In food packaging, smart indicator films based on natural resources have greatly attracted researchers to minimize the environmental issues as well as to satisfy consumer preferences for food safety. In this research, pH-sensitive films were prepared using purple-fleshed sweet potato starch (SPS) and sweet potato peel (SPP). Two categories of the film (i) SPS and (ii) SPS/SPP, were fabricated via solvent casting technique, incorporating different concentrations of commercial purple sweet potato anthocyanin (CA) at 0%, 1%, 1.5%, and 2% (w/v) and the physicochemical, mechanical, thermal, and morphological properties of the films were investigated. The thickness, water solubility, and swelling degree of the films increased with the increment of CA, whereas there were no significant changes in the water content (WC) of the films. Water vapor permeability (WVP) was decreased for SPS films while statistically similar for SPS/SPP films. The addition of CA reduced the tensile strength (TS) and tensile modulus (TM) yet increased the elongation at break (EaB) of the films as compared to films without CA. The FTIR results confirmed the immobilization of anthocyanin into the film. In SEM images, roughness in the surfaces of the CA-associated films was observed. A reduction of thermal stability was found for the films with anthocyanin except for the SPS/SPP CA 2% film. Furthermore, the CA-associated films showed a remarkable color response when subjected to pH buffers (pH 1 to 12) and successfully monitored chicken freshness. The fastest color migration was observed in acidic conditions when the films were immersed into aqueous, acidic, low fat, and fatty food simulants. The findings of this work demonstrated that the developed pH indicator films have the potential to be implemented as smart packaging to monitor food freshness and quality for safe consumption.

According to the Food Wastage Footprint and Climate Change Report, about 15% of all fruits and 25% of all vegetables are wasted at the base of the food production chain. The significant losses and wastes in the fresh and processing industries is becoming a serious environmental issue, mainly due to the microbial degradation impacts. There has been a recent surge in research and innovation related to food, packaging, and pharmaceutical applications to address these problems. The underutilized wastes (seed, skin, rind, and pomace) potentially present good sources of valuable bioactive compounds, including functional nutrients, amylopectin, phytochemicals, vitamins, enzymes, dietary fibers, and oils. Fruit and vegetable wastes (FVW) are rich in nutrients and extra nutritional compounds that contribute to the development of animal feed, bioactive ingredients, and ethanol production. In the development of active packaging films, pectin and other biopolymers are commonly used. In addition, the most recent research studies dealing with FVW have enhanced the physical, mechanical, antioxidant, and antimicrobial properties of packaging and biocomposite systems. Innovative technologies that can be used for sensitive bioactive compound extraction and fortification will be crucial in valorizing FVW completely; thus, this article aims to report the progress made in terms of the valorization of FVW and to emphasize the applications of FVW in active packaging and biocomposites, their by-products, and the innovative technologies (both thermal and non-thermal) that can be used for bioactive compounds extraction.

This work aims to develop corn starch/chitosan nanoparticles/thymol (CS/CNP/Thy) bio-nanocomposite films as potential food packaging materials that can enhance the shelf life of food. CS/CNP/Thy bio-nanocomposite films were prepared by the addition of different concentrations of thymol (0, 1.5, 3.0, 4.5 w/w%) using a solvent casting method. The resulting films were characterized in terms of optical, mechanical, and water vapor permeability (WVP) properties. The addition of thymol was found to reduce the tensile strength (TS), elongation at break (EAB), and Young’s modulus (YM) of the films. Generally, the increment in the concentration of thymol did not significantly affect the TS, EAB, and YM values. The addition of 1.5 w/w% thymol increased the WVP of the films but the WVP reduced with the increase in thymol concentrations. CS/CNP/Thy-3% bio-nanocomposite films demonstrated the potential to lengthen the shelf life of cherry tomatoes packed with the films, whereby the cherry tomatoes exhibited no significant changes in firmness and the lowest weight loss. In addition, no mold growth was observed on the sliced cherry tomatoes that were in direct contact with the films during 7 days of storage, proving the promising application of the films as active food packaging materials.

Starch-based nanocomposite films containing chitosan nanoparticles (S/CNP films) are biodegradable and promising alternatives for non-biodegradable synthetic plastics. Nonetheless, limited work has been conducted to investigate the biodegradability of the films in soil. Thus, this work is aimed at investigating the biodegradation of starch-based films containing different concentrations of CNP (0, 10, 15, 20, 25% w/w solid starch) via a soil burial test using compost and planting soils. The biodegradability was investigated in terms of weight loss, visual appearance, morphology, and structural changes. It was found that S/CNP films biodegraded slower than neat starch films, and the degradation rate was reduced by 46 and 44% in compost and planting soils, respectively, with the increase in the concentrations of CNP from 10 to 25% w/w incorporated into the films. The degradation rate of films in compost soil after 8 days was found to be higher (0.0617 g/day) than in planting soil (0.0266 g/day). Visual appearance, morphology, and structural change results also supported these findings. The biodegradable S/CNP films can be used to reduce the usage of synthetic plastic.

Despite the utilization of dusting flour and oil to reduce dough stickiness during the production process in food industry, they do not effectively help in eliminating the problem. Stickiness remains the bane of the production of bakery and confectionery products, including cookies. In addition, the high moisture content of cookie dough is unduly important to obtain a high breaking and compression strengths (cookies with high breaking tolerance). This study was conducted in light of insufficient research hitherto undertaken on the utilization of response surface methodology and superimposition to enhance the stickiness and moisture content of quick oat-based cookie dough. The study aims at optimizating, validating and superimposing the best combination of factors, to produce the lowest stickiness and highest moisture content in cookie dough. In addition, the effect of flour content and resting time on the stickiness and moisture content of cookie dough was also investigated, and microstructure analysis conducted. The central composite design (CCD) technique was employed and 39 runs were generated by CCD based on two factors with five levels, which comprised flour content (50, 55, 60, 65, and 70%), resting time (10, 20, 30, 40, and 50 min) and three replications. Results from ANOVA showed that all factors were statistically significant at p < 0.05. Flour content between 56% and 62%, and resting time within 27 and 50 min, resulted in dough with high stickiness. High-region moisture content was observed for flour content between 60% and 70%, and within 10 and 15 min of resting time. The optimized values for flour content (V₁) = 67% and resting time (V₂) = 10 min. The predicted model (regression coefficient model) was found to be accurate in predicting the optimum value of factors. The experimental validation showed the average relative deviation for stickiness and moisture content was 8.54% and 1.44%, respectively. The superimposition of the contour plots was successfully developed to identify the optimum region for the lowest stickiness and highest moisture content which were at 67–70% flour content and 10–15 min resting time.