A literature review of the five main theories describing the interaction mechanisms in the bitumen/aggregate system was conducted: theory of weak boundary layers, mechanical theory, electrostatic theory, chemical bonding theory, and thermodynamic theory (adsorption theory). The adhesion assessment methods in the bitumen/aggregate system are described, which can be divided into three main groups: determination of adhesion forces for bitumen with different materials, determination of bitumen resistance to the exfoliating action of water with different materials, and determination of adhesion as a fundamental value (contact angle measurements, interfacial fracture energy, adsorption capacity and others). It is proposed to evaluate the quality of adhesive interaction in the bitumen/aggregate system in two stages. The authors recommend using the adhesion determination methods for these two stages from the second group of methods the determination of bitumen resistance to the exfoliating action of water with different materials. In the first stage, the adhesion in the bitumen/aggregate system is determined by an accelerated technique in which the used bitumen binder and mineral material are considered as test materials. After the first stage, there are positive results in the second tests on compacted mixtures (indirect tensile strength test, Modified Lottman indirect tension test, immersion-compression test, and Hamburg wheel tracking test).

In this study, the phenol-cresol-formaldehyde (PhCR-F) resin was synthesised from the phenolic fraction of coal tar resin and formaldehyde through polycondensation. The physico-mechanical properties of the asphalt concrete were subsequently characterised to examine its water saturation, coefficient of long-term water-resistance (after 15 and 30 days), and compressive strength (at 20°C and 50°C). The results revealed that the addition of PhCR-F markedly increased the adhesion index with the surface of granite aggregates and glass before and after heating the bitumen. Furthermore, the PhCR-F addition enhanced the bitumen softening point, long-term water resistance, and thermo-stability but decreased the water-saturation index along with the penetration and ductility of bitumen. In conclusion, the study findings revealed that the synthesised PhCR-F resin is a promising adhesion promoter in pavement grade oil bitumen for application with asphalt concrete.

With the continuing growth of waste sulfur production from the petroleum industry processes, its utilization for the production of useful, low-cost, and environmentally beneficial materials is of primary interest. Elemental sulfur has a significant and established history in the modification of bitumen binders, while the sulfur-containing high-molecular compounds are limited in this field. Herein, we report a novel possibility to utilize the sulfur/organic copolymers obtained via the inverse vulcanization process as modifiers for bitumen binders. Synthesis and thermal characterization (TGA-DSC) of polysulfides derived from elemental sulfur (S₈) and unsaturated organic species (dicyclopentadiene, styrene, and limonene) have been carried out. The performance of modified bitumen binders has been studied by several mechanical measurements (softening point, ductility, penetration at 25 °C, frass breaking point, adhesion to glass and gravel) and compared to the unmodified bitumen from the perspective of normalized requirements concerning polymer-modified bitumen. The interaction of bitumen binder with sulfur/organic modifier has been studied by means of FTIR spectroscopy and DSC measurements. The impact of the modification on the performance properties of bitumen has been demonstrated. The bitumen binders modified with sulfur/organic copolymers are in general less sensitive to higher temperatures (higher softening point up to 7 °C), more resistant to permanent deformations (lower penetration depth), and more resistant to aging processes without intrusive deterioration of parameters at lower temperatures. What is more, the modification resulted in significantly higher adhesion of bitumen binders to both glass (from 25% up to 87%) and gravel surfaces in combination with a lower tendency to form permanent deformations (more elastic behavior of the modified materials).