We show that the switchable mirror material ${\mathrm{YH}}_x$ can be used both as an indicator to monitor and as an agent to control hydrogen diffusion in thin films. The applicability of the optical-indicator technique is demonstrated for ${\mathrm{VH}}_x$ thin films. The diffusion coefficient is typically ${10}^{-5}{\mathrm{cm}}^2/\mathrm{s}$ at concentrations around 0.7 H/V at temperatures between 373 and 473 K. Deposition of a layer of Y on V makes it also possible to tune the effective hydrogen mobility via the V/Y thickness ratio. This can be used for investigation of hydrogen diffusion waves in laterally structured objects.

Chitosan is one of the most commonly employed natural polymers for biomedical applications. However, in order to obtain stable chitosan biomaterials with appropriate strength properties, it is necessary to subject it to crosslinking or stabilization. Composites based on chitosan and bioglass were prepared using the lyophilization method. In the experimental design, six different methods were used to obtain stable, porous chitosan/bioglass biocomposite materials. This study compared the crosslinking/stabilization of chitosan/bioglass composites with ethanol, thermal dehydration, sodium tripolyphosphate, vanillin, genipin, and sodium β-glycerophosphate. The physicochemical, mechanical, and biological properties of the obtained materials were compared. The results showed that all the selected crosslinking methods allow the production of stable, non-cytotoxic porous composites of chitosan/bioglass. The composite with genipin stood out with the best of the compared properties, taking into account biological and mechanical characteristics. The composite stabilized with ethanol is distinct in terms of its thermal properties and swelling stability, and it also promotes cell proliferation. Regarding the specific surface area, the highest value exposes the composite stabilized by the thermal dehydration method.

Hydroxyapatite (HAp) of different morphologies was prepared by the direct decomposition of calcium lactate pentahydrate chelates using dipotassium hydrogen phosphate under hydrothermal conditions. The proposed technique allows for precise control of the HAp crystals morphology and product purity, which are necessary for biomedical applications. The synthesis parameters such as reagent concentrations, pH, reaction time, temperature, pressure, and stirring rate were optimized in order to produce calcium phosphates (CaPs) ceramics with restricted morphologies and composition. As a result, we obtained hydroxyapatite in the form of whiskers, hexagonal rods, nano particles, flowers, and cylinders. The products were characterized according to their structure (FTIR and XRD), morphology (SEM), and functional properties, i.e., the specific surface area. The obtained results indicate that the reagent concentration and pH values have the greatest impact on the HAp properties; however, the proper combination of all the mentioned parameters should be considered when there is a need for a bioceramic with defined physicochemical properties and an appropriate morphology.

The rheological properties of shear thickening fluids based on silica powder of particles size in range 0.10 – 2.80 μm and poly(propylene glycol) of 425, 1000, 2000 g/mol molar mass were investigated. The effect of particle size and the length of the polymeric chain was considered. The objective of this study was to understand basic trends of physicochemical properties of used materials on the onset and the maximum of shear thickening and dilatant effect. Outcome of the research suggested that an increase in the particle size caused a decrease in dilatant effect and shift towards higher shear rate values. Application of carrier fluid of higher molar mass allowed to increase dilatant effect but it resulted in the increase of the initial viscosity of the fluid.

The development of innovative biomaterials with improved integration with bone tissue and stimulating regeneration processes is necessary. Here, we evaluate the usefulness of bioactive glasses from the SiO₂-P₂O₅-CaO system enriched with 2 wt.% SrO or ZnO in the manufacturing of chitosan-based scaffolds. Bioglasses produced using the sol-gel method were subjected to thermal treatment in different regimes. Chitosan/bioglass composites were produced with a weight ratio. Bioglasses were evaluated via TG-DTA, FTIR, and SEM-EDS before and after incubation in simulated body fluid (SBF). The release of ions was tested. The cytocompatibility of the composites in contact with MG63 osteoblast-like cells was evaluated. The results showed that the presence of the crystalline phase decreased from 41.2–44.8% for nonmodified bioglasses to 24.2–24.3% for those modified with ZnO and 22.0–24.2% for those modified with SrO. The samples released Ca²⁺, Zn²⁺, and/or Sr²⁺ ions and were bioactive according to the SBF test. The highest cytocompatibility was observed for the composites containing nonmodified bioglasses, followed by those enriched with SrO bioglasses. The least cytocompatible were the composites containing ZnO bioglasses that released the highest amount of Zn²⁺ ions (0.58 ± 0.07 mL/g); however, those that released 0.38 ± 0.04 mL/g were characterised by acceptable cytocompatibility. The study confirmed that it is feasible to control the biological performance of chitosan/bioglass composites by adjusting the composition and heat treatment parameters of bioglasses.