Nanostructured bainite is a novel ultra-high-strength steel-concept under intensive current research, in which the optimization of its mechanical properties can only come from a clear understanding of the parameters that control its ductility. This work reviews first the nature of this composite-like material as a product of heat treatment conditions. Subsequently, the premises of ductility behavior are presented, taking as a reference related microstructures: conventional bainitic steels, and TRIP-aided steels. The ductility of nanostructured bainite is then discussed in terms of work-hardening and fracture mechanisms, leading to an analysis of the three-fold correlation between ductility, mechanically-induced martensitic transformation, and mechanical partitioning between the phases. Results suggest that a highly stable/hard retained austenite, with mechanical properties close to the matrix of bainitic ferrite, is advantageous in order to enhance ductility.

The thermal stability of nanostructured microstructures consisting of a mixture of bainitic ferrite and carbon-enriched retained austenite has been studied in two steels containing 0.6 C (wt %) by tempering cycles of 1 h at temperatures ranging from 450 to 650 °C. Volume changes due to microstructural transformations during thermal treatments were measured by high-resolution dilatometry. The correlation of these results with the detailed microstructural characterization performed by X-ray diffraction and scanning electron microscope examination showed a sequence of different decomposition events beginning with the precipitation of very fine cementite particles. This precipitation, which starts in the austenite thin films and then continues in retained austenite blocks, decreases the carbon content in this phase so that fresh martensite can form from the low-carbon austenite on cooling to room temperature. In a subsequent tempering stage, the remaining austenite decomposes into ferrite and cementite, and due to carbide precipitation, the bainitic ferrite loses its tetragonality, its dislocation density is reduced, and the bainitic laths coarsen.

High silicon (>1.5%) steels with different compositions were isothermally transformed to bainite at 220 and 250 °C to produce what is often referred to as nanostructured bainite. Interrupted tensile tests were carried out and the retained austenite was measured as a function of strain. Results were correlated with tensile ductility. The role of retained austenite stability is remarkably underlined as strongly affecting the propensity to brittle failure, but also the tensile ductility. A simple quantitative relationship is proposed that clearly delimitates the different behaviours (brittle/ductile) and correlates well with the measured ductility. Conclusions are proposed as to the role of retained austenite fraction and the existence of a threshold value associated with tensile rupture.

The recently developed nanobainitic steels show high strength as well as high ductility. Although this combination seems to be promising for fatigue design, fatigue properties of nanostructured bainitic steels are often surprisingly low. To improve the fatigue behavior, an understanding of the correlation between the nanobainitic microstructure and the fatigue limit is fundamental. Therefore, our hypothesis to predict the fatigue limit was that the main function of the microstructure is not necessarily totally avoiding the initiation of a fatigue crack, but the microstructure has to increase the ability to decelerate or to stop a growing fatigue crack. Thus, the key to understanding the fatigue behavior of nanostructured bainite is to understand the role of the microstructural features that could act as barriers for growing fatigue cracks. To prove this hypothesis, we carried out fatigue tests, crack growth experiments, and correlated these results to the size of microstructural features gained from microstructural analysis by light optical microscope and EBSD-measurements. Finally, we were able to identify microstructural features that influence the fatigue crack growth and the fatigue limit of nanostructured bainitic steels.