The effect of extended H₂ sorption cycles on the structure and on the hydrogen storage performances of MgH₂ powders with 5 wt% of Fe particle catalyst is reported. MgH₂ powders with and without Fe have been ball milled under Argon, the doped MgH₂ nanocomposite has been cycled under hydrogen pressure up to a maximum of 47 desorption and absorption cycles at 300 °C. After acceleration during the first 10 cycles, the kinetics behavior of doped MgH₂ is constant after extended cycling, in terms of maximum storage capacity and rate of sorption. The major effect of cycling on particle morphology is the progressive extraction of Mg from the MgO shell surrounding the powder particles. The Mg extraction from the MgO shell leaves the catalyst particles inside the hydride particles. Many empty MgO shells are observed in the pure ball milled MgH₂ upon cycling at higher temperature, suggesting that this enhancement of the extraction efficiency is related to the higher operating temperature which favors Mg diffusivity with respect to the H ion one.

For the few past decades, study of new hydrogen storage materials has been captivating scientists worldwide. Magnesium hydride, MgH₂, is considered one of the most promising materials due to its low cost, high hydrogen capacity, reversibility and the abundance of Mg. However, it requires further research to improve its hydrogen storage performance as it has some drawbacks such as poor dehydrogenation kinetic, high operational temperature, which limit its practical application. In this study, we introduce an overview of recent progress in improving the hydrogen storage performance of MgH₂ by the addition of titanium-based additives, which are one of the important groups of additives. The role of Ti-based additive hydrides, oxides, halides, carbides and carbonitrides are overviewed. In addition, the existing challenges and future perspectives of Mg-based hydrides are also discussed.

The inter-critically reheated grain coarsened heat affected zone (IC GC HAZ) has been reported as one of the most brittle section of high-strength low-alloy (HSLA) steels welds. The presence of micro-alloying elements in HSLA steels induces the formation of microstructural constituents, capable to improve the mechanical performance of welded joints. Following double welding thermal cycle, with second peak temperature in the range between Ac1 and Ac3, the IC GC HAZ undergoes a strong loss of toughness and fatigue resistance, mainly caused by the formation of residual austenite (RA). The present study aims to investigate the behavior of IC GC HAZ of a S355 steel grade, with the addition of different vanadium contents. The influence of vanadium micro-alloying on the microstructural variation, RA fraction formation and precipitation state of samples subjected to thermal cycles experienced during double-pass welding was reported. Double-pass welding thermal cycles were reproduced by heat treatment using a dilatometer at five different maximum temperatures of the secondary peak in the inter-critical area, from 720 °C to 790 °C. Although after the heat treatment it appears that the addition of V favors the formation of residual austenite, the amount of residual austenite formed is not significant for inducing detrimental effects (from the EBSD analysis the values are always less than 0.6%). Moreover, the precipitation state for the variant with 0.1 wt.% of V (high content) showed the presence of vanadium rich precipitates with size smaller than 60 nm of which, more than 50% are smaller than 15 nm.

Opuntia cladodes are a typical vegetable waste, from which mucilage in gel form can be extracted. This work proposes blending it with a self-produced thermoplastic starch (TPS), originating from potato starch with a high content in glycerol (ca. 30%). Three methods were compared for extraction, bare maceration (MA), mechanical blending (ME) and mechanical blending following maceration (MPM) to produce films with an approximate thickness of 150 μm. For the comparison, tensile testing, differential scanning calorimetry and scanning electron microscopy were used. The MPM process proved the most effective, not only for extraction yielding, but also to obtain a larger deformation of the samples with respect to the one allowed by the pure TPS films. A considerable plasticization effect was observed. Despite this, the mechanical performance is still not completely satisfactory, and the expected effect of the calcium and magnesium salts contained in the mucilage to improve the rigidity of the TPS film was not really revealed. Prospected improvements would concern the fabrication process and the investigation of other possible loading modes and sample geometries.

Dry fibers coming from garden waste, originating from Opuntia ficus indica, were introduced in amounts of either 8 or 16 wt % into a self-produced thermoplastic starch (TPS) based on potato starch and glycerol. Thermal (differential scanning calorimetry, DSC), mechanical (tensile tests), and morphological characterization with scanning electron microscopy (SEM) and performing energy-dispersive X-ray spectrometry (microanalysis) were carried out. The results indicated that the uneven distribution and variable geometry of fibers introduced led to a reduction of tensile stress and strain with respect to pure TPS. However, the positive effects of prolonged mixing and increased thickness were highlighted, which suggest the fabrication of the composite could be improved in the future by controlling the manufacturing procedure.

Exposure to high levels of radiation can cause acute, long-term health effects, such as acute radiation syndrome, cancer, and cardiovascular disease. This is an important occupational hazard in different fields, such as the aerospace and healthcare industry, as well as a crucial burden to overcome to boost space applications and exploration. Protective bulky equipment made of heavy metals is not suitable for many advanced purporses, such as mobile devices, wearable shields, and manned spacecrafts. In the latter case, the in-space manufacturing of protective shields is highly desirable and remains an unmet need. Composites made of polymers and high atomic number fillers are potential means for radiation protection due to their low weight, good flexibility, and good processability. In the present work, we developed electrospun composites based on polycaprolactone (polymer matrix) and tungsten powder for application as shielding materials. Electrospinning is a versatile technology that is easily scalable at an industrial level and allows obtaining very lightweight, flexible sheet materials for wearables. By controlling tungsten powder size, we engineered homogeneous, stable and processable suspensions to fabricate radiation composite shielding sheets. The shielding capability was assessed by an in vivo model on prototype composite sheets containing 80 w% of W filler in a polycaprolactone (PCL) fibrous matrix by means of irradiation tests (X-rays) on mice. The obtained results are promising; as expected, the shielding effectivity of the developed composite material increases with the thickness/number of stacked layers. It is worth noting that a thin barrier consisting of 24 layers of the innovative shielding material reduces the extent of apoptosis by 1.5 times compared to the non-shielded mice.