The paper presents the characteristics of unplasticized PVC composites modified with biofiller obtained from the waste eggshells of hen eggs. The composites obtained by extrusion contained from 10 phr to 40 phr of biofiller. The filler was characterized using the SEM, TG, and sieve analysis methods. The influence of the filler on the processing properties was determined using plastographometric and MFR tests. Fundamental analysis of mechanical properties was also performed, i.e., Charpy impact strength and determination of tensile properties. The mechanical properties were supported with dynamical mechanical thermal analysis, time of thermal stability, and thermogravimetric analysis. Structure analysis was also performed using SEM and X-ray microcomputed tomography (micro-CT). The processing properties of the tested composites do not give grounds for disqualifying such material from traditional processing PVC mixtures. Notably, the biofiller significantly improves thermal stability. Ground eggshells (ES) work as scavengers for the Cl radicals released in the first stage, which delays the PVC chain’s decay. Additionally, a significant increase in the value of the modulus of elasticity and softening point (VST) of the composites concerning PVC was found. Ground hen eggshells can be used as an effective filler for PVC composites.

Hydrogels are hydrophilic, porous polymer networks that can absorb up to thousands of times their own weight in water. They have many potential applications, one of which is the encapsulation of freestanding black lipid membranes (BLMs) for novel separation technologies or biosensor applications. We investigated gels for in situ encapsulation of multiple BLMs formed across apertures in a hydrophobic ethylene tetrafluoroethylene (ETFE) support. The encapsulation gels consisted of networks of poly(ethylene glycol)-dimethacrylate or poly(ethylene glycol)-diacrylate polymerized using either a chemical initiator or a photoinitiator. The hydrogels were studied with regards to volumetric stability, porosity, and water permeability. All hydrogels had pore sizes around 7 nm with volumetric changes >2% upon crosslinking. Photoinitiated hydrogels had a lower hydraulic water permeability compared to chemically initiated hydrogels; however, for all hydrogels the permeability was several-fold higher than the water permeability of conventional reverse osmosis (RO) membranes. Lifetimes of freestanding BLM arrays in gel precursor solutions were short compared to arrays formed in buffer. However, polymerizing (crosslinking) the gel stabilized the membranes and resulted in BLM arrays that remained intact for days. This is a substantial improvement over lifetimes for freestanding BLM arrays. Optical images of the membranes and single channel activity of incorporated gramicidin ion channels showed that the lipid membranes retained their integrity and functionality after encapsulation with hydrogel. Our results show that hydrogel encapsulation is a potential means to provide stability for biomimetic devices based on functional proteins reconstituted in biomimetic membrane arrays. Copyright © 2010 John Wiley & Sons, Ltd.

The article presents the research results on the influence of variable shock conditions, such as temperature and water, thus reflecting shock atmospheric conditions during freezing and thawing, on the properties of samples produced using 3D printing technology from commonly used materials such as ABS, HIPS, PLA, and ASA. Understanding how different environmental conditions affect the quality, reliability, and durability of 3D prints can help to optimize the printing process and provide valuable information about their application possibilities. Tests related to the strength of the materials, such as static tensile testing, Charpy impact testing, and evaluation of structures, were carried out using a scanning electron microscope (SEM). Changes in chemical properties were measured by performing tests such as FTIR and TGA. Variations in chemical properties were measured by performing tests such as FTIR and TGA. One shock cycle lasting 7 days was sufficient to alter the properties of 3D prints, with the extent of changes depending on the material, as summarized in the test results.

The internal structure of samples produced by additive manufacturing (AM) technology of copolymer acrylonitrile-butadiene-styrene (ABS) was studied by microcomputer tomography (micro-CT). The results of micro-CT were correlated with the mechanical properties of samples. The aim of this paper was to demonstrate the acetone vaporization influence on the structure and mechanical properties of ABS samples printed with additive manufacturing technology. Samples were printed on three different devices and scanned with micro-CT after acetone vapors treatment. Mass and hardness of the samples were measured. Finally, the static tensile test was performed. Irregularly spaced voids, which directly affected samples properties, have been detected. Under the influence of acetone vaporization, the properties of the samples have changed such as: number of voids, mass, hardness, tensile strength.

Thin-walled and thick-walled microcellular moldings were obtained by MuCell^® technology with nitrogen as a supercritical fluid. 2 mm thick polyamide 6 (PA6) with 30% wt. glass fiber (GF) samples were cut from automotive industrial elements, while 4 mm, 6 mm, and 8.4 mm thick moldings of PA6.6 with 30% wt. GF were molded into a dumbbell shape. The internal structure was investigated by scanning electron microscopy (SEM) and X-ray computed microtomography (micro-CT) and compared by numerical simulations for microcellular moldings using Moldex3D^® 2022 software. Young’s modulus, and tensile and impact strength were investigated. Weak mechanical properties of 2 mm thick samples and excellent results for thick-walled moldings were explained. SEM pictures, micro-CT, and simulation graphs revealed the tendency to decrease the cell size diameter together with increasing sample thickness from 2 mm up to 8.4 mm.

The paper describes the type of changes in the structure and mechanical properties of 3D printed shapes under the influence of mineral oil. The effects of a room (23 °C) and elevated temperature (70 °C) on 3D prints manufactured by the FDM method and stored in oil for 15, 30, and 60 days on the change of properties and structure were investigated. The samples were produced from ABS (poly(acrylonitrile-co-butadiene-co-styrene)), ASA (poly(acrylonitrile-co-styrene-co-acrylate), PLA (poly(lactic acid)), and HIPS (high-impact polystyrene). Tests related to the strength of the materials, such as the static tensile test and Charpy impact test, were carried out. The structure was evaluated using a scanning electron microscope, and changes in chemical structure were determined by conducting FTIR (Fourier transform infrared spectroscopy) and TGA (thermogravimetric analysis) tests. The analysis of the results provided important information about the impact of mineral oil on specific materials. This is critical for designing and manufacturing components that can withstand mineral oil exposure in real-world environments. The materials underwent varying changes. Strength increased for PLA by about 28%, remained unchanged for ABS and HIPS during exposure for 30 days, and decreased for ASA with extended exposure up to 14%.