The purpose of this qualification work is to study the physical and mechanical behavior of concrete with the addition of 0.5% and 1% coconut fiber, which has been subjected to two chemical treatments to reduce its degradation. The coconut fibers were extracted from the raw material and cut into pieces 4 cm long. Subsequently, the fibers were subjected to two chemical treatments. The first involved immersing the fibers in 4% sodium hydroxide (NaOH) solution, and the second treatment involved coating them with gum arabic and silica fume. A total of 50 samples of fibers were collected in their natural and post-treated state to be tested. The dosage was prepared for design strengths of 210 and 240 kg/cm² (20.59 and 23.54 MPa), so that the percentages of 0.5% and 1% volume of coconut fiber, for the two treatments selected, replaced the respective volume of coarse aggregates. The cylinders with 1% addition of fibers had the best performance for the design strength of 20.59 MPa, including the cylinders without fibers. Those with 0.5% addition of fibers presented better performance for the 23.54 MPa dosage, although this was lower than the cylinders without fibers. In all cases, the cylinders with NaOH-treated fibers outperformed their counterparts with fibers treated with gum arabic and silica fume. Finally, a CO₂ balance was determined, and an environmental gain up to 14 kg in CO₂ emissions was established for each cubic meter of composite concrete.

Durante años se ha venido construyendo losas de hormigón sobre vigas de acero, sin embargo, el no considerar la trasmisión de esfuerzos de corte entre ellas, ocasiona que los elementos trabajen por separado. Para asegurar la transmisión de esfuerzos, la carga debe transmitirse mediante conectores mecánicos. En la construcción comúnmente se utilizan pernos stud, perfiles angulares y tornillos como conectores, aunque no todos se encuentren normados. El presente trabajo analiza el comportamiento de conectores de corte tipo ángulo, cuando están localizados de diferente manera a la expuesta en códigos de diseño. Para ello, se consideraron conectores de corte tipo ángulo, colocados de manera perpendicular respecto a la cara del patín de la viga de acero, analizando dos tipos de posiciones (45 y 90° referente al eje longitudinal del patín). Para comprobar cuál tiene un comportamiento y resistencia adecuada, se realizaron ensayos push-out, con un total de 6 probetas por posición. Las curvas fuerza vs. deslizamiento obtenidas del conector a 45°, presentaron un comportamiento más homogéneo en todos los parámetros analizados, en comparación con las curvas obtenidas para el conector a 90°. Su óptimo rendimiento hace que el conector a 45° sea el más adecuado para implementación.

The objective of this work is to study the physical and mechanical behavior of concrete with the addition of 0.5% and 1.0% of coconut fibers subjected to two chemical treatments in order to reduce their degradation and optimize their use in the elaboration of concrete specimens, which must comply with the standards of the American Society for Testing of Materials (ASTM), the American Concrete Institute (ACI) and the Instituto Ecuatoriano de Normalización (INEN). The coconut fibers were obtained from the raw material by hand and cut to a length of 4 cm. Subsequently, the coconut fibers were subjected to two chemical treatments: The first treatment is the immersion of the coconut fibers in 4% sodium hydroxide (NaOH) solution and the second treatment, the coconut fibers were immersed in gum arabic to consequently coat them with silica fume. A particular dosage was carried out with a proportion of 0.5% and 1.0% volume of coconut fiber for the two chemical treatments, replacing the volume of coarse aggregate. Simple concrete joists were made without fiber and with the post-treatment coconut fibers, which were subjected to flexural tests. The results indicated that the best chemical treatment is sodium hydroxide with a concentration of 4% and 1.0% coconut fiber for strengths of 210 kg/cm² and 240 kg/cm². In general, the joists with coconut fiber treated with sodium hydroxide outperformed the fibers treated with gum arabic and silica fume.

The present article is oriented to the reinforcement of a house built informally with 3 floors located in the citadel Emprovit, Turubamba sector in the south of the city of Quito - Ecuador, which, through field visits and laboratory tests, obtained all the data necessary for the correct development of the work. The structural system of the house is based on frames assembled by columns, lightened slab in two directions and band beams. An evaluation was made in accordance with the parameters established by the NEC15 and ASCE 41-17 standards, in which it results that the house has a high seismic vulnerability, in addition, that the structural analysis resulted in that it does not have a good behavior. dynamic, in addition to this, the building does not perform well in the non-linear range, so structural reinforcement is necessary. Two strengthening alternatives may be needed in order to withstand major seismic events, wall cladding and column cladding. It will be extended that the alternative with the best results is the cladding of walls, since it improves its lateral and dynamic behavior, in addition to not exceeding the admissible stress of the soil, on the contrary, the cladding of columns, although it improves the dynamic behavior , the soil stress exceeds the admissible one, so it is necessary to reinforce the foundation, in addition to this, with the proposed sections, the drifts do not comply with the regulations, so larger sections are necessary, which will cause a much higher cost of reinforcement and an impact to the architectural part, due to the reduction of spaces. El presente artículo se orienta al reforzamiento de una vivienda construida de manera informal, de tres plantas, ubicada en la ciudadela Emprovit, sector Turubamba en el sur de la ciudad de Quito, Ecuador. Mediante visitas de campo y ensayos de laboratorio se obtuvieron todos los datos necesarios para el correcto desenvolvimiento del trabajo. El sistema estructural de la vivienda se basa en pórticos constituidos por columnas, losa alivianada en dos direcciones y vigas banda. Se hizo una evaluación de acuerdo con los parámetros establecidos por las normas NEC15 y ASCE 41-17, la cual dio como resultado que la vivienda tiene una vulnerabilidad sísmica alta, además, el análisis estructural arrojó que no posee un buen comportamiento dinámico. Adicional a esto, la edificación no cumple con un buen desempeño en el rango no lineal, por lo que es necesario un reforzamiento estructural. Se propuso dos alternativas de reforzamiento con el objetivo de soportar eventos sísmicos importantes, el enchapado de paredes y el encamisado de columnas. Se determinó que la alternativa con mejores resultados es el enchapado de paredes, ya que mejora su comportamiento lateral y dinámico, además de no superar el esfuerzo admisible del suelo; por el contrario, el encamisado de columnas, si bien mejora el comportamiento dinámico, el esfuerzo del suelo supera al admisible, por lo que es necesario un reforzamiento a la cimentación. Adicionalmente, con las secciones propuestas, las derivas no cumplen en relación con la normativa, razón por la cual se requieren secciones más grandes, que causan un costo de reforzamiento mucho más elevado y un impacto a la parte arquitectónica, debido a la reducción de espacios.

En la investigación que aquí se presenta se evaluó el comportamiento estructural de dos viviendas adosadas construidas de manera informal, las cuales mostraban diversos problemas estructurales como: golpeteo, columnas cortas y discontinuidad de columnas; se determinaron las propiedades mecánicas de los materiales y de suelo por medio de ensayos in situ y de laboratorio. Posteriormente, se realizó el análisis mediante modelos matemáticos, mismos que se calibraron con periodos tomados de vibraciones ambientales. En esta etapa se encontró que las estructuras no exhibían un comportamiento adecuado para resistir fuerzas gravitacionales y sísmicas, por lo que se propuso el reforzamiento de ambas estructuras por medio del enchape de mampostería, además se planteó unir ambas viviendas a nivel de losa con placas metálicas para eliminar el problema del golpeteo. Finalmente, se evaluó el reforzamiento propuesto y se evidenció que el enchape rigidizó las estructuras permitiendo que estas cumplan con los requisitos establecidos por la normativa vigente a bajo costo

La falta de planificación desde una etapa temprana en el sector de la construcción ha dado lugar a un crecimiento vertical, haciendo necesarios edificios cada vez más altos y esbeltos, en consecuencia, los elementos compuestos se presentan como una alternativa que busca cubrir las deficiencias que los materiales muestran al trabajar exclusivamente de manera individual. Partiendo de esto, se realizó un estudio comparativo técnico y económico con el propósito de analizar el aporte que tienen las columnas compuestas dentro de un sistema estructural porticado, para el cual se propuso la modelación de dos estructuras de acero con pórticos especiales resistentes a momentos, una con columnas rectangulares de acero huecas y la otra con columnas rectangulares de acero rellenas de hormigón. Se analizaron parámetros como modos de vibración, cortante basal, derivas de piso, peso propio de la estructura y costos. Como resultado se concluye que la estructura con columnas rectangulares rellenas de hormigón presenta un buen comportamiento estructural utilizando perfiles de menor espesor en comparación a la estructura con columnas rectangulares de acero huecas, lo que se traduce en un menor costo. Además, se evidenció que las columnas compuestas presentan una mayor capacidad de carga axial por compresión.