Wood-plastic composites (WPCs) made by selective laser sintering (SLS) approach of 3D printing offer many advantages over single polymer materials, such as low cost, sustainability, and better sintering accuracy. However, WPCs made via SLS are too weak to have widespread applications. In order to increase the mechanical properties of WPCs, a novel type of WPCs containing 0, 0.05, 0.1 and 0.15 wt % carbon nanotubes (CNT), 14 wt % wood fibers, 86 wt % polyether sulfone (PES) was manufactured via SLS. The experimental results showed that the addition of small amount of CNTs can significantly increase the mechanical properties of the wood/PES composite material. The tensile strength, bending strength, and elasticity modulus were 76.3%, 227.9%, and 128.7% higher with 0.1 wt % CNTs than those without CNTs. The mechanical properties of specimens first increased and then decreased with the addition of CNTs. The SEM results of the specimens’ fracture morphology indicate that the preferable bonding interfaces between wood flour grains and PES grains were achieved by adding CNTs to the composites. There are two reasons why the composites possessed superior mechanical properties: CNTs facilitate the laser sintering process of WPCs due to their thermal conductivities, and CNTs directly reinforce WPCs.

Z-pinning can significantly improve the interlaminar shear properties of carbon fiber-reinforced aluminum matrix composites (Cf/Al). However, the effect of the metal z-pin on the in-plane properties of Cf/Al is unclear. This study examines the effect of the z-pin on the flexural strength and failure mechanism of Cf/Al composites with different volume contents and diameters of the z-pins. The introduction of a z-pin leads to the formation of a brittle phase at the z-pin/matrix interface and microstructural damage such as aluminum-rich pockets and carbon fiber waviness, thereby resulting in a reduction of the flexural strength. The three-point flexural test results show that the adding of a metal z-pin results in reducing the Cf/Al composites’ flexural strength by 2–25%. SEM imaging of the fracture surfaces revealed that a higher degree of interfacial reaction led to more cracks on the surface of the z-pin. This crack-susceptible interface layer between the z-pin and the matrix is likely the primary cause of the reduction of the flexural strength.

This paper presents the effect of through-thickness reinforcement by steel z-pins on the interlaminar shear properties and strengthening mechanisms of carbon fiber reinforced aluminum matrix composites (Cf/Al) with a short beam shear test method. Microstructural analysis reveals that z-pins cause minor microstructural damage including to fiber waviness and aluminum-rich regions, and interface reaction causes a strong interface between the stainless steel pin and the aluminum matrix. Z-pinned Cf/Al composites show reduced apparent interlaminar shear strength due to a change in the failure mode compared to unpinned specimens. The changed failure mode could result from decreased flexural strength due to microstructural damage as well as increased actual interlaminar shear strength. Fracture work is improved significantly with a z-pin diameter. The strong interface allows the deformation resistance of the steel pin to contribute to the crack bridging forces, which greatly enhances the interlaminar shear properties.

A new type of low cost, environmentally friendly wood-plastic composites (WPC) containing carbon nanotubes(CNT)of low content 0%, 0.05wt%, 0.1wt% and 0.15wt%, wood fibers of 14wt% and polymer PES of 86wt% was manufactured by the selective laser sintering (SLS) approach of 3D printing. The experimental results showed that the incorporating of CNTs could obviously increase the mechanical properties of the wood/PES composites material. The tensile strength, bending strength and elasticity modulus were 76.3%, 227.9% and 128.7% higher with 0.1wt% CNTs than without CNTs. And the mechanical properties of specimens firstly increased and then decreased with the increasing contents of CNTs. The SEM results of the specimens’ fracture morphology indicated that the preferable bonding interfaces between wood flour grains and PES grains were achieved by adding CNTs to the composites. There are two reasons to explain why the composites possessed the superior mechanical properties: CNTs could facilitate the laser sintering process of wood plastic composites due to their thermal conductivities; also, CNTs could directly reinforce the WPC composites as reinforcement.

Inside a scanning electron microscope (SEM) chamber, we performed an in situ interlaminar shear test on a z-pinned carbon fiber-reinforced aluminum matrix composite (Cf/Al) fabricated by the pressure the infiltration method to understand its failure mechanism. Experiments show that introducing a stainless-steel z-pin increases the interlaminar shear strength of Cf/Al composite by 148%. The increase in interlaminar shear strength is attributed to the high strength of the stainless-steel z-pin and the strong bonding between the z-pin and the matrix. When the z-pin/matrix interface failed, the z-pin can still experience large shear deformation, thereby enhancing delamination resistance. The failure mechanism of composite includes interfacial debonding, aluminum plough, z-pin shear deformation, frictional sliding, and fracture. These results in this study will help us understand the interlaminar strengthening mechanism of z-pins in the delamination of metal matrix composites.