As a special engineering plastic, polyphenylene sulfide (PPS) can also be used to prepare membranes for membrane separation processes, adsorption, and catalytic and battery separators because of its unique properties, such as corrosion resistance, and chemical and thermal stability. Nowadays, many researchers have developed various types of PPS membranes, such as the PPS flat membrane, PPS microfiber membrane and PPS hollow fiber membrane, and have even achieved special functional modifications. In this review, the synthesis and modification of PPS resin, the formation of PPS membrane and the research progress of functional modification methods are systematically introduced, and the future perspective of PPS membrane is discussed.

In order to realize high-efficiency and high-value recycling of waste hemp fibers, the macromolecular structure, the supramolecular structure, and the morphological structure of waste hemp fibers were investigated by using Fourier transform infrared spectroscopy, X-ray diffractometry, upright metallurgical microscopy, and scanning electron microscopy. According to its structural characteristics, the sound-absorbing mechanism of waste hemp fiber was analyzed, and the reason for the good sound-absorbing performance of waste hemp fiber was clarified. The acoustic impedance transfer function test was used to analyze and compare the sound-absorbing performance of waste hemp fiber and several other fiber aggregates that could be used in the field of sound-absorbing, and the sound-absorbing performance of a waste hemp fiber composite material was tested. The research revealed that: the sequence of sound-absorbing performance of several fiber aggregates was cotton fiber, waste hemp fiber, wool fiber, and polyester fiber; that waste hemp fiber had excellent high-frequency sound-absorbing performance, with a maximum sound absorption coefficient of 0.95; and that the maximum sound absorption coefficient of the waste hemp fiber composite reached 0.93. Therefore, the waste hemp fiber has excellent sound-absorbing properties and has high application value in the field of sound absorption.

To broaden the application fields of waste hemp stalks, the macromolecular, supramolecular, and morphological structures of waste hemp stalks were analyzed, and the relationship between these properties and the sound absorption properties of the hemp stalks was explored. Then, waste hemp stalk/polycaprolactone sound-absorbing composite materials were prepared by the hot pressing method. The influence of hemp stalk length and mass fraction, and the density and thickness of the composite materials on the sound absorption properties of composites prepared with the hot pressing temperature set to 140 °C, the pressure set to 8 MPa, and the pressing time set to 30 min was investigated. The results showed that, when the sound energy acts on the hemp stalk, the force between the chain segments, the unique hollow structure, and the large specific surface, act together to attenuate the sound energy and convert it into heat and mechanical energy in the process of propagation, to produce a good sound absorption effect. When the hemp stalk length and mass fraction were set to 6 mm and 50%, respectively, and the density and thickness of the material were set to 0.30 g/cm³ and 1.5 cm, respectively, the average sound absorption coefficient of the waste hemp stalk/polycaprolactone sound-absorbing composite material was 0.44, the noise reduction coefficient was 0.42, the maximum sound absorption coefficient was 1.00, and the sound-absorbing band was wide. The study provided an experimental and theoretical basis for the development of waste hemp stalk/polycaprolactone sound-absorbing composite materials, and provided a new idea for the recycling of the waste hemp stalk.

In order to solve defects such as poor integrity, delamination failure, and narrow absorption bandwidth, three-dimensional (3D) gradient honeycomb woven composites (GHWCs) with triangular sections were designed and prepared. Three-dimensional gradient honeycomb woven fabric was crafted with carbon fiber (CF) filaments and basalt fiber (BF) filaments as raw materials on an ordinary loom. Then, the 3D honeycomb woven fabric filled with rigid polyurethane foam was used as the reinforcement, and epoxy resin (EP) doped with carbon black (CB) and carbonyl iron powder (CIP) was conducted as the matrix. The 3D GHWC with triangular sections, which had both EM-absorbing and load-bearing functions, was prepared by the VARTM process. Through the macro test and micro characterization of 3D GHWCs with triangular sections, the overall absorbing properties and mechanical properties of the materials were analyzed. Moreover, the EM-absorbing mechanism and failure mode of the materials were clarified in this work. The results indicated that the CF filament reflective layer effectively improved the EM-absorbing and mechanical properties. Adding a CB/CIP-absorbing agent enhanced the overall EM-absorbing property but reduced the mechanical properties. The increasing number of gradient layers increased the maximum bending load, but the EM-absorbing performance first increased and then decreased. When the thickness was 15 mm, the maximum bending load was 3530 N, and the minimum reflection loss (RL_min) was −21.6 dB. The synergistic effects of EM-absorbing and mechanical properties were the best right now. In addition, this work provided a feasible strategy that adjusting the type of absorber and gradient aperture size ratio could meet the unique requirements of absorbing frequency and intensity, which has excellent application prospects in civil and military fields.