Among the various welding techniques used to bond thermoplastic composites, induction welding stands out as a fast, clean, and contact-free process that shortens the welding time and prevents the weight increase of mechanical fastening, such as rivets and bolts. In this study, we manufactured polyetheretherketone (PEEK)-resin-based thermoplastic carbon fiber (CF) composite materials at different automated fiber placement laser powers (3569, 4576, and 5034 W) and investigated their bonding and mechanical characteristics after induction welding. The quality of the composite was evaluating using various techniques, including optical microscopy, C-scanning, and mechanical strength measurements, and a thermal imaging camera was used to monitor the surface temperature of the specimen during its processing. The results revealed that the preparation conditions of the polymer/carbon fiber composites, such as the laser power and surface temperature, significantly affect the quality and performance of the induction-welding-bonded composites. A lower laser power during preparation resulted in weaker bonding between components of the composite and yielded samples with a lower shear stress.

Conventional thermosetting composites exhibit advantageous mechanical properties owing to the use of an autoclave; however, their wide usage is limited by high production costs and long molding times. In contrast, the fabrication of thermoplastic composites involves out-of-autoclave processes that use press equipment. In particular, induction-heating molding facilitates a quicker thermal cycle, reduced processing time, and improved durability of the thermoplastic polymers; thus, the process cost and production time can be reduced. In this study, carbon fiber/polyphenylene sulfide thermoplastic composites were manufactured using induction-heating molding, and the relationships among the process, structure, and mechanical properties were investigated. The composites were characterized using optical and scanning electron microscopy, an ultrasonic C-scan, and X-ray computed tomography. In addition, the composites were subjected to flammability tests. This study provides novel insights into the optimization of thermoplastic composite manufacturing and thermoset composite curing processes.