The hydrothermal method has been utilized to synthesize graphitic carbon nitride (g-C₃N₄) polymers and cobalt oxide composites effectively. The weight percentage of g-C₃N₄ nanoparticles influenced the electrochemical performance of the Co₃O₄-g-C₃N₄ composite. In an aqueous electrolyte, the Co₃O₄-g-C₃N₄ composite electrode, produced with 150 mg of g-C₃N₄ nanoparticles, revealed remarkable electrochemical performance. With an increase in the weight percentage of g-C₃N₄ nanoparticles, the capacitive contribution of the Co₃O₄-g-C₃N₄ composite electrode increased. The Co₃O₄-g-C₃N₄-150 mg composite electrode shows a specific capacitance of 198 F/g. The optimized electrode, activated carbon, and polyvinyl alcohol gel with potassium hydroxide were used to develop an asymmetric supercapacitor. At a current density of 5 mA/cm², the asymmetric supercapacitor demonstrated exceptional energy storage capacity with remarkable energy density and power density. The device retained great capacity over 6k galvanostatic charge–discharge (GCD) cycles, with no rise in series resistance following cyclic stability. The columbic efficiency of the asymmetric supercapacitor was likewise high.

This review article focuses on the potential of cobalt oxide composites with conducting polymers, particularly polypyrrole (PPy) and polyaniline (PANI), as advanced electrode materials for supercapacitors, batteries, and supercapatteries. Cobalt oxide, known for its high theoretical capacitance, is limited by poor conductivity and structural degradation during cycling. However, the integration of PPy and PANI has been proven to enhance the electrochemical performance through improved conductivity, increased pseudocapacitive effects, and enhanced structural integrity. This synergistic combination facilitates efficient charge transport and ion diffusion, resulting in improved cycling stability and energy storage capacity. Despite significant progress in synthesis techniques and composite design, challenges such as maintaining structural stability during prolonged cycling and scalability for mass production remain. This review highlights the synthesis methods, latest advancements, and electrochemical performance in cobalt oxide/PPy and cobalt oxide/PANI composites, emphasizing their potential to contribute to the development of next-generation energy storage devices. Further exploration into their application, especially in battery systems, is necessary to fully harness their capabilities and meet the increasing demands of energy storage technologies.

Energy harvesting systems fabricated from rubber composite materials are promising due to their ability to produce green energy with no environmental pollution. Thus, the present work investigated energy harvesting through piezoelectricity using rubber composites. These composites were fabricated by mixing titanium carbide (TiC) and molybdenum disulfide (MoS₂) as reinforcing and electrically conductive fillers into a silicone rubber matrix. Excellent mechanical and electromechanical properties were produced by these composites. For example, the compressive modulus was 1.55 ± 0.08 MPa (control) and increased to 1.95 ± 0.07 MPa (6 phr or per hundred parts of rubber of TiC) and 2.02 ± 0.09 MPa (6 phr of MoS₂). Similarly, the stretchability was 133 ± 7% (control) and increased to 153 ± 9% (6 phr of TiC) and 165 ± 12% (6 phr of MoS₂). The reinforcing efficiency (R.E.) and reinforcing factor (R.F.) were also determined theoretically. These results agree well with those of the mechanical property tests and thus validate the experimental work. Finally, the electromechanical tests showed that at 30% strain, the output voltage was 3.5 mV (6 phr of TiC) and 6.7 mV (6 phr of MoS₂). Overall, the results show that TiC and MoS₂ added to silicone rubber lead to robust and versatile composite materials. These composite materials can be useful in achieving higher energy generation, high stretchability, and optimum stiffness and are in line with existing theoretical models.