The depletion of petroleum-based resources and the adverse environmental problems, such as pollution, have stimulated considerable interest in the development of environmentally sustainable materials, which are composed of natural fiber–reinforced polymer composites. These materials could be tailored for a broad range of sustainable industrial applications with new surface functionalities. However, there are several challenges and drawbacks, such as composites processing production and fiber/matrix adhesion, that need to be addressed and overcome. This review could provide an overview of the technological challenges, processing techniques, characterization, properties, and potential applications of NFRPC for sustainable industrial applications. Interestingly, a roadmap for NFRPC to move into Industry 4.0 was highlighted in this review.

The development of antimicrobial packaging has been growing rapidly due to an increase in awareness and demands for sustainable active packaging that could preserve the quality and prolong the shelf life of foods and products. The addition of highly efficient antibacterial nanoparticles, antifungals, and antioxidants to biodegradable and environmentally friendly green polymers has become a significant advancement trend for the packaging evolution. Impregnation of antimicrobial agents into the packaging film is essential for impeding or destroying the pathogenic microorganisms causing food illness and deterioration. Higher safety and quality as well as an extended shelf life of sustainable active packaging desired by the industry are further enhanced by applying the different types of antimicrobial packaging systems. Antimicrobial packaging not only can offer a wide range of advantages, but also preserves the environment through usage of renewable and biodegradable polymers instead of common synthetic polymers, thus reducing plastic pollution generated by humankind. This review intended to provide a summary of current trends and applications of antimicrobial, biodegradable films in the packaging industry as well as the innovation of nanotechnology to increase efficiency of novel, bio-based packaging systems.

According to the Food Wastage Footprint and Climate Change Report, about 15% of all fruits and 25% of all vegetables are wasted at the base of the food production chain. The significant losses and wastes in the fresh and processing industries is becoming a serious environmental issue, mainly due to the microbial degradation impacts. There has been a recent surge in research and innovation related to food, packaging, and pharmaceutical applications to address these problems. The underutilized wastes (seed, skin, rind, and pomace) potentially present good sources of valuable bioactive compounds, including functional nutrients, amylopectin, phytochemicals, vitamins, enzymes, dietary fibers, and oils. Fruit and vegetable wastes (FVW) are rich in nutrients and extra nutritional compounds that contribute to the development of animal feed, bioactive ingredients, and ethanol production. In the development of active packaging films, pectin and other biopolymers are commonly used. In addition, the most recent research studies dealing with FVW have enhanced the physical, mechanical, antioxidant, and antimicrobial properties of packaging and biocomposite systems. Innovative technologies that can be used for sensitive bioactive compound extraction and fortification will be crucial in valorizing FVW completely; thus, this article aims to report the progress made in terms of the valorization of FVW and to emphasize the applications of FVW in active packaging and biocomposites, their by-products, and the innovative technologies (both thermal and non-thermal) that can be used for bioactive compounds extraction.

Compressive strength is an important property in construction material, particularly for thermal insulation purposes. Although the insulation materials possess high fire-retardant characteristics, their mechanical properties are relatively poor. Moreover, research on the correlation between fire-retardant and compressive strength of rice husk ash (RHA)-based geopolymer binder (GB) is rather limited. In addition, previous studies on RHA-based GB used the less efficient one-factor-at-a-time (OFAT) approach. In understanding the optimum value and significant effect of factors on the compressive strength, it was deemed necessary to employ statistical analysis and a regression coefficient model (mathematical model). The objective of the study is to determine the effect of different material behavior, namely brittle and ductile, on the compressive strength properties and the optimum material formulation that can satisfy both compressive strength and fire-retardant properties. The factors chosen for this study were the rice husk ash/activated alkaline solution (RHA/AA) ratio and the sodium hydroxide (NaOH) concentration. Compressive strength and fire-retardant tests were conducted as part of the experiments, which were designed and analyzed using the response surface methodology (RSM). The microstructure of geopolymer samples was investigated using a scanning electron microscope (SEM). Results showed that RHA/AA ratio was highly significant (p < 0.000) followed by NaOH concentration (p < 0.024). When the RHA/AA ratio was at 0.7 to 0.8 and the NaOH concentration was between 12 and 14 M, high compressive strength above 28 MPa was recorded. Optimum compressive strength of approximately 47 MPa was achieved when the RHA/AA ratio and NaOH concentration were 0.85 and 14 M, respectively. Brittle samples with low Si/Al ratio of 88.95 were high in compressive strength, which is 33.55 MPa, and showed a high degree of geopolymerization. Inversely, ductile samples showed low compressive strength and degree of geopolymerization. Water content within the geopolymer binder had a major effect on its fire-retardant properties. Semi-ductile GB showed the best fire-retardant properties, followed by semi-brittle and brittle GB. Using RHA as an aluminosilicate source has proven to be a promising alternative.

If the coating is sufficiently flexible, no tears, cracks, or debond will occur. Although geopolymers have a great potential as a coating material, research on the flexural properties is very limited. In this study, a three-point bending test and scanning electron microscope were used to investigate the flexural properties and microstructure of the geopolymer composite coating (GCC), respectively. Response Surface Methodology (RSM) consists of a combination of mathematical and statistical techniques, which is useful in modelling, analyzing, and optimizing responses that are influenced by several factors. It was used in determining the relationship between each factor and determining the best composition for the composite coating. Several factors were considered including ratio of activated alkaline (AA) solution (V₁), RHA/AA ratio (V₂), and curing temperature (V₃). Results showed that the RHA/AA ratio mostly influenced the response, followed by curing temperature while the ratio of AA was not significant. Lower V₂ and V₃ values provided the highest flexural strength and modulus. The optimum composition which provided the best coating of flexural properties were V₁ = 3.5, V₂ = 0.39, and V₃ = 45.7 °C. Microscopic images showed that coating with high flexural properties (ductile coating) exhibited minor and rough cracks as compared to that of coating with low flexural properties (brittle coating) which displayed a crack with a clean linear cut. Brittle coating was highly agglomerated and has a significant negative effect on the flexural properties. By developing the optimum composition, the GCC may potentially be a good alternative as a building construction coating material.