Traditional Portland cement is widely used in the preparation of various hydraulic concrete. However, the high alkalinity produced by cement hydration threatens the survival of aquatic animals and plants. In this paper, a new eco-friendly, ultra-low alkalinity, cementitious material was prepared with industrial waste phosphogypsum, granulated ground blast slag (GGBS) and sulphoaluminate cement. When appropriate proportions are used, the pH value of the test blocks’ pore solutions at different ages were all less than 9, showing the remarkable characteristic of ultra-low alkalinity. The XRD and SEM analyses showed that the 56 d hydration products were mainly ettringite and hydrated calcium silicate, and the content of Ca(OH)₂ was not detected. The new cementitious material also has the advantages of short setting time, low heat of hydration, high strength of cement mortar and the ability to fix harmful substances in phosphogypsum, such as phosphate, fluoride and Cr and Ba elements. It has a broad application prospect in the construction of island and reef construction, river restoration and so on.

The modification mechanism of low-molecular-weight organic acids on a single-chain silicate mineral (wollastonite) was investigated through a leaching method. Solid and liquid samples were analyzed using atomic absorption spectrophotometer (AAS), X-ray diffraction (XRD), scanning electron microscope (SEM), and Fourier-transform infrared spectroscopy (FTIR). After 720 h of reaction, the results revealed that the dissolution concentration of Si (2200 μmol/L) in citric acid solution is more than that (1950 μmol/L) in oxalic acid. In the composite acids (citric acid and oxalic acid), the dissolution concentration of Si release from wollastonite reached the maximum value of 3304 μmol/L. The dissolution data of Si in wollastonite were fittingly described by the parabolic equation (Ct = a + bt^1/2), with the highest correlation coefficients (R² > 0.993), in the presence of the low-molecular-weight organic acids. The dissolution data suggested that the dissolution reaction process of Si was consistent with the diffusion-controlled model. Citric acid exhibited a higher affinity for attacking the (200) surface, while oxalic acid was prone to dissolve the (002) crystal face. The synergistic effects of oxalic acid and citric acid led to the weakening of the XRD diffraction peak intensity of wollastonite. When exposed to composite acids, the surface of wollastonite was covered with insoluble reactants that restricted the substance diffusion and hindered the reaction. This study offers valuable theoretical insights into the modification or activation of wollastonite by composite low-molecular-weight organic acids.

Feldspar is a high-abundance mineral in the earth’s crust, and its natural weathering and dissolution processes are an important phenomenon on the earth’s surface. This study focused on the dissolution behavior of silicon (Si) and aluminum (Al) in feldspar minerals (microcline and albite) when exposed to low-molecular-weight organic acids (LMWOAs). Various analytical techniques, including atomic absorption spectrophotometer, X-ray diffraction, scanning electron microscope, and Fourier-transform infrared spectroscopy, were employed to investigate these processes. The results revealed that the concentration of Si and Al released from alkali feldspar increased after treatment with LMWOAs, exhibiting non-stoichiometric dissolution. The Si/Al release ratio from feldspar deviated from the expected value of three. Among the LMWOAs tested, oxalic acid was found to be more effective in dissolving aluminum, while citric acid showed greater efficacy in dissolving silicon. Notably, the composite acid demonstrated the highest capacity for feldspar dissolution, with values of 538 μM (Si) and 287 µM (Al) after treatment for 720 h, respectively. The dissolution data for Si and Al in the organic acid solution was fittingly described by a first-order equation, with high correlation coefficients (R² ≥ 0.992). The characterization of feldspar powders indicated that the (040) crystal plane of feldspar was particularly susceptible to attack by organic acids. In the presence of these acids, the chemical bonds Si (Al)-O, Si-Si(Al), and O-Si(Al)-O shifted to higher wavenumbers. Additionally, the surface corrosion morphology of feldspar exhibited distinct nanostructures, which became more pronounced with increasing exposure time. It was also observed that the reactivity of feldspar increased over time. These findings provide valuable insights into the natural dissolution process of feldspar and offer a new perspective for the study of this phenomenon.

A high sintering temperature is required to acquire excellent performance in the production of porcelain but results in high fuel consumption. To prepare the porcelain with outstanding performance at a lower temperature, a self-produced additive containing calcium (CaK) was added into a three-component system of kaolinite–feldspar–quartz. XRD and SEM were used to characterize the samples. The toughening mechanism and Gibbs free energy were investigated. After introducing the CaK, the bending strength of the porcelain fired at 1513 K increased from 56.32 ± 0.65 MPa to 95.31 ± 0.63 MPa, which was 21.83% higher than that of the porcelain without CaK at an optimal firing temperature of 1603 K. The main crystal phase of the sample comprised mullite and quartz in the raw materials at 1453~1603 K. The anorthite was observed at 1453 K and interlocked with needle-shaped mullite at 1513 K in the porcelain after adding CaK, which resulted in the higher bending strength. Quantitative analysis indicated that the amount of anorthite decreased at 1513 K and disappeared at 1543 K; the amount of mullite increased with temperature. The Gibbs free energy of the reaction (CaO•Al₂O₃•2SiO₂ + 2(Al₂O₃•2SiO₂) → 3Al₂O₃•2SiO₂ + CaO + 4SiO₂) at high temperature was negative, which suggested that the formation of mullite (3Al₂O₃•2SiO₂) from anorthite (CaO•Al₂O₃•2SiO₂) was possible. These findings implied that the addition of CaK contributed to the appropriate phase composition and microstructure, and the excellent performance of the porcelain at a lower temperature. In addition, the transformation between anorthite and mullite was possible in the special raw material system. The results are of interest in producing anorthite/mullite ceramics at reduced sintering temperatures and the conversion between anorthite and mullite.

The molecular clusters ((HO)₃Si-O-Si(OH)₃ and (HO)₃Al-O-Si(OH)₃) representative of aluminosilicate mineral surface were employed to study the dissolution of aluminosilicate in acidic condition via density functional theory (DFT) with the M06-2X+G(d,p) methodology. The surface termination sites (Si and Al) were both tetra-coordinated and the terminal oxygen was protonated in an acidic condition. In the dissolution reaction, the calculated barrier height of the six-membered ring transition state complex containing two water molecules was predicted to be 76.13 kJ/mol, lower than that of the four-membered ring transition state complex containing one water molecule. The barrier height of the reaction decreased to 6.17 kJ/mol and was 91.90% lower than that for the Si_ter-O-Si without protonation. In addition, the calculated barrier heights for Al-terminated sites were predicted to be 22.23 kJ/mol, lower than those for the Si-terminated sites, suggesting that breaking the Al-O bond is easier than the Si-O bond in the aluminosilicate mineral surface. With the fracture of Si-O and Al-O bonds, the Si and Al release from the aluminosilicate. The results indicate that the acidic condition facilitates the release of Si and Al from the aluminosilicate, and the concentration of Al leaching from the aluminosilicate is higher than the Si.

A three-dimensional porous bacterial cellulose/graphene oxide (BC/GO) composite hydrogel (BC/GO) was synthesized with multi-layer graphene oxide (GO) as the modifier and bacterial cellulose as the skeleton via an ultrasonic shaking process to absorb lead ions effectively. The characteristics of BC/GO were investigated through TEM, SEM, FT-IR, NMR and Zeta potential experiments. Compared to bacterial cellulose, the ultrasonic method and the carboxyl groups stemming from GO helped to enhance the availability of O(3)H of BC, in addition to the looser three-dimensional structure and enriched oxygen-containing groups, leading to a significantly higher adsorption capacity for Pb(II). In this paper, the adsorption behavior of BC/GO is influenced by the GO concentration, adsorption time, and initial concentration. The highest adsorption capacity for Pb(II) on BC/GO found in this study was 224.5 mg/g. The findings implied that the pseudo-second-order model explained the BC/GO adsorption dynamics and that the data of its adsorption isotherm fit the Freundlich model. Because of the looser three-dimensional structure, the complexation of carboxyl groups, and the enhanced availability of O(3)H, bacterial cellulose exhibited a much better adsorption capacity.