In recent years, reduced graphene oxide (rGO) received considerable interest as a lubricant nano-additive for enhancing sliding and rolling contacts. This paper investigates the tribological and dynamic behavior of ball bearings lubricated by lithium grease at different weight percentages of rGO. Full bearing tests were conducted for experimental modal analysis, vibration analysis, ultrasonic analysis, and infrared thermography. Modal analysis indicated considerable improvements of the damping ratio values up to 50% for the bearings with rGO nano-additives. These findings were confirmed by the corresponding reductions in vibrations and ultrasound levels. The steady-state temperatures of bearings running with lithium grease reached 64 °C, whereas the temperature of bearings lubricated by grease with 2 wt.% rGO measured only 27 °C. A Timken Load test was conducted on grease samples with and without rGO additives. Grease samples having 2, 3.5, and 5 wt.% rGO showed the highest OK load with an increase of 25%, 50%, and 100% as compared to values of lithium grease. For comparison, all tests were conducted on samples of the same grease blended with graphite and MWCNTs’ nano-additives. The results proved the superiority of graphene in enhancing the load-carrying capacity and damping of grease in rolling bearings.

A worldwide growing trend is dedicated towards reducing carbon dioxide emissions from mechanical systems in different industries. One key factor under focus of research is to decrease energy losses in rotating machinery during operation by improving lubrication performance. This paper presents a novel grease nano-additive using activated carbon (AC) as a byproduct from recycled polymer waste. Five different concentrations of AC nanoparticles (ACNPs) are added to lithium grease to obtain blends containing 0.025 wt.%, 0.05 wt.%, 0.1 wt.%, 0.5 wt.%, and 1 wt.%. The tribological assessment of blends has been performed using a four-ball wear test and load carrying capacity test. The obtained results for blends are compared to samples of base grease and to blends with 2 wt.% reduced graphene oxide (rGO). Test results showed a remarkable enhancement of load carrying capacity of AC samples by 20–30% as compared to base grease. By observing wear scar in rolling elements, the ACNPs lowered the average wear scar diameter (WSD) for all samples by 30–36%. Base grease samples showed the highest coefficient of friction (COF) values between 0.15 and 0.17. These values are reduced to 0.03 and 0.06 for grease with ACNPs reaching their minimum in the case of 1 wt.% AC. These outcomes are found consistent with the enhancements in driving power saving values. The results proved the competitiveness and suitability of the AC as a recycled waste and nano-additive for improving the tribological performance of grease lubrication.

This paper presents a novel grease from jojoba oil and activated carbon nanoparticles (ACNPs) extracted from banana peel waste. The raw jojoba oil and ACNPs are first characterized for structural properties. Samples of jojoba grease blended with 0.5 and 1.5 wt. % ACNPs are prepared and tested for physicochemical and tribological properties as compared to plain jojoba grease. Adding ACNPs to jojoba grease improves corrosion resistance from grade 2c to 1a while increasing the dropping point from 100 to 109 °C. ACNPs enhanced the viscosity of jojoba oil by up to 33% for testing temperature range of 40–100 °C. The load-carrying capacity of jojoba grease is increased by about 60% when blended with 1.5 wt.% ACNPs. The same blending decreased both the coefficient of friction and the wear scar diameter by 38% and 24%, respectively. A customized test rig is used to test the effectiveness of the grease samples in rolling bearing lubrication in terms of vibration levels and power consumption. The novel jojoba grease proved to show exceptional reductions power consumption reaching 25%. The vibration spectra show the absence of resonant peaks at high frequencies suggesting the capability of jojoba grease to form a stable full film lubrication.