Crumb rubber modified bitumen (CRMB) has excellent high-temperature performance and fatigue resistance, and is widely used in asphalt pavement to cope with increasing traffic axle load and changing climate. Under conventional preparation conditions, the swelling degree of CR can directly impact the comprehensive properties of CRMB; however, physical and chemical properties research on swelling crumb rubber (SCR) and crumb rubber recycled bitumen (CRRB) in CRMB is relatively lacking. In this paper, the working performance of CRMB and CRRB in high-temperature and low-temperature conditions were studied through physical and working performance testing of bitumen. The CR and SCR were tested by scanning electron microscope (SEM), Fourier transform infrared spectrometer (FTIR), gel permeation chromatography (GPC), and particle size distribution (PSD) tests to study the physicochemical behavior and microscopic effects before and after CR swelling. The results showed that CR dosage was in the range of 10%, 15%, and 20%, as well as that CR dosages have a positive effect on the high- and low-temperature performance, storage stability, and elastic recovery of bitumen. The high-temperature PG grades of bitumen were directly improved by four grades, and the elastic recovery rate increased by 339.9%. CR improved the ultra-low temperature crack resistance of bitumen. Due to the absorption of lighter components by CR, the relative content of the heavy component of bitumen increased; however, its low-temperature performance decreased significantly. After swelling, the CR particle size increased and the range became wider, the surface complexity of CR became higher, and the specific surface area was larger. At the same time, CR carried out the transformation process from large and medium molecules to small molecules. During the swelling process, a new benzene ring structure appeared in the CR, and the C–C bond and C–S bond of CR broke, forming part of the C=C bond.

During the service period, asphalt materials are affected by various natural factors, including heat, ultraviolet light, oxygen and moisture, etc., resulting in the reduction of pavement performance, the increase of pavement distress and shortening of service life. This study aims to investigate the aging performance of asphalt under multiple aging conditions of heat, UV and aqueous solution. Thermal-oxygen aging, UV aging and hydrostatic erosion tests were carried out sequentially on asphalt. The rheological properties, chemical structure and element composition of asphalt were characterized before and after aging, and the effect mechanism of multiple conditions was discussed. The results show that the multiple conditions of heat and UV can increase the rutting resistance and weaken the cracking resistance of asphalt. However, the effect degree of UV decreases gradually with the deepening of aging degree. Additionally, the effect of water on the physicochemical properties is less than that of UV; however, water can increase the sensitivity of physicochemical properties to UV. In summary, this study explored the short-term cycling effect of heat, light and water on asphalt and provided an idea for simulation test of asphalt under multiple aging condition.

In recent years, recycling steel slag is receiving growing interest in the road base layer construction field due to its role in alleviating land occupation and resource shortages. However, the mixture compaction and its environmental impact on practical construction sites remain unclear, which may hinder the application of steel slags in road layers. This study investigates the pavement construction of the ‘Baotou-Maoming’ motorway, located in Inner Mongolia, China, analyzing the compaction procedures and assessing the environmental impacts caused by the road base layer containing steel slag. Firstly, mechanical properties and texture appearances of the steel slag aggregates are characterized. Afterwards, the comparative assessments for steel slag and andesite layers compaction are quantified from equivalent CO₂ emission and energy consumption aspects, respectively. The results show that the steel slag has a better surface texture than the natural aggregates; physical properties including compactness, flatness and compressive strength comply with the requirements for applying steel slag to a hydraulically bound mixture. Compared to the base layer using andesite aggregates, the compaction vibration period of the course containing steel slags should be reduced to achieve a proper density due to the “hard-to-hard” effect that occurs between the adjacent steel slag particles. Consequently, the additional energy and the equivalent CO₂ are generated at 2.67 MJ/m³ and 0.20 kg/m³, respectively.

As two kinds of solid wastes, waste tires and steel slag have caused serious threats to the environment. Both waste tire rubber (WTR) and steel slag powder (SSP) can improve the performance of asphalt, while the performance indexes and modification mechanism of modified asphalt are not clear. In this paper, asphalt modified with SSP and WTR was prepared, and its performance was evaluated. The physical properties of asphalt modified with SSP and WTR, including penetration, the softening point, and viscosity, were investigated. Furthermore, high-temperature performance, fatigue resistance, low-temperature performance, and blending mechanism of asphalt modified with SSP and WTR were tested with a dynamic shear rheometer (DSR), bending beam rheometer (BBR), and Fourier transform infrared spectrometer (FTIR). The results showed that with the same content of WTR and SSP, WTR reveals a more significant modification effect on physical properties, fatigue, and low-temperature performance of base asphalt than SSP. The anti-rutting performance of SSP-modified asphalt is better than that of WTR-modified asphalt at 30~42 °C, and the anti-rutting performance of WTR-modified asphalt is better than that of SSP-modified asphalt at 42~80 °C. When the total content of WTR and SSP is the same, the physical properties, high-temperature resistance, fatigue resistance, and low-temperature performance of the asphalt modified with WTR and SSP decrease with the decrease in the ratio of WTR and SSP, and their performance is between WTR-modified asphalt and SSP-modified asphalt. Infrared spectrum results verified that the preparation of WTR- and SSP-modified asphalt is mainly a physical blending process. Overall, this research is conducive to promoting the application of modified asphalt with WTR and SSP in the construction of high-standard pavement.

Erosion and the stripping effect of moisture on asphalt mixtures is one of the main reasons for the shortened service life of asphalt pavements. The common mean of preventing asphalt pavements from being damaged by moisture is adding anti-stripping agents (ASAs) to asphalt mixtures. However, the effect regularity and mechanism of anti-stripping agents on the physicochemical properties of asphalt is not exactly defined. This study compared the physical properties of ASA-modified asphalt (AMAs) to determine the optimal dosage and investigated the rheological and adhesion properties. Based on the roller bottle method and water immersion method, the moisture susceptibility of AMAs with three particle sizes was investigated. The results showed that the modification of asphalt using anti-stripping agents was a physical modification. At the optimum dosage of anti-stripping agents (0.3%), the basic physical properties of AMA1 were the most desirable. ASA2 increased the resistance of asphalt for deformation at high temperature by 46%, and AMA3 had the best low-temperature performance. ASAs enhanced the dispersed and polar components in the asphalt binder, improving the adhesion energy of asphalt. AMA3 had the strongest adhesion to the aggregate, with an increase in adhesion work by 2.8 times and a 45% of increase in ER value. This was attributed to ASA3 containing with a large number of metal cations and polar functional groups. It was shown that ASAs provided the most improvement in the anti-stripping performance of asphalt mixtures with 9.5–13.2 mm particles. The amide ASA, phosphate ASA and aliphatic amine ASA improved the water damage resistance of asphalt by 65%, 45% and 78%, respectively. This study can help engineers realize the effects of different types of ASAs on the physicochemical properties of asphalt and select the most suitable type of ASAs according to the service requirements.