The conducted research aimed to evaluate the influence of admixtures of various modified starches on the rheological properties of cement composites and their influence on the compressive strength of hardened cement mortars. The study involved 17 different modified starch admixtures. Using a rheometer, the values of viscosity and tangential stresses were determined depending on the shear rate, and were subsequently used to determine the yield point and plastic viscosity of cement slurries. The next parameters tested were the flow of fresh cement slurry and the compressive strength of hardened cement composite. The highest fluidisation was recorded for retentate LU-1420-0.5%Ac-R, an increase of 82%. The conducted tests led to the conclusion that admixing cement composites with modified starches changes the rheological parameters and the compressive strength of cement composites. The highest strength gains occurred for the admixtures of retentate LU-1412-R (increase of 25%). Declines in compressive strength were noticed in the retentate LU-1422-R (decrease by 13%) and the retentate OSA-2.5%-R (decrease of 17%). The admixture of starch hydrolysate significantly decreases the yield point of slurries, which in turn may contribute to the fluidisation of concrete mixes and the reduction of mixing water. The lowest values were obtained for retentates LU-1420-0.5%Ac-R (decrease of 94%), and LU-1412-R (decrease of 93%). It was found that the consistency and compressive strength of cement mortars are affected by both the type of modification and the length of the chemical chain of starch.

Growing interest in the use of natural organic compounds in the production of green concrete with the use of plasticizers has been particularly noticeable in the literature of recent decades. Starch is an attractive material due to its abundance, the low cost of sourcing it, and its biodegradability, biocompatibility, and susceptibility to modification. The objective of the study was to evaluate the effect of starch hydrolysate additives on the physicochemical properties of cement composites and concrete. Compressive strength tests and cement slurry rheology measurements were carried out for water–cement ratios from 0.40 to 0.50 and for amounts of added dextrin from 0.0 to 0.7% in relation to the cement weight. The dextrins used were characterized in terms of their viscosity, polymerisation degree, and surface activity in air/water systems. Conducted research indicates that even the minimum content of dextrin increases the fluidization of cement mixes (the flow diameter increased by 67.5% compared with the mixture without the admixture), enables the reduction of mixing water, and contributes to the compressive strength of cement mortars. A further decrease in the w/c ratio to the value of 0.40 resulted in an increase in the strength value of up to 67.9 MPa, which provided a 40% increase in strength. The degree of the polymerisation of added dextrin is seen as having an effect on the physical parameters of the cement mortar; the shorter the polymer chain of the studied dextrin, the more packed the adsorbent layer, and the greater the flow diameter of the cement mortar.

The food industry extensively uses chemically modified starches and their hydrolysates, which is mainly due to their emulsification ability. Therefore, it becomes inevitable to develop new starch derivatives, including modified starch hydrolysates, and effective preparation methods to meet the increasing demands of producers, consumers, and technology. This study comprehensively researches the physical, chemical, and functional properties (such as the water-binding capacity, swelling power, solubility, and fat absorption capacity) of chemically modified biopolymers and their enzymatic hydrolysis products. We utilized oxidized and acetylated potato and waxy-corn starches with varying degrees of substitution by carboxyl and acetyl groups in our research. The process of enzymatic hydrolysis was performed in a recirculated membrane reactor (CRMR). Our findings indicated that the physicochemical properties of starch derivatives and their hydrolysates depended on the biological origin of the biopolymer and the type and degree of modification. However, the presence of carboxyl groups in the modified starch molecules is critical and affects the rheological properties and water-binding capacity of the starch preparations. For example, in the case of waxy-corn starch preparations with a lower content of carboxyl groups (i.e., derivatives with a low degree of oxidation), the water-binding capacity (WBC) increases when compared to native starch. The highest WBC value of 206.3% was noted for the doubly modified waxy-corn starch with an oxidation degree of 0.2% and an acetylation degree of 2.5%, while native waxy-corn starch shows a WBC of 161.4%. In contrast, it was observed that preparations with a higher content of carboxyl groups, i.e., derivatives with an oxidation degree of 2.5%, show a lower swelling power compared to native waxy starch.

Selenium nanoparticles (SeNPs) were synthesized and stabilized by biopolymers, namely, sodium lignosulfonate (LS) and starch sodium octenyl succinate (OSA). The obtained selenium nanoparticles were studied for their catalytic activity in the reduction of a dye (C.I. Basic Blue 9, methylene blue) by sodium borohydride. The SeNPs-OSA and SeNPs-LS nanoparticles were also dispersed in a photosensitive matrix and studied as polymer composites. The research confirmed the catalytic abilities of the prepared SeNPs in the reduction of the organic dye. Mechanical tests on the polymers and their composites showed an improvement in the composites’ strength in all tested cases. An increase in hardness and Young’s modulus values of the filled materials compared to the pure matrix was found as well.

The adsorption behavior of walnut shells in the presence of colloidal gold for thallium(I) ions from aqueous solution was investigated. The thallium content in the samples before and after contact with walnut shells was determined by differential pulse anodic stripping voltammetry. The adsorption capacity was studied in relation to the function of equilibrium time, the amount of adsorbent, the concentration of thallium, and pH. For the sake of comparison, the sorptive properties of walnut shells were compared to soapnut powder. The obtained results clearly indicate that both walnut shells and soap nuts are effective sorbents for thallium(I) ions (removal efficiency over 90%). The best results of sorption were achieved at pH = 7.5 after contact time of 30 min. The addition of colloidal gold stabilised by lignosulfonate as the co-adsorber enhances the sorption ability of walnut shells to over 99%.