In recent years, reduced graphene oxide (rGO) received considerable interest as a lubricant nano-additive for enhancing sliding and rolling contacts. This paper investigates the tribological and dynamic behavior of ball bearings lubricated by lithium grease at different weight percentages of rGO. Full bearing tests were conducted for experimental modal analysis, vibration analysis, ultrasonic analysis, and infrared thermography. Modal analysis indicated considerable improvements of the damping ratio values up to 50% for the bearings with rGO nano-additives. These findings were confirmed by the corresponding reductions in vibrations and ultrasound levels. The steady-state temperatures of bearings running with lithium grease reached 64 °C, whereas the temperature of bearings lubricated by grease with 2 wt.% rGO measured only 27 °C. A Timken Load test was conducted on grease samples with and without rGO additives. Grease samples having 2, 3.5, and 5 wt.% rGO showed the highest OK load with an increase of 25%, 50%, and 100% as compared to values of lithium grease. For comparison, all tests were conducted on samples of the same grease blended with graphite and MWCNTs’ nano-additives. The results proved the superiority of graphene in enhancing the load-carrying capacity and damping of grease in rolling bearings.

Bio-lubricants have demonstrated promising tribological and physical properties, suggesting their potential advantages in the lubrication of critical machinery components. This study investigates the impact of using blended individual and hybrid nanoadditives, such as graphene nanoplatelets, ZnO, and an ionic liquid (IL) of Trihexyltetradecylphosphonium bis(2,4,4-trimethylpentyl)phosphinate, on the rheological, tribological, and physical characteristics of rapeseed oil. A commercial cutting fluid (BLASER Vasco 6000) (VB 6000) is used for comparison. The results revealed a substantial improvement in viscosity index (VI) values for mixtures containing graphene nanoplatelets, reaching up to 150%, as compared to VB 6000. Regarding the tribological behavior, the friction coefficient achieved a reduction of up to 20% at room temperature (RT) and 26% at 60 °C for the hybrid containing all three nanoadditives (H3), outperforming the commercial fluid. Moreover, H3 demonstrated the most substantial reductions in wear volume (84%) and surface roughness (60%). The wettability of H3 benefited from the combined mechanisms of the applied nanoadditives; its application the contact angle decreased by 63%, revealing its outstanding spreadability. The results reveal the high potential of the H3 hybrid as a competitive and green metal working fluid that can replace hostile and toxic ones in industrial applications.

Graphene has been recently introduced as a promising material for various applications due to its outstanding mechanical, electrical, and thermal properties. It is classified as an allotropic form of carbon with the size of a single layer of graphite. This paper provides an extensive review regarding different critical applications of graphene including three categories namely: energy harvesting, strain sensors technology, and steel industry. The paper highlights what has been traversed in each category and provides an insight for researchers on what still needs to be investigated, which would open new horizons for scientific research and industrial applications. This field of research is expected to yield results that will have a considerable advance specially in 3D strain sensing technology. Also a special attention is given to the application of graphene in steel coating, steel welding, and lubrication.

A worldwide growing trend is dedicated towards reducing carbon dioxide emissions from mechanical systems in different industries. One key factor under focus of research is to decrease energy losses in rotating machinery during operation by improving lubrication performance. This paper presents a novel grease nano-additive using activated carbon (AC) as a byproduct from recycled polymer waste. Five different concentrations of AC nanoparticles (ACNPs) are added to lithium grease to obtain blends containing 0.025 wt.%, 0.05 wt.%, 0.1 wt.%, 0.5 wt.%, and 1 wt.%. The tribological assessment of blends has been performed using a four-ball wear test and load carrying capacity test. The obtained results for blends are compared to samples of base grease and to blends with 2 wt.% reduced graphene oxide (rGO). Test results showed a remarkable enhancement of load carrying capacity of AC samples by 20–30% as compared to base grease. By observing wear scar in rolling elements, the ACNPs lowered the average wear scar diameter (WSD) for all samples by 30–36%. Base grease samples showed the highest coefficient of friction (COF) values between 0.15 and 0.17. These values are reduced to 0.03 and 0.06 for grease with ACNPs reaching their minimum in the case of 1 wt.% AC. These outcomes are found consistent with the enhancements in driving power saving values. The results proved the competitiveness and suitability of the AC as a recycled waste and nano-additive for improving the tribological performance of grease lubrication.

The role of industrial lubricants in machinery is to reduce friction and wear between moving components. Due to the United Nations’ tendency to reduce dependency on fossil fuel, a general awareness is strongly driven towards developing more eco-friendly lubricants. Palm oil possesses promising properties, which promote it to be a competitive alternative to the hostile mineral oils. Still, marginal oxidation stability, viscosity, and tribological properties remain critical issues for performance improvement. This paper presents an improved palm grease using reduced graphene oxide (rGO) and zinc oxide (ZnO) nano-additives at different concentrations. Oil and grease samples were tested for viscosity, oxidation stability, pour point, penetration, roll stability, dropping point, churned grease-oil release, copper corrosion, friction, and wear. ZnO additives enhanced the oxidation stability by 60% and shifted the pour point to 6 °C. Adding ZnO and rGO to the palm grease increased the load-carrying capacity between 30% and 60%, respectively, and reduced the friction coefficient by up to 60%. From the wear scar morphologies, it is believed that graphene 2D nanoparticles formed absorption layers which contributed to the increase in load-carrying capacity, while ZnO chemically reacted with the metallic surface layer, forming zinc compounds that resulted in a protective boundary lubricating film.