Non-isothermal oxidation is one of the important issues for the safe application of Ti-Al alloys, so this study aimed to illustrate the non-isothermal oxidation behaviors and the corresponding mechanisms of a TiAl-based alloy in comparison with a Ti₃Al-based alloy. The non-isothermal oxidation behaviors of Ti-46Al-2Cr-5Nb and Ti-24Al-15Nb-1.5Mo alloys in pure oxygen were comparatively investigated with a thermogravimetry-differential scanning calorimetry (TGA/DSC) simultaneous thermal analyzer heating from room temperature to 1450 °C with a heating rate of 40 °C/min. When the temperature rose above 1280 °C, the oxidation rate of the Ti-46Al-2Cr-5Nb alloy sharply increased and exceeded that of the Ti-24Al-15Nb-1.5Mo alloy owing to the occurrence of internal oxidation. When the temperature was higher than 1350 °C, the oxidation rate of the Ti-46Al-2Cr-5Nb alloy decreased obviously due to the generation of an oxygen-barrier β-Al₂TiO₅-rich layer by a chemical reaction between Al₂O₃ and TiO₂ in the oxide scale. Based on Wagner’s theory of internal oxidation, the reason for the occurrence of internal oxidation in the Ti-46Al-2Cr-5Nb alloy is the formation of the α phase in the subsurface, while no internal oxidation occurred in the Ti-24Al-15Nb-1.5Mo alloy due to the existence of the β phase in the subsurface with the enrichment of Nb and Mo.

FeCoCrNiNb_xN (x = 0, 0.25, 0.5, 0.75, 1 molar) high-entropy nitride (HEN) films were fabricated on 304 stainless steel and Si wafers using magnetron sputtering to investigate the influence of Nb content on the microstructure, mechanical properties, and tribological performance. X-ray diffraction (XRD) analysis reveals a face-centered cubic (FCC) structure with a preferred orientation in the (200) plane, which transfers to the (111) plane as the Nb content increases. The lattice distortion induced by Nb incorporation enhanced crystallinity, with the Nb_0.5N film exhibiting the highest diffraction peak intensity and interplanar distance. Cross-sectional SEM images displayed columnar crystal structures, while the surface morphology evolved from “cauliflower-like” to smoother clusters with increasing Nb content, reducing average roughness from 7.54 nm (Nb₀) to 4.89 nm (Nb₁). The hardness and elastic modulus initially decrease, then peak at 25.56 GPa and 265.36 GPa, respectively, for the Nb₁ film, attributed to solid solution strengthening and high-entropy effects. Tribological tests demonstrated that Nb₁ achieved the lowest coefficient of friction (0.46), wear volume (1.23 × 10⁻³ mm³), and wear rate (5.11 × 10⁻⁸ mm³·N⁻¹·m⁻¹), owing to NbN phase formation, refined grains, and reduced surface roughness. The wear mechanisms are abrasive and oxidative wear.