This paper investigates the feasibility and performance of the fabrication of platinum high-temperature thin-film strain sensors on nickel-based alloy substrates by additive manufacturing. The insulating layer was made of a dielectric paste by screen printing process. A 1.8-micron-thick platinum film was deposited directly on the insulating layer. The four-wire resistance measurement method was used to eliminate the contact resistance of the solder joints. Comprehensive morphological and electrical characterization of the platinum thin-film strain gauge was carried out, and good static and dynamic strain responses were obtained, which confirmed that the strain gauge was suitable for in situ strain monitoring of high-temperature complex components.

During the last decades, the ionic polymer-metal composite (IPMC) received much attention because of its potential capabilities, such as large displacement and flexible bending actuation. In this paper, a biomimetic flapping air vehicle was proposed by combining the superiority of ionic polymer metal composite with the bionic beetle flapping principle. The blocking force was compared between casted IPMC and IPMC. The flapping state of the wing was investigated and the maximum displacement and flapping angle were measured. The flapping displacement under different voltage and frequency was tested. The flapping displacement of the wing and the support reaction force were measured under different frequency by experiments. The experimental results indicate that the high voltage and low frequency would get large flapping displacement.

The in-situ strain/stress detection of hot components in harsh environments remains a challenging task. In this study, ZrB₂/SiCN thin-film strain gauges were fabricated on alumina substrates by direct writing. The effects of ZrB₂ content on the electrical conductivity and strain sensitivity of ZrB₂/SiCN composites were investigated, and based on these, thin film strain gauges with high electrical conductivity (1.71 S/cm) and a gauge factor of 4.8 were prepared. ZrB₂/SiCN thin-film strain gauges exhibit excellent static, cyclic strain responses and resistance stability at room temperature. In order to verify the high temperature performance of the ZrB₂/SiCN thin-film strain gauges, the temperature-resistance characteristic curves test, high temperature resistance stability test and cyclic strain test were conducted from 25 °C to 600 °C. ZrB₂/SiCN thin-film strain gauges exhibit good resistance repeatability and stability, and highly sensitive strain response, from 25 °C to 600 °C. Therefore, ZrB₂/SiCN thin-film strain gauges provide an effective approach for the measurement of in-situ strain of hot components in harsh environments.