Spinel ZnGa₂O₄ has received significant attention from researchers due to its wide bandgap and high chemical and thermal stability; hence, paving the way for it to have potential in various applications. This review focuses on its physical, optical, mechanical and electrical properties, contributing to the better understanding of this material. The recent trends for growth techniques and processing in the research and development of ZnGa₂O₄ from bulk crystal growth to thin films are discussed in detail for device performance. This material has excellent properties and is investigated widely in deep-ultraviolet photodetectors, gas sensors and phosphors. In this article, effects of substrate temperature, annealing temperature, oxygen partial pressure and zinc/gallium ratio are discussed for device processing and fabrication. In addition, research progress and future outlooks are also identified.

In this study, the hopping conduction distance and bipolar switching properties of the Gd:SiOx thin film by (radio frequency, rf) rf sputtering technology for applications in RRAM devices were calculated and investigated. To discuss and verify the electrical switching mechanism in various different constant compliance currents, the typical current versus applied voltage (I-V) characteristics of gadolinium oxide RRAM devices was transferred and fitted. Finally, the transmission electrons’ switching behavior between the TiN bottom electrode and Pt top electrode in the initial metallic filament forming process of the gadolinium oxide thin film RRAM devices for low resistance state (LRS)/high resistance state (HRS) was described and explained in a simulated physical diagram model.

We investigated the bipolar resistive switching characteristics of the resistive random access memory (RRAM) device with amorphous carbon layer. Applying a forming voltage, the amorphous carbon layer was carbonized to form a conjugation double bond conductive filament. We proposed a hydrogen redox model to clarify the resistive switch mechanism of high/low resistance states (HRS/LRS) in carbon RRAM. The electrical conduction mechanism of LRS is attributed to conductive sp² carbon filament with conjugation double bonds by dehydrogenation, while the electrical conduction of HRS resulted from the formation of insulating sp³-type carbon filament through hydrogenation process.

Spinel ZnGa₂O₄ films were grown on c-plane sapphire substrates at the substrate temperature of 400 °C by radio-frequency magnetron sputtering. Post thermal annealing was employed at the annealing temperature of 700 °C in order to enhance their crystal quality. The effect of thermal annealing on the microstructural and optoelectronic properties of ZnGa₂O₄ films was systematically investigated in various ambiences, such as air, nitrogen, and oxygen. The X-ray diffraction patterns of annealed ZnGa₂O₄ films showed the crystalline structure to have (111) crystallographic planes. Transmission electron micrographs verified that ZnGa₂O₄ film annealed under air ambience possesses a quasi-single-crystalline structure. This ZnGa₂O₄ film annealed under air ambience exhibited a smooth surface, an excellent average transmittance above 82% in the visible region, and a wide bandgap of 5.05 eV. The oxygen vacancies under different annealing ambiences were revealed a substantial impact on the material and photodetector characteristics by X-ray photoelectron spectrum investigations. ZnGa₂O₄ film exhibits optimal performance as a metal-semiconductor-metal photodetector when annealed under air ambience. Under these conditions, ZnGa₂O₄ film exhibits a higher photo/dark current ratio of ~10⁴ order, as well as a high responsivity of 2.53 A/W at the bias of 5 V under an incident optical light of 240 nm. These results demonstrate that quasi-single-crystalline ZnGa₂O₄ films have significant potential in deep-ultraviolet applications.

In this letter, the special role of hydrogen ions in hafnium doped silicon oxide resistive random access memory (RRAM) is presented. In addition to the more typical oxygen ion-dominated resistive switching, hydrogen ions were also observed to trigger a resistance transformation phenomenon, producing a tri-resistive device. Unlike a normal RRAM device, a hydrogen plasma-treated device is operated with a reversed voltage polarity, and the direction of hydrogen ion migration results in the chemical bonds breaking and repairing. By changing the voltage polarity and stop voltage, this tri-resistive behavior can be achieved. This particular hydrogen-induced switching behavior suggests a different RRAM switching mechanism and is finally explained by our model.