Flax shive is the main waste (up to 70 wt %) in the production of flax fiber. It represents the lignified parts of the flax stem mainly in the form of small straws. Complex processing of such wastes is a significant problem due to the heterogeneity of the chemical structure of lignin. This article presents the results of reductive catalytic fractionation (RCF) of flax shive in ethanol and isopropanol at elevated temperatures (225–250 °C) in the presence of a bifunctional catalyst (Ru/C) and molecular hydrogen. This provides solvolytic depolymerization of lignin and hemicelluloses presented in flax shive. Catalytic hydrogenation effectively stabilizes the formed lignin intermediates and prevents repolymerization reactions producing the lignin fraction with a high degree of depolymerization. RCF of flax shive produces solid products with a high cellulose content and liquid products consisting mainly of monophenolic compounds. Furthermore, the effect of different characteristics (the ruthenium content, particle size, and support acidity) of the bifunctional catalysts containing ruthenium nanoparticles supported on mesoporous, graphite-like carbon material Sibunit^®-4 on the yield and composition of the products of hydrogenation of flax shive in sub- and super-critical ethanol has been studied. Bifunctional catalysts Ru/C used in the RCF of flax shive increase its conversion from 44 to 56 wt % and the yield of monophenols from 1.1 to 10.2 wt % (based on the weight of lignin in the sample). Using the best Ru/C catalyst containing 3% of Ru on oxidized at 400 °C carbon support, the high degree of delignification (up to 79.0%), cellulose yield (up to 67.2 wt %), and monophenols yield (up to 9.5 wt %) have been obtained.

In this study, hemicelluloses of aspen wood (Pópulus trémula) were obtained by oxidative delignification in an acetic acid‒water‒hydrogen peroxide medium at temperatures of 70‒100 °C and a process time of 1‒4 h. The maximum polysaccharide yield of up to 9.68 wt% was reported. The composition and structure of the hemicelluloses were studied using a complex of physicochemical methods: gas and gel permeation chromatography, Fourier-transform infrared spectroscopy, 2D nuclear magnetic resonance spectroscopy, and thermogravimetric analysis. The xylose, mannose, galactose, and glucose monomer units were identified in the hemicelluloses by gas chromatography. The weight average molecular weight M_w of the products determined by gel permeation chromatography was found to range within 8932‒33,142 g/mol. The reported Fourier-transform spectra of the hemicelluloses contain all the bands characteristic of heteropolysaccharides; a weak lignin absorption signal in the spectra at 1500‒1510 cm⁻¹ is attributed to a minor content of phenolic fragments in the structure of the obtained hemicelluloses. The use of thermogravimetric analysis established that the hemicelluloses isolated from aspen wood are resistant against heating to temperatures of up to 90–100 °C and, upon further heating up to 400 °C, start destructing at an increasing rate. The antioxidant activity of the hemicelluloses was examined using the compounds that mimic free radicals (1,1-diphenyl-2-picrylhydrazyl) and hydroxyl radicals (salicylic acid). It was found that the activity of all polysaccharides in neutralizing DPPH and hydroxyl radicals is lower than the absorption capacity of vitamin C at all the tested concentrations (0.5, 2, and 5 mg/mL) and attains 81.7 and 82.9%, respectively.

Reductive catalytic fractionation (RCF) has emerged as an effective lignin-first biorefinery strategy to depolymerize lignin into tractable fragments in high yields. Herein, we propose the RCF of spruce wood over a Ru/C bifunctional catalyst in the medium of ethanol and molecular hydrogen to produce monomeric phenolic compounds from lignin, polyols from hemicelluloses, and microcrystalline cellulose. This contribution attempts to elucidate the role of the Ru/C bifunctional catalysts characteristics. The results clarify the particular effect of the carbon support acidity, catalyst grain size, content and dispersion of Ru on the effectiveness of lignin and hemicelluloses extraction and the yields of liquid and gaseous products. The most efficient catalysts for RCF of spruce wood, providing high yields of the monomeric phenols, glycols, and solid product with content of cellulose up to 90 wt%, bear 3 wt% of Ru with a dispersion of 0.94 based on an acidic oxidized graphite-like carbon support Sibunit^®, and having a grain size of 56–94 μm. The Ru/C catalysts intensify the reactions of hydrodeoxygenation of liquid products from lignin. The main phenolic monomers are 4-propyl guaiacol, 4-propenyl guaiacol, and 4-propanol guaiacol. We explored the effect of the process temperature and time on the yield and composition of the liquid, solid, and gaseous products of spruce wood RCF. The optimal trade-off between the yields of phenolic monomers (30.0 wt%). polyols (18.6 wt%) and the solid product containing 84.4 wt% of cellulose is reached at 225 °C and 3 h over the most acidic Ru/C catalyst.

Thermal conversion of flax shives was studied in sub- and supercritical ethanol medium at 225 and 250 °C in the presence of the bifunctional catalyst 3% Ru/C. The use of 3% Ru/C catalyst in the process of thermal conversion of flax shives in supercritical ethanol was found to increase the conversion of the shives by 27% and the yield of liquid products by 10%. The use of 3% Ru/C catalyst in sub- and supercritical ethanol led to the destruction of both lignin and cellulose. The degree of delignification in the non-catalytic thermal conversion increased upon transition from subcritical (225 °C) to supercritical (250 °C) conditions. Main monomeric products of the thermal conversion process were guaiacylpropene or guaiacylpropane depending on the process temperature. In the presence of Ru/C catalyst, the molecular weight distribution was shifted towards an increase in the content of monomeric compounds in the liquid products.

Cellulose sulfates are important biologically active substances with a wide range of useful properties. The development of new methods for the production of cellulose sulfates is an urgent task. In this work, we investigated ion-exchange resins as catalysts for the sulfation of cellulose with sulfamic acid. It has been shown that water-insoluble sulfated reaction products are formed in high yield in the presence of anion exchangers, while water-soluble products are formed in the presence of cation exchangers. The most effective catalyst is Amberlite IR 120. According to gel permeation chromatography, it was shown that the samples sulfated in the presence of the catalysts KU-2-8, Purolit s390 plus, and AN-31 SO₄²⁻ underwent the greatest degradation. The molecular weight destribution profiles of these samples are noticeably shifted to the left towards low-molecular-weight compounds with an increase in fractions in the regions Mw ~2.100 g/mol and ~3.500 g/mol, indicating the growth of microcrystalline cellulose depolymerization products. The introduction of a sulfate group into the cellulose molecule is confirmed using FTIR spectroscopy by the appearance of absorption bands at 1245–1252 cm⁻¹ and 800–809 cm⁻¹, which correspond to the vibrations of the sulfate group. According to X-ray diffraction data, amorphization of the crystalline structure of cellulose is observed during sulfation. Thermal analysis has shown that with an increase in the content of sulfate groups in cellulose derivatives, thermal stability decreases.

During magnetron sputtering of graphite using hydrogen as plasma-forming gas, a material sputtered from the target deposited only on heated substrates. When using currentheated Ni-Fe foils as...