This work aimed to investigate the degradation performance of natural cellulose acetate (CA) membranes filled with ZnO nanostructures. Photocatalytic degradation of reactive toxic dye methylene blue (MB) was studied as a model reaction using UV light. A CA membrane was previously casted and fabricated through the phase inversion processes and laboratory-synthesized ZnO microparticles as filler. The prepared membrane was characterized for pore size, ultrafiltration (UF) performance, porosity, morphology using scanning electron micrographs (SEM), water contact angle and catalytic degradation of MB. The prepared membrane shows a significant amount of photocatalytic oxidation under UV. The photocatalytic results under UV-light radiation in CA filled with ZnO nanoparticles (CA/ZnO) demonstrated faster and more efficient MB degradation, resulting in more than 30% of initial concentration. The results also revealed how the CA/ZnO combination effectively improves the membrane’s photocatalytic activity toward methylene blue (MB), showing that the degradation process of dye solutions to UV light is chemically and physically stable and cost-effective. This photocatalytic activity toward MB of the cellulose acetate membranes has the potential to make these membranes serious competitors for removing textile dye and other pollutants from aqueous solutions. Hence, polymer–ZnO composite membranes were considered a valuable and attractive topic in membrane technology.

Washingtonia is a desert plant with great sustainability and renewability in nature and is abundantly cultivated across global urban regions. Its fibre biomass comprises cellulose as the major structural part, and this is why it can be potentially utilized as an alternative biomaterial for manufacturing microcrystalline cellulose (MCC) products that can be widely applied in industrial fields. In the present study, NaOH-treated Washingtonia fibre (WAKL), NaClO₂-treated Washingtonia fibre (WBLH), and Washingtonia microcrystalline cellulose (WMCC) were extracted through combined treatments of alkalization, bleaching, and acidic hydrolysis, respectively. The obtained chemically treated fibre samples were subjected to characterization to investigate their morphology, physico-chemistry, and thermal stability. In a morphological examination, the large bunch WAKL fibre reduced into small size WMCC fibrils, evidencing that the lignin and hemicellulose components were greatly eliminated through chemical dissolution. The elemental composition revealed that almost all impurities of anions and cations had been removed, particularly for the WMCC sample, showing its high purity of cellulose content. Additionally, the WMCC sample could attain at 25% yield, giving it the advantage for feasible economic production. Furthermore, the physicochemical analysis, Fourier Transform Infrared-ray (FTIR), indicated the presence of a crystalline cellulose region within the WMCC structure, which had promoted it with high crystallinity of 72.6% as examined by X-ray diffraction (XRD). As for thermal analysis, WMCC showed greater thermal stability comparing to WAKL and WBLC samples at high temperature. Therefore, Washingtonia fibre can be a reliable biosubstituent to replace other plant material for MCC production in the future.

Styrene-butadiene rubber (SBR) is a synthetic polymer primarily used in the tire industry, due to its good collaborative properties with additives and fillers. In the present work, we aim to synthesize an SBR composite reinforced with graphene oxide filler to be made biodegradable. In composite preparation, we fabricated styrene-butadiene rubber/graphene oxide/collagen (SBR/GO/COL) composites by adding a biodegradable biomolecule of elastin collagen fillers at 1.5 wt% and 2.5 wt%. Those prepared SBR/GO/COL composites, along with pure SBR and SBR/GO as control samples, were characterized using advanced analysis techniques, and their biodegradability was also evaluated. From microscopy examination results, the morphology of pure SBR had been improved after the addition of GO for SBR/GO composite by revealing a compact structure with a smoother surface. As for the SBR/GO/1.5COL sample, the 1.5 wt% COL filler was found to be effectively embedded in the SBR/GO matrix. However, the 2.5 wt% COL amount led to the formation of an aggregated structure in the SBR/GO/2.5COL sample due to the unreacted interface between COL filler and SBR/GO. The porosity had also been improved for SBR/GO/1.5COL sample, imparting it with a surface area suitable for tires in the automobile industry. From elemental analysis, the presence of nitrogen was detected for the collagen-filled SBR composite, proving the successful incorporation of collagen fibrils. The physicochemical analysis also detected a trace of graphene oxide and collagen functional groups in the SBR composite. In addition, the thermal analysis revealed those collagen-filled composites had stable heat tolerance behavior, which is suitably used in extreme weather conditions. Moreover, the SBR/GO/1.5COL sample exhibited good characteristics in both mechanical and biodegradable properties. Thus, the product of SBR/GO/1.5COL could be regarded as a promising composite for green tires in the auto industry in the future.

In this paper, the interaction of imipramine hydrochloride (IMP, antidepressant drug) and a non-ionic surfactant Triton X-100 (TX-100) mixture in five different ratios through the tensiometric method in different solvents (aqueous/0.050 mol·kg⁻¹ aqueous NaCl/0.250 mol·kg⁻¹ aqueous urea (U)) were examined thoroughly at a temperature of 298 K. UV–Visible studies in an aqueous system of IMP + TX-100 mixtures were also investigated and discussed in detail. The pure (IMP and TX-100) along with the mixtures’ critical micelle concentration (cmc) were assessed by a tensiometric technique. The obtained deviation of the mixtures’ cmc values from their ideal values revealed the nonideal behavior of IMP + TX-100 mixtures amongst IMP and TX-100. Compared to aqueous systems, in the presence of aqueous NaCl, several changes in micelles/mixed micelles occurred, and hence a synergism/attractive interaction amongst components was found increased while in the existence of U, the synergism/attractive interaction between them decreased. The evaluated interaction parameter (β^Rb) value of mixed micelles showed the attractive or synergism between the IMP and TX-100. Various evaluated thermodynamic parameters in an aqueous system showed that the mixed micellization of the IMP + TX-100 mixture was an entropically spontaneous phenomenon, although the existence of salt in all studied systems can somewhat increase the spontaneity of the micellization process and in the aqueous U system, the spontaneity of the micellization process decreased. In an aqueous system, the interaction between IMP and TX-100 was also confirmed by UV–Visible study.

Currently, polymer organic solar cells (POSCs) are widely utilized due to their significant application, such as low-cost power conversion efficiencies (PCEs). Therefore, we designed a series of photovoltaic materials (D1, D2, D3, D5 and D7) by the incorporation of selenophene units (n = 1–7) as π₁-spacers by considering the importance of POSCs. Density functional theory (DFT) calculations were accomplished at MPW1PW91/6-311G (d, p) functional to explore the impact of additional selenophene units on the photovoltaic behavior of the above-mentioned compounds. A comparative analysis was conducted for designed compounds and reference compounds (D1). Reduction in energy gaps (∆E = 2.399 − 2.064 eV) with broader absorption wavelength (λ_max = 655.480 − 728.376 nm) in chloroform along with larger charge transference rate was studied with the addition of selenophene units as compared to D1. A significantly higher exciton dissociation rate was studied as lower values of binding energy (E_b = 0.508 − 0.362 eV) were noted in derivatives than in the reference (E_b = 0.526 eV). Moreover, transition density matrix (TDM) and density of state (DOS) data also supported the efficient charge transition origination from HOMOs to LUMOs. Open circuit voltage (V_oc) was also calculated for all the aforesaid compounds to check the efficiency, and significant results were seen (1.633–1.549 V). All the analyses supported our compounds as efficient POSCs materials with significant efficacy. These compounds might encourage the experimental researchers to synthesize them due to proficient photovoltaic materials.

Lipases are extensively utilized industrial biocatalysts that play an important role in various industrial and biotechnological applications. Herein, polyacrylonitrile (PAN) was treated with hexamethylene diamine (HMDA) and activated by glutaraldehyde, then utilized as a carrier support for Candida rugosa lipase. In this regard, the morphological structure of modified PAN before and after the immobilization process was evaluated using FTIR and SEM analyses. The immobilized lipase exhibited the highest activity at pH 8.0, with an immobilization yield of 81% and an activity of 91%. The optimal pH and temperature for free lipase were 7.5 and 40 °C, while the immobilized lipase exhibited its optimal activity at a pH of 8.0 and a temperature of 50 °C. After recycling 10 times, the immobilized lipase maintained 76% of its activity and, after 15 reuses, it preserved 61% of its activity. The lipase stability was significantly improved after immobilization, as it maintained 76% of its initial activity after 60 days of storage. The calculated Km values were 4.07 and 6.16 mM for free and immobilized lipase, and the Vmax values were 74 and 77 μmol/mL/min, respectively. These results demonstrated that synthetically modified PAN is appropriate for immobilizing enzymes and has the potential for commercial applications.