Although, quantum dots (QDs) of two-dimensional (2D) molybdenum disulfide (MoS₂) have shown great potential for various applications, such as sensing, catalysis, energy storage, and electronics. However, the lack of a simple, scalable, and inexpensive fabrication method for QDs is still a challenge. To overcome this challenge, a lot of attention has been given to the fabrication of QDs, and several fabrication strategies have been established. These exfoliation processes are mainly divided into two categories, the ‘top-down’ and ‘bottom-up’ methods. In this review, we have discussed different top-down exfoliation methods used for the fabrication of MoS₂ QDs and the advantages and limitations of these methods. A detailed description of the various properties of QDs is also presented.

Many of the previously reported preparation methods for MoS2quantum dots (QDs) are limited by production rate, time consumption, tedious processes or the final quality of the as-prepared QDs....

Composite materials made of polymer and clay are effective at blocking mass transport. In this study, the blocking efficacy of layer-by-layer (LbL) coatings of exfoliated montmorillonite (MMT) and polyethylenimine (PEI) was studied using cyclic voltammetry and a redox couple, indigo carmine (IC). The pH of the MMT solution was varied from 4 to 10 to prepare LbL coatings of different surface roughness on metal substrates. It was found that the coated electrode had a lower redox peak current value than without the coating, demonstrating the reduction of the mass transport of IC to the metal surface. The peak values decreased with decreasing the coating’s roughness and increasing the number of layers, indicating that the blocking capability can be controlled by changing the deposition conditions. Smooth LbL coatings deposited with MMT at pH 4 showed the highest blocking efficacy up to 97.5%. The IC adsorbed at the interface between the coating and the metal substrate was found to cause the peak current measured for the coated electrode. It was also confirmed that the same coating on the copper substrate reduced the corrosion of the copper during the electrochemical potential cycling.