Currently, protective clothing used in clinical field is the most representative example of efforts to reduce radiation exposure to radiation workers. However, lead is classified as a substance harmful to the human body that can cause lead poisoning. Therefore, research on the development of lead-free radiation shielding bodies is being conducted. In this study, the shielding body was manufactured by changing the size, layer, and height of the nozzle, using a 90.7% pure tungsten filament, a 3D printer material, and we compared its performance with existing protection tools. Our findings revealed that the shielding rate of the mixed tungsten filament was higher than that of the existing protective tools, confirming its potency to replace lead as the most protective material in clinical field.

We recently developed a long-length detector that combines three detectors and successfully acquires whole-body X-ray images. Although the developed detector system can efficiently acquire whole-body images in a short time, it may show problems with diagnostic performance in some areas owing to the use of high-energy X-rays during whole-spine and long-length examinations. In particular, during examinations of relatively thin bones, such as ankles, with a long-length detector, the image quality deteriorates because of an increase in X-ray transmission. An additional filter is primarily used to address this limitation, but this approach imposes a higher load on the X-ray tube to compensate for reductions in the radiation dose and the problem of high manufacturing costs. Thus, in this study, a newly designed additional filter was fabricated using 3D printing technology to improve the applicability of the long-length detector. Whole-spine anterior–posterior (AP), lateral, and long-leg AP X-ray examinations were performed using 3D-printed additional filters composed of 14 mm thick aluminum (Al) or 14 mm thick Al + 1 mm thick copper (Cu) composite material. The signal-to-noise ratio (SNR), contrast-to-noise ratio (CNR), and radiation dose for the acquired X-ray images were evaluated to demonstrate the usefulness of the filters. Under all X-ray inspection conditions, the most effective data were obtained when the composite additional filter based on a 14 mm thick Al + 1 mm thick Cu material was used. We confirmed that an SNR improvement of up to 46%, CNR improvement of 37%, and radiation dose reduction of 90% could be achieved in the X-ray images obtained using the composite additional filter in comparison to the images obtained with no filter. The results proved that the additional filter made with a 3D printer was effective in improving image quality and reducing the radiation dose for X-ray images obtained using a long-length detector.