The manuscript aimed to review the types of acrylate polymers used in dentistry, as well as their chemical, physical, mechanical, and biological properties. Regarding their consistency and purpose, dental acrylate polymers are divided into hard (brittle), which includes acrylates for the production of plate denture bases, obturator prostheses, epitheses and maxillofacial prostheses, their repairs and lining, and soft (flexible), which are used for lining denture bases in special indications. Concerning the composition and method of polymerization initiation, polymers for the production of denture bases are divided into four types: heat-, cold-, light-, and microwave-polymerized. CAD/CAM acrylate dentures are made from factory blocks of dental acrylates and show optimal mechanical and physical properties, undoubtedly better monomer polymerization and thus biocompatibility, and stability of the shape and colour of the base and dentures. Regardless of the number of advantages that these polymers have to offer, they also exhibit certain disadvantages. Technological development enables the enhancement of all acrylate properties to respond better to the demands of the profession. Special attention should be paid to improving the biological characteristics of acrylate polymers, due to reported adverse reactions of patients and dental staff to potentially toxic substances released during their preparation and use.

The surface quality of denture base resins allows for easy colonization by microorganisms including Candida albicans and Staphylococcus aureus, which cause major diseases of the oral cavity such as denture stomatitis. The widespread use of silver nanoparticles (AgNPs) in various fields of medicine has led to research of their possible application in dentistry, mostly in the prevention of bacterial adhesion, proliferation, and biofilm formation. The aim of the study was to synthesize cold and heat-curing denture base resins modified with AgNPs and AgCl, and evaluate the potential of the modified resins to reduce the growth of C. albicans and S.aureus. The produced material was characterized by Fourier transform infrared spectroscopy (FTIR). The antimicrobial potential of the modified material was demonstrated by the disc-diffusion method, microdilution method, and a modified microdilution method (i.e., disk-diffusion method in broth with viable counting). Spectroscopy confirmed the incorporation of biocidal materials into the structure of the denture base resins. The AgCl and AgNPs modified resins showed an antimicrobial effect. The significance of the study is in the potential therapeutic effects of the modified materials for prevention and threating staphylococci and candida in elderly patients, who are in most cases denture wearers and have a greater susceptibility to develop opportunistic infections. Modified denture base resins can significantly reduce the presence of infection at the point of contact between the denture and the mucous membrane of the prosthetic restoration. Biological tests of modified denture base resins will follow.

Background/Aim. Tooth loss affects oral health-related life quality. More than a third of edentulous patients are not fully satisfied with their complete dentures and mainly complain of insufficient stability, retention, and pain during mastication. Solving the problem may include relining by materials that are based on silicone or acrylic. The aim of this study was to determine the level of patients? satisfaction before and after relining upper dentures with soft and rigid liners. Methods. The patients (n = 24) were divided into two study groups. Maxillary denture relining of the first group of patients was performed with hard acrylic based resins while in the second group of patients complete denture was relined with a silicone-based soft liner. They were asked the questions from the specifically adapted the Oral Health Impact Profile Questionnaire for edentulous patients before and three months after relining dentures. Results. After relining the patients showed a higher degree of satisfaction with their dentures in all the tested domains (masticatory function, psychological discomfort, social disability and retention and hygiene). The patients with soft denture relines were more satisfied. Conclusion. Relining of maxillary complete dentures significantly positively impacts the quality of life of patients in all the tested domains (masticatory function, psychological discomfort, social disability, pain and oral hygiene). Better results were achieved using a silicone-based soft liner, which recommends it as the material of choice for relining dentures.

The aim of the present study was to determine the content of residual monomer methyl methacrylate (MMA) in cold and hot polymerized poly(methyl methacrylate) (PMMA), both widely applicable in dentistry, by using MHE-GC-MS (multiple headspace extraction analysis by gas chromatography-mass spectrometry) in combination with GC-FID (gas chromatography with flame-ionization detection). The samples of PMMA were obtained by free-radical polymerization of MMA at room temperature (cold polymerized PMMA) and at 100 °C (hot polymerized PMMA), according to the manufacturer’s instructions. The MHE-GC-MS method consisted of ten successive extractions of MMA from the polymerized samples. According to the constructed calibration curve, the content of residual MMA in PMMA samples (mg_MMA/g_PMMA) was determined. Intramuscular implantation of sample materials was performed in experimental animals (rats) in order to demonstrate potential adverse effects of the unpolymerized residual reactants to the tissue in direct contact with polymeric implants. The content of residual monomer in cold polymerized PMMA was higher (15.75 mg_MMA/g_PMMA) in comparison to hot polymerized PMMA (10.96 mg_MMA/g_PMMA). The implanted samples of cold-polymerized acrylic resin showed intense inflammatory response of the surrounding tissue. According to the obtained results, hot polymerized PMMA is safer for use in dentistry.

Background/Aim. The vertical dimension of occlusion is a very important parameter for proper reconstruction of the relationship between the jaws. The literature describes many methods for its finding, from the simple, easily applicable clinically, to quite complicated, with the use of one or more devices for determination. The aim of this study was to examine the possibility of determining the vertical dimension of occlusion using the vocals ?O? and ?E? with the control of values o btained by applying cognitive functions. Methods. This investigation was performed with the two groups of patients. The first group consisted of 50 females and 50 males, aged 18 to 30 years. In this group the distance between the reference points (on top of the nose and chin) was measured in the position of the mandible in the vertical dimension of occlusion, the vertical dimension at rest and the pronunciation of the words ?OLO? and ?ELE?. Checking the correctness of the particular value for the word ?OLO? was also performed by the phonetic method with the application of cognitive exercises when the patients counted from 89 to 80. The obtained difference in the average values i n determining the vertical dimension of occlusion and the ?OLO? and ?ELE? in the first group was used as the reference for determining the vertical dimension of occlusion in the second group of patients. The second group comprised of 31 edentulous persons (14 females and 17 males), aged from 54 to 85 years who had been made a complete denture. Results. The average value obtained for the vertical dimension of rest for the entire sample was 2.16 mm, for the word ?OLO? for the entire sample was 5.51 mm and for the word ?ELE? for the entire sample was 7.47 mm. There was no statistically significant difference between the genders for the value of the vertical dimension at rest, ?ELE? and ?OLO?. There was a statistically significant difference between the values f or the vertical dimension at rest, ?OLO? and ?ELE? for both genders. There was a statistically significant correlation between the value for the vertical dimension at rest, ?OLO? and ?ELE?, for both groups of subjects. Conclusion. Determining the vertical dimension of occlusion requires 5.5 mm subtraction from the position of the mandible in pronunciation of the word ?OLO? or 7.5 mm in pronunciation of the word ?ELE?.

Background/Aim. Polymethyl methacrylate is used for producing a denture basis. It is a material made by the polymerization process of methyl methacrylate. Despite of the polymerization type, there is a certain amount of free methyl methacrylate (residual monomer) incorporated in the denture, which can cause irritation of the oral mucosa. The aim of this study was to determine the amount of residual monomer in four different denture base acrylic resins by liquid chromatography and the possibility of its reduction. Methods. After the polymerization, a postpolymerization treatment was performed in three different ways: in boiling water for thirty minutes, with 500 W microwaves for three minutes and in steam bath at 22º C for one to thirty days. Results. The obtained results showed that the amount of residual monomer is significantly higher in cold polymerizing acrylates (9.1-11%). The amount of residual monomer after hot polymerization was in the tolerance range (0.59- 0.86%). Conclusion. The obtained results denote a low content of residual monomer in the samples which have undergone postpolymerization treatment. A lower percent of residual monomer is established in samples undergone a hot polymerization.