The rheological properties of shear thickening fluids based on silica powder of particles size in range 0.10 – 2.80 μm and poly(propylene glycol) of 425, 1000, 2000 g/mol molar mass were investigated. The effect of particle size and the length of the polymeric chain was considered. The objective of this study was to understand basic trends of physicochemical properties of used materials on the onset and the maximum of shear thickening and dilatant effect. Outcome of the research suggested that an increase in the particle size caused a decrease in dilatant effect and shift towards higher shear rate values. Application of carrier fluid of higher molar mass allowed to increase dilatant effect but it resulted in the increase of the initial viscosity of the fluid.

This work focuses on research on obtaining and characterizing Al₂O₃/ZrO₂ materials formed via slip casting method. The main emphasis in the research was placed on environmental aspects and those related to the practical use of ceramic materials. The goal was to analyze the environmental loads associated with the manufacturing of Al₂O₃/ZrO₂ composites, as well as to determine the coefficient of thermal expansion of the obtained materials, classified as technical ceramics. This parameter is crucial in terms of their practical applications in high-temperature working conditions, e.g., as parts of industrial machines. The study reports on the four series of Al₂O₃/ZrO₂ materials differing in the volume content of ZrO₂. The sintering process was preceded by thermogravimetric measurements. The fabricated and sintered materials were characterized by dilatometric study, scanning electron microscopy, X-ray diffraction, and stereological analysis. Further, life cycle assessment was supplied. Based on dilatometric tests, it was observed that Al₂O₃/ZrO₂ composites show a higher coefficient of thermal expansion than that resulting from the content of individual phases. The results of the life cycle analysis showed that the environmental loads (carbon footprint) resulting from the acquisition and processing of raw materials necessary for the production of sinters from Al₂O₃ and ZrO₂ are comparable to those associated with the production of plastic products such as polypropylene or polyvinyl chloride.

This paper focuses on the possibility of adapting the centrifugal slip casting method to obtain zirconia–alumina composite materials in the form of finished tube-shaped products. These types of products, due to their unique properties, can be utilised, for example, in the transport of aggressive substances, even in extreme temperatures or corrosive conditions. The study reports on the two series of zirconia–alumina composites differing in the content of ZrO₂—2.5 and 25 vol%. The fabricated and sintered materials were characterised using scanning electron microscopy (SEM), X-ray diffraction (XRD) and stereological analysis. Moreover, a life cycle assessment (LCA) was provided in accordance with the requirements of the ISO 14044 and EN 15805 standards. The obtained data clearly show that the centrifugal slip casting method allows obtaining samples with high density and extremely uniform distribution of the ZrO₂ phase in the alumina matrix. The stereological analysis results proved also that the addition of ZrO₂ is effective in reducing the growth of Al₂O₃ grains during the sintering process. The phase analysis carried out by means of XRD showed that during the sintering process, in the case of composites with a lower ZrO₂ content (2.5 vol%), the monoclinic to tetragonal transformation of ZrO₂ was total, while for samples containing 25 vol% ZrO₂, the monoclinic phase remained in a small amount in the final product.

Shear thickening fluids (STFs) are innovative materials that can find applications in smart body armor. However, the usage of STFs is limited by the aging of these materials. This work aims to analyze the influence of UV radiation on the aging process of STFs. The investigation was done experimentally, and artificial aging was applied to investigate the impact of UV radiation on the properties of STFs. The shear-thickening properties of obtained STFs were confirmed by viscosity measurements. The STFs based on PPG425, PPG2700, and KE-P10 exhibited a very high maximum viscosity of up to 580.7 Pa·s and 3313 Pa·s for the STF425 and STF2700, respectively. The aging of the obtained STFs caused the liquid matrix degradation, causing damage to the STFs and their change from liquid into solid. Furthermore, the FT-IR, ¹H NMR, and ¹³C NMR spectroscopies were used for the confirmation of the breakdown of STFs. The FT-IR spectroscopy revealed the appearance of carbonyl groups in STFs after aging. Moreover, ¹H NMR and ¹³C NMR spectroscopy confirmed the formation of the typical groups containing carbonyl groups. Our results demonstrate that STFs are UV light-sensitive and may lose their properties during storage.

The present work deals with the evaluation of the effect of ZrO₂ on the structure and selected properties of shapes obtained using the centrifugal slip casting method. The samples were made of alumina and zirconia. The applied technology made it possible to produce tubes with a high density reaching 99–100% after sintering. Very good bonding was obtained at the Al₂O₃/ZrO₂ interphase boundaries with no discernible delamination or cracks, which was confirmed by STEM observations. In the case of Al₂O₃/ZrO₂ composites containing 5 vol.% and 10 vol.% ZrO₂, the presence of equiaxial ZrO₂ grains with an average size of 0.25 µm was observed, which are distributed along the grain boundaries of Al₂O₃. At the same time, the composites exhibited a very high hardness of 22–23 GPa. Moreover, the environmental influences accompanying the sintering process were quantified. The impacts were determined using the life cycle analysis method, in the phase related to the extraction and processing of raw materials and the process of producing Al₂O₃/ZrO₂ composites. The results obtained show that the production of 1 kg of sintered composite results in greenhouse gas emissions of 2.24–2.9 kg CO₂ eq. which is comparable to the amount of emissions accompanying the production of 1 kg of Polyvinyl Chloride (PVC), Polypropylene (PP), or hot-rolled steel products.