Graphene oxide (GO) has a unique layered structure with excellent gas and liquid blocking properties. It is widely used in many areas, such as gas sensors, carbon-based electronics, impermeable membranes, and polymeric composite materials. In order to evaluate whether GO (1% and 3% by weight of asphalt) can improve the aging resistance performance of the asphalt, 80/100 penetration grade asphalt (90 A) and styrene–butadiene–styrene modified asphalt (SBS MA) were used to prepare the GO modified asphalt by the melt blending method. The surface morphology of the GO was analyzed by scanning electron microscope (SEM). The UV aging test was conducted to simulate the aging during the service period. After UV aging test, the physical performances of GO-modified asphalts were tested, and the I_C=O and I_S=O increments were tested by Fourier transform infrared spectroscopy (FTIR) to evaluate the aging resistance performance of the GO modified asphalt. In addition, the rheological properties of GO modified asphalts were studied using a dynamic shear rheometer (DSR). The SEM analysis indicated that the GO exhibits many shared edges, and no agglomeration phenomenon was found. With respect to the physical performance test, the FTIR and the DSR results show that GO can improve the UV aging resistance performance of 90 A and SBS MA. In addition, the analysis indicated that the improvement effect of 3% GO is better than the 1% GO. The testing on the rheological properties of the modified asphalt indicated that the GO can also improve the thermo-oxidative aging resistance performance of asphalt.

The properties of asphalt pavement are damaged under the effects of moisture. The pH value and salt concentration of water are the key factors that affect the chemical and rheological properties of asphalt during moisture damage. Four kinds of water solutions, including distilled water, an acidic solution, alkaline solution and saline solution were used to investigate the effects of aqueous solute compositions on the chemical and rheological properties of asphalt. Thin-layer chromatography with flame ionization detection (TLC-FID), Fourier transform infrared (FTIR) spectroscopy and dynamic shear rheometer (DSR) were applied to investigate the components, chemistry and rheology characteristics of asphalt specimens before and after water solute exposure. The experimental results show that moisture damage of asphalt is not only associated with an oxidation process between asphalt with oxygen, but it is also highly dependent on some compounds of asphalt dissolving and being removed in the water solutions. In detail, after immersion in water solute, the fraction of saturates, aromatics and resins in asphalt binders decreased, while asphaltenes increased; an increase in the carbonyl and sulphoxide indices, and a decrease in the butadiene index were also found from the FTIR analyzer test. The rheological properties of asphalt are sensitive to water solute immersing. The addition of aqueous solutes causes more serious moisture damage on asphalt binders, with the pH11 solution presenting as the most destructive during water solute exposure.

Although huge numbers of investigations have been conducted for the ultraviolet (UV) aging of asphalt binder, research rarely focuses on the asphalt mixture. In order to evaluate the aging effect of UV radiation on the asphalt mixture, a dense grade of asphalt mixture was designated and aged by UV radiation for 7, 14 and 28 days respectively. After that, the chemical functional groups of asphalt binder were tested by Fourier transform infrared spectrometer (FTIR). The semi-circular bending strength and fatigue resistance of asphalt concrete were tested to characterize the mechanical properties of the asphalt concrete. To evaluate the self-healing effect of the macro-structure continuity of asphalt concrete intuitively, the computed tomography (CT) scanning machine was used to characterize the crack size of asphalt concrete samples both before and after self-healing. The results show that, with the increase of UV irradiation time, the relative ratios of the C=O and S=O bands’ areas of recovered asphalt binder increase significantly. UV radiation can significantly weaken the mechanical and self-healing properties of asphalt mixture, making the asphalt mixture to have worse macro-structure continuity, lower failure strength and worse fatigue resistance. Moreover, the longer the UV irradiation time is, the degradation effect of UV radiation on asphalt mixture becomes more obvious.