Optically transparent wood is a type of composite material, combining wood as a renewable resource with the optical and mechanical properties of synthetic polymers. During this study, the effect of monochromatic UV-C (λ—250 nm) radiation on transparent wood was evaluated. Samples of basswood were treated using a lignin modification method, to preserve most of the lignin, and subsequently impregnated with refractive-index-matched types of acrylic polymers (methyl methacrylate, 2-hydroxyethyl methacrylate). Optical (transmittance, colour) and mechanical (shore D hardness) properties were measured to describe the degradation process over 35 days. The transmittance of the samples was significantly decreased during the first seven days (12% EMA, 15% MMA). The average lightness of both materials decreased by 10% (EMA) and 17% (MMA), and the colour shifted towards a red and yellow area of CIE L*a*b* space coordinates. The influence of UV-C radiation on the hardness of the samples was statistically insignificant (W+MMA 84.98 ± 2.05; W+EMA 84.89 ± 2.46), therefore the hardness mainly depends on the hardness of used acrylic polymer. The obtained results can be used to assess the effect of disinfection of transparent wood surfaces with UV-C radiation (e.g., due to inactivation of SARS-CoV-2 virus) on the change of its aesthetic and mechanical properties.

Fire-retardant (FR) treated wood-based panels, used commonly in furniture and construction, need to meet stringent fire safety regulations. This study presents a novel treatment for imparting fire resistance to wood composites by applying separate solutions of phytic acid and sodium silicate onto wood particles before the hot pressing at 160 °C. A scanning electron microscopy-energy dispersive X-ray spectroscopy (SEM-EDX) analysis revealed that phytic acid and sodium silicate were uniformly distributed throughout the wood particles, and the formation of silica gel resulted in the aggregation of elemental silicon. Fourier-transform infrared spectroscopy (FTIR) displayed that phytic acid caused the thermal degradation of hemicelluloses, which led to a brownish outer appearance of the FR-treated composites. Fire performance was assessed using both limiting oxygen index (LOI) and a cone calorimeter. These techniques showed a higher LOI value and a significant reduction in heat-release rate (HRR), total heat release (THR), smoke-production rate (SPR), and total smoke production (TSP). In addition, cone calorimeter and thermogravimetric (TGA) analyses consistently showed increased char residue in treated wood composites. Moreover, internal bond strength (IB) and modulus of elasticity (MOE) of the wood composite were not significantly changed compared with those of the untreated composite. Surprisingly, in the FR-treated composite, the 24 h-thickness swelling, and the water uptake were slightly decreased. Consequently, this new treatment has the potential to increase the fire retardancy of wood composites, such as particleboard, without deteriorating the key mechanical properties.

Methanol and ethanol are among the most important biofuels and raw materials used to produce biorenewable fuels. These fuels are used with varying water contents. Nevertheless, the exact impact of the water content of these fuels on the energy potential and combustion characteristics is still unknown. Besides that, there are two noticeable risks (environmental impact of combustion and fire risk) associated with their production, processing, and utilization. Likewise, impact of the water content of these fuels on fire risk and the impact of their combustion on the environment is also unknown. The best indicator of energy potential is the effective heat of combustion, and the best combustion characteristic and indicator of the impact of the combustion of alcohols on the environment is the carbon monoxide (CO) yield, whereas the fire risk of liquid fuels is quantified by the flash point and maximum heat release rate (mHRR). The dependency of flash point on the water content was determined via the Pensky-Martens apparatus and the dependencies of the effective heat of combustion, CO yield, and mHRR on the water content were determined via the cone calorimeter. With increased water content, the flash points of both methanol and ethanol exponentially increased and the both effective heat of combustion and mHRR almost linearly decreased. In the range of water content from 0 to 60%, the CO yield of both methanol and ethanol was practically independent of the water content.

Heat release rate (HRR) is the principal fire characteristic of materials. There are three known methods for the measurement of HRR (based on oxygen consumption, mass loss rate, and combustion products temperature rise). The method based on oxygen consumption is considered to be the reference. However, this method is expensive and for a large part of laboratories and universities unavailable. The simplest method is based on combustion products’ temperature rise. However, this method has a fundamental problem with the temperature dependence of the heat capacity of combustion products and the thermal inertia of the measurement system. This problem has been solved by training neural networks to predict molar heat capacity and the amount of substance (chemical amount) flow rate of combustion products in the cone calorimeter exhaust duct. Data were obtained for six different wood species: birch (Betula verrucosa Ehrh.), oak (Quercus robur L.) spruce (Picea abies (L.) H. Karst.), locust (Robinia pseudoacacia L.), poplar (Populus nigra × P. maximowiczii L.), and willow (Salix alba L.) woods at heat fluxes from 25 to 50 kW m⁻² have been used for neural network training. Data from three other wood species iroko (Milicia excelsa (Welw.) C.C. Berg), pine (Pinus sylvestris L.), and paulownia (Paulownia tomentosa (Thunb.) Steud.) woods have been used for testing of trained neural network. The average percentage ratio of the predicted to the true value of HRR (during the test) has been 103.8%. In addition to that, some key average fire characteristics of wood have been determined: critical heat flux 20.7 kW m⁻², effective heat of combustion 14.01 MJ kg⁻¹, and the average value of molar heat capacity of combustion products 0.045 kJ mol⁻¹ K⁻¹.

This study focuses on the energy potential and combustion process of torrefied wood. Samples were prepared through the torrefaction of five types of wood: Ash, beech, oak, pine and spruce. These were heated for 2 h at a temperature of 300 °C under a nitrogen atmosphere. Torrefied wood was prepared from wood samples with dimensions of 100 × 100 × 20 mm³. These dimensions have enabled investigation of torrefied wood combustion in compact form. The effect of the external heat flux on the combustion of the samples was measured using a cone calorimeter. The observed parameters, include initiation times, heat release rate and combustion efficiency. The results show that increasing the external heat flux decreases the evenness of combustion of torrefied wood. At the same time, it increases the combustion efficiency, which reached an average value of approximately 72% at 20 kW m⁻², 81% at 30 kW m⁻² and 90% at 40 kW m⁻². The calculated values of critical heat flux of the individual samples ranged from 4.67 kW m⁻² to 15.2 kW m⁻², the thermal response parameter ranged from 134 kW s^0.5 m⁻² to 297 kW s^0.5 m⁻² and calculated ignition temperature ranged from 277 °C to 452 °C. Obtained results are useful both for energy production field and for fire safety risk assessment of stored torrefied wood.

Aim of this study was to evaluate the effect of aluminium hydroxide and borates, separately or combined with ammonium polyphosphate (APP), upon the technological and fire properties of medium density fibreboard (MDF). Fire resistant MDF was fabricated in the laboratory from Scots pine (Pinus sylvestris L.) fibres bonded with a high molar ratio melamine-urea-formaldehyde resin. Overall, 24 h-swelling and water absorption properties of the treated boards were improved or remained unchanged compared to untreated ones. On the contrary, the internal bond strength (IB) of the fibreboards was significantly reduced up to 48%. The fire properties of the fibreboards were assessed by the determination of limiting oxygen index and cone calorimetry. As expected, the tested fire-retardants improved the fire resistance of the boards. Furthermore, the combination of aluminium hydroxide with ammonium polyphosphate considerably upgraded the fire retardancy while the incorporation of borates into APP showed much weaker effects.