Natural plant fibers represent a sustainable alternative to conventional fiber reinforcement materials in cementitious materials due to their suitable mechanical properties, cost-effective availability and principle carbon neutrality. Due to its high tensile strength and stiffness as well as its worldwide distribution along with rapid growth, bamboo offers itself in particular as a plant fiber source. In experimental studies on concrete beams reinforced with plant fibers, a positive influence of the fibers on the flexural behavior was observed. However, the load-bearing effect of the fibers was limited by the poor bond, which can be attributed, among other things, to the swelling behavior of the fibers. In addition, the plant fibers degrade in the alkaline environment of many cementitious building materials. In order to improve the bond and to limit the alkalinity and to increase the durability, the use of ultra-high performance concrete (UHPC) offers itself. Since no tests have been carried out, investigations on the flexural behavior of UHPC with bamboo fibers were carried out at the Institute of Concrete Construction of Leibniz University Hannover. The test results show a significantly improved load-bearing behavior of the fibers and the enormous potential of the combination of UHPC and bamboo fibers.

Due to its high strength, the use of ultra-high-performance concrete (UHPC) is particularly suitable for components subjected to compressive loads. Combined with its excellent durability, UHPC can be used to produce highly resource-efficient components that represent a sustainable alternative to conventional load-bearing structures. Since UHPC fails in a brittle manner without the addition of fibers, it is typically used in conjunction with micro steel fibers. The production of these steel fibers is both expensive and energy-intensive. Natural plant fibers, due to their good mechanical properties, cost-effective availability, and inherent CO₂ neutrality, can provide a sustainable alternative to conventional steel fibers. Thanks to the low alkaline environment and dense matrix of UHPC, the use of natural plant fibers in terms of durability and bond is possible in principle. For the application of natural plant fibers in UHPC, however, knowledge of the load-bearing and post-cracking behavior or the performance of UHPC reinforced with natural plant fibers is essential. Currently, there are no tests available on the influence of different types of natural plant fibers on the load-bearing behavior of UHPC. Therefore, five series of compression and bending tensile tests were conducted. Three series were reinforced with natural plant fibers (bamboo, coir, and flax), one series without fibers, and one series with steel fibers as a reference. Under compression loads, the test specimens reinforced with natural plant fibers did not fail abruptly and exhibited a comparable post-failure behavior and damage pattern to the reference specimens reinforced with steel fibers. In contrast, the natural plant fibers did not perform as well as the steel fibers under bending tensile stress but did show a certain post-cracking bending tensile strength. A final life cycle assessment demonstrates the superiority of natural plant fibers and shows their positive impact on the environment.