the glass wool of the synthetic foams used in the building sector.