Appropriate selection of wire–arc additive manufacturing (WAAM) variables imparts bead geometries with characteristics of multi-layer structures. Thus, the present study aimed to optimize the gas metal arc welding (GMAW)-based WAAM variables of travel speed (TS), wire feed speed (WFS), and voltage (V) for the bead geometries of bead width (BW) and bead height (BH) on an SS 316L substrate. Single-layer depositions were made through a metallic wire of SS 316L by following an experimental matrix of the Box–Behnken design (BBD) technique. Multivariable regression equations were generated for design variables and responses, and ANOVA was used to investigate the feasibility of the obtained regression equations. WFS was the highest contributor affecting the BW, followed by V and TS, while WFS was again the highest contributor affecting the BH, followed by TS and V. Heat transfer search (HTS) optimization was used to attain optimal combinations. The single-objective optimization result showed a maximum bead height and minimum bead width of 6.72 mm and 3.72 mm, respectively. A multi-layer structure was then fabricated by considering an optimization case study, and it showed optimized parameters at a WFS of 5.50 m/min, TS of 141 mm/min, and voltage of 19 V with the bead height and bead width of 5.01 mm and 7.81 mm, respectively. The multi-layered structure obtained at the optimized parameter was found to be free from disbonding, and seamless fusion was detected between the obtained layers of the structure. The authors believe that the present study will be beneficial for industrial applications for the fabrication of multi-layer structures.

The fabrication of components involves the deposition of multiple beads in multiple layers for wire-arc additive manufacturing (WAAM). WAAM performed using gas metal arc welding (GMAW) allows for the manufacturing of parts through multiple-bead multi-layer deposition, which depends on the process variables. Thus, the selection of process parameters along with their required levels is mandatory to deposit multiple layers for WAAM. To obtain the desired levels of parameters, bead-on-plate trials were taken on the base plate of low alloy steel by following an experimental matrix produced through the Box–Behnken design (BBD) on GMAW-based WAAM. Wire feed speed, travel speed, and voltage were chosen as the input parameters and bead width and bead height were chosen as the output parameters. Furthermore, the robustness and adequacy of the obtained regression equations were analyzed by using analysis of variance (ANOVA). For both responses of BW and BH, values of R² and adj. R² were found to be near unity, which has shown the fitness of the model. Teaching–learning-based optimization (TLBO) technique was then employed for optimization. Within the selected range of process variables, the single-objective optimization result showed a maximum bead height (BH) of 7.81 mm, and a minimum bead width (BW) of 4.73 mm. To tackle the contradicting nature of responses, Pareto fronts were also generated, which provides a unique non-dominated solution. Validation trials were also conducted to reveal the ability and suitability of the TLBO algorithm. The discrepancy between the anticipated and measured values was observed to be negligible, with a deviation of less than 5% for all the validation trials. This demonstrates the success of the established model and TLBO algorithm. The optimum feasible settings for multi-layer metal deposition were determined after further tuning. A multi-layer structure free from any disbonding was successfully manufactured at the optimized variables. The authors suggest that the optimum parametric settings would be beneficial for the deposition of layer-by-layer weld beads for additive manufacturing of components.

Multi-material additive manufacturing (MMAM) have the capability to directly fabricate three-dimensional (3D) parts consisting of more than one material. Multi-