The development of additive manufacturing methods known as “3D printing” started in the 1980s. In these methods, spatial models are created from a semi-finished product such as a powder, filament or liquid. The model is most often created in layers, which are created from the semi-finished product, which is most often subjected to thermal treatment or using light or ultraviolet rays. The technology of additive manufacturing has both advantages and disadvantages when compared to the traditionally used methods of processing thermoplastic materials, such as, for example, injection or extrusion. The most important advantages are low cost, flexibility and speed of manufacturing of elements with different spatial shapes. From the point of view of the user of the product, the most important disadvantages are the lower mechanical properties and lower resistance to environmental factors that occur during the use of the manufactured products. The purpose of this review is to present current information and a compilation of features in the field of research on the effects of the interactions of different types of environments on the mechanical properties of 3D-manufactured thermoplastic products. Changes in the structure and mechanical properties of the material under the influence of factors such as humidity, salt, temperature, UV rays, gasoline and the environment of the human body are presented. The presented article enables the effects of environmental conditions on common materials used in 3D printing technology to be collated in one place.

The article presents the research results on the influence of variable shock conditions, such as temperature and water, thus reflecting shock atmospheric conditions during freezing and thawing, on the properties of samples produced using 3D printing technology from commonly used materials such as ABS, HIPS, PLA, and ASA. Understanding how different environmental conditions affect the quality, reliability, and durability of 3D prints can help to optimize the printing process and provide valuable information about their application possibilities. Tests related to the strength of the materials, such as static tensile testing, Charpy impact testing, and evaluation of structures, were carried out using a scanning electron microscope (SEM). Changes in chemical properties were measured by performing tests such as FTIR and TGA. Variations in chemical properties were measured by performing tests such as FTIR and TGA. One shock cycle lasting 7 days was sufficient to alter the properties of 3D prints, with the extent of changes depending on the material, as summarized in the test results.

3D printing technology is becoming a widely adopted alternative to traditional polymer manufacturing methods. The most important advantage of 3D printing over traditional manufacturing methods, such as injection molding or extrusion, is the short time from the creation of a new design to the finished product. Nevertheless, 3D-printed parts generally have lower strength and lower durability compared to the same parts manufactured using traditional methods. Resistance to the environmental conditions in which a 3D-printed part operates is important to its durability. One of the most important factors that reduces durability and degrades the mechanical properties of 3D-printed parts is temperature, especially rapid temperature changes. In the case of inhomogeneous internal geometry and heterogeneous material properties, rapid temperature changes can have a significant impact on the degradation of 3D-printed parts. This degradation is more severe in high-humidity environments. Under these complex service conditions, information on the strength and fatigue behavior of 3D-printed polymers is limited. In this study, we evaluated the effects of high humidity and temperature changes on the durability and strength properties of 3D-printed parts. Samples made of commonly available materials such as ABS (Acrylonitrile Butadiene Styrene), ASA (Acrylonitrile-Styrene-Acrylate), HIPS (High-Impact Polystyrene), and PLA (Poly(lactic acid)) were subjected to temperature cycling, from an ambient temperature to −20 °C, and then were heated to 70 °C. After thermal treatment, the samples were subjected to cyclic loading to determine changes in their fatigue life relative to non-thermally treated reference samples. The results of cyclic testing showed a decrease in durability for samples made of ASA and HIPS. The ABS material proved to be resistant to the environmental effects of shocks, while the PLA material exhibited an increase in durability. Changes in the internal structure and porosity of the specimens under temperature changes were also evaluated using microcomputed tomography (microCT). Temperature changes also affected the porosity of the samples, which varied depending on the material used.

The paper describes the type of changes in the structure and mechanical properties of 3D printed shapes under the influence of mineral oil. The effects of a room (23 °C) and elevated temperature (70 °C) on 3D prints manufactured by the FDM method and stored in oil for 15, 30, and 60 days on the change of properties and structure were investigated. The samples were produced from ABS (poly(acrylonitrile-co-butadiene-co-styrene)), ASA (poly(acrylonitrile-co-styrene-co-acrylate), PLA (poly(lactic acid)), and HIPS (high-impact polystyrene). Tests related to the strength of the materials, such as the static tensile test and Charpy impact test, were carried out. The structure was evaluated using a scanning electron microscope, and changes in chemical structure were determined by conducting FTIR (Fourier transform infrared spectroscopy) and TGA (thermogravimetric analysis) tests. The analysis of the results provided important information about the impact of mineral oil on specific materials. This is critical for designing and manufacturing components that can withstand mineral oil exposure in real-world environments. The materials underwent varying changes. Strength increased for PLA by about 28%, remained unchanged for ABS and HIPS during exposure for 30 days, and decreased for ASA with extended exposure up to 14%.

Three-dimensionally printed parts are increasingly used in industry for quick repairs. They are often operated in the presence of grease, oil, and others. This article describes the effect of engine mineral oil on the fatigue life of 3D-printed FDM plastic samples. For this reason, this article aimed to investigate the influence of oil on the fatigue life of materials made using this technology. Samples made of ABA, ASA, PLA, and HIPS materials were printed with 100% fill. Divided into groups, they were stored for 15, 30, and 60 days in an oil bath at a room temperature of 23 °C and an increased temperature of 70 °C. To compare the effect of storage in oil, static tests were performed to determine the tensile strength of the specimens and to determine the load levels for the cyclic tests. Cyclic tests were performed to determine the effect of oil and temperature on the fatigue life. Internal structure studies of the specimens were performed using computed microtomography to determine the changes in the porosity of the specimens under the influence of oil. In the case of ABS, the oil-bathed samples showed a clear increase in the fatigue life, especially at 23 °C. For the ASA specimens, an increase was also evident, especially for the lower stress value. For HIPS and PLA, no clear effect of the oil bath on the fatigue life value of the samples was determined. Porosity studies using computed microtomography showed a clear decrease in the porosity of the samples as a result of the oil bath for all of them.

The authors wish to make a change to their published paper