In this work, Ni₃V₂O₈ (NVO) and Ni₃V₂O₈-reduced graphene oxide (NVO-rGO) are synthesized hydrothermally, and their extensive structural, morphological, and electrochemical characterizations follow subsequently. The synthetic materials’ crystalline structure was confirmed by X-ray diffraction (XRD), and its unique marigold-like morphology was observed by field emission scanning electron microscopy (FESEM). The chemical states of the elements were investigated via X-ray photoelectron spectroscopy (XPS). Electrochemical impedance spectroscopy (EIS), Galvanostatic charge–discharge (GCD), and cyclic voltammetry (CV) were used to assess the electrochemical performance. A specific capacitance of 132 F/g, an energy density of 5.04 Wh/kg, and a power density of 187 W/kg were demonstrated by Ni₃V₂O₈-rGO. Key electrochemical characteristics were b = 0.67; a transfer coefficient of 0.52; a standard rate constant of 6.07 × 10⁻⁵ cm/S; a diffusion coefficient of 5.27 × 10⁻⁸ cm²/S; and a series resistance of 1.65 Ω. By employing Ni₃V₂O₈-rGO and activated carbon, an asymmetric supercapacitor with a specific capacitance of 7.85 F/g, an energy density of 3.52 Wh/kg, and a power density of 225 W/kg was achieved. The series resistance increased from 4.27 Ω to 6.63 Ω during cyclic stability tests, which showed 99% columbic efficiency and 87% energy retention. The potential of Ni₃V₂O₈-rGO as a high-performance electrode material for supercapacitors is highlighted by these findings.

This paper introduces a novel chemical reduction synthesis method for preparing bimetallic Zn-doped perovskite NiMnO ₃ ultrafine nanocrystals, which are further supported on reduced graphene oxide (rGO).