Polyethylene terephthalate glycol (PETG) is a thermoplastic formed by polyethylene terephthalate (PET) and ethylene glycol and known for his high impact resistance and ductility. The printability of PETG for fused deposition modelling (FDM) is studied by monitoring the filament temperature using an infra-red camera. The microstructural arrangement of 3D printed PETG is analysed by means of X-ray micro-tomography and tensile performance is investigated in a wide range of printing temperatures from 210 °C to 255 °C. A finite element model is implemented based on 3D microstructure of the printed material to reveal the deformation mechanisms and the role of the microstructural defects on the mechanical performance. The results show that PETG can be printed within a limited range of printing temperatures. The results suggest a significant loss of the mechanical performance due to the FDM processing and particularly a substantial reduction of the elongation at break is observed. The loss of this property is explained by the inhomogeneous deformation of the PETG filament. X-ray micro-tomography results reveal a limited amount of process-induced porosity, which only extends through the sample thickness. The FE predictions point out the combination of local shearing and inhomogeneous stretching that are correlated to the filament arrangement within the plane of construction.

The microstructure and mechanical performance of wood-based filament is investigated in the case of Fused Deposition Modelling (FDM) technique using experimental and numerical approaches. The printing process of wood-PLA/PHA is conducted by varying the printing temperature, typically from 210 °C to 250 °C. The filament temperature during the laying down is measured using infra-red camera to study the thermal cycling. In addition, X-ray micro-tomography is used to evaluate the material arrangement of printed wood-PLA/PHA at different length scales. Tensile experiments are performed to rank the loss in mechanical performance with respect to the filament properties. Finally, finite element computation is considered to predict the tensile behaviour based on the implementation of the real 3D microstructure issued from X-ray micro-tomography. The results show that the wood-based filament is printable over a wide range of temperatures and exhibits a marked heat accumulation tendency at high printing temperatures. However, the limited gain in tensile performance at these temperatures makes 220 °C an optimal choice for printing wood-based filament. The elongation at break of 3D-printed wood-PLA/PHA is remarkably similar to the results observed for the filament. Finite element computation reveals that despite this apparent similarity, the associated deformation mechanisms are different.

This study aims at showing the potential of additive manufacturing as a new processing route for designing future insulators in the building sector. Polycarbonate (PC) is studied as a possible candidate for designing these new insulators. This polymer offers several advantages, among them fire resistance and stability of its physical properties at high temperatures. The 3D printing of PC is attempted using fused deposition modelling technology. The printing temperature and infill rate are varied to achieve optimal mechanical and thermal characteristics. The results show that an optimal printing temperature of 280 °C is needed to achieve high tensile performance. In addition, thermal properties including thermal conductivity and effusivity increase with the increase of the infill rate in opposition to the thermal diffusivity decrease.

This study was aimed at considering the potential of wood-based composites processed using additive manufacturing as insulators in the building sector. A polylactic acid blend with 30% wood particles was used as a feedstock material in fused filament technology. Its thermal and mechanical properties were determined for various processing conditions, including printing temperature and infill rate. The results showed a minor contraction in its tensile performance as a result of the printing process. The printing temperature had a negligible effect on its stiffness and a limited influence on the other engineering constants, such as the tensile strength and ultimate stress. The thermal properties of printed structures have been found to significantly depend on the infill rate. Although the tested 3D printed wood-PLA material exhibited good thermal properties, which were tuneable using the printing conditions, its performance was still 38% to 57% lower compared to insulators such as the glass wool of the synthetic foams used in the building sector.

Few studies have reported the performance of Polylactic acid (PLA) flax feedstock composite for additive manufacturing. In this work, we report a set of experiments conducted by fused filament technology on PLA and PLA-flax with the aim of drawing a clear picture of the potential of PLA-flax as a feedstock material. Nozzle and bed temperatures are both combined with the printing angle to investigate their influence on structural and mechanical properties. The study shows a low sensitivity of PLA-flax to process parameters compared to PLA. A varied balance between shearing and uniaxial deformation is found consistent with tensile results where filament crossing at −45/+45° provides the optimal load-bearing capabilities. However, Scanning Electron Microscopy (SEM) and high-speed camera recording shows a limiting reinforcing effect of flax fibre due to the presence of intra-filament porosity and a significant amount of fibre pull-out resulting from the tensile loading. These results suggest that the quality of the bond between PLA matrix and flax fibre, intra-filament porosity, and surface roughness should receive more attention as well as the need for more continuous fibre reinforcement in PLA filaments to optimise the performance of PLA-flax printed materials.

The influence of the microstructural arrangement of 3D-printed polylactic acid (PLA) on its mechanical properties is studied using both numerical and experimental approaches. Thermal cycling during the laying down of PLA filament is investigated through infra-red measurements for different printing conditions. The microstructure induced by 3D printing is determined using X-ray micro-tomography. The mechanical properties are measured under tensile testing conditions. Finite element computation is considered to predict the mechanical performance of 3D-printed PLA by converting the acquired 3D images into structural meshes. The results confirm the leading role of the printing temperature on thermal cycling during the laying down process. In addition, the weak influence of the printing temperature on the stiffness of 3D-printed PLA is explained by the relatively small change in porosity content. However, the influence of the printing temperature on the ultimate properties is found to be substantial. This major influence is explained from finite element predictions as an effect of pore connectivity which is found to be the control factor for tensile strength.