The use of Supplementary Cementitious Materials (SCMs) or industrial wastes as a partial replacement for cement in the production of concrete is an urgent need in the construction industry due to cement's growing environmental challenges and rising cost. In respect of this, we conducted research work on proportioning binary concrete mixes. Fly ash (FA) replaced 10 %, 20 %, and 30 % of the cement, while silica fume (SF) replaced 5 %, 10 %, and 15 % of the cement. A control concrete mix was also developed with 100 % cement and no SCM. The results showed no increase in compressive strength for FA concrete compared to control at the early age of 3–28 days, but a maximum increase in compressive strength of 4 % was discovered at a later age of 56 days for concrete with 20 % FA. For 5 % SF concrete, a considerable strength increase of 15 % was seen at the early age of 3 days. Like with FA concrete, 2 % improvement in strength was recorded at the later age of 56 days for 10 % SF concrete. This study further focused on the concrete's temporal evolution of compressive strength by developing a strength evolution model (SEM) using nonlinear regression analysis at a 95 % confidence level. Pearson correlation coefficient was used to determine the correlation between the model values and the experimental results. For comparison, the fib Model Code 2010 was applied to the experimental data, and a good agreement was observed among the proposed model, the fib Model values, and the experimental results. The proposed model can be expanded to address further regression-related problems. Finally, environmental life cycle assessment revealed that utilizing 10 %, 20 %, and 30 % of FA lowered Global Warming Potential (GWP) by 9 %, 19 %, and 29 %, respectively. Likewise, using 5 %, 10 %, and 15 % of SF reduced the GWP by 5 %, 9 %, and 14 %.

Sufficient deformability can be achieved in concrete while maintaining segregation resistance either by using a chemical viscosity-modifying admixture (VMA) or increasing the fine content in the concrete. Using VMA, the initial cost of self-compacting concrete (SCC) increases, making it unsuitable for general construction. As a result, alternative methods for lowering the cost of SCC must be investigated. In this study, we assess the effectiveness of fly ash (FA) as a viscosity-modifying agent in the production of cost-effective and durable SCC. We also forge new pathways for sustainable development. The percentage of FA, superplasticizer dose, and water/binder ratio were varied, whereas the amounts of cement and water, as well as fine/coarse aggregate content were kept constant. Fresh properties, such as flow, filling and passing abilities, viscosity, and segregation resistance, were measured. Compressive/flexural strength, density, water absorption, and rate of water absorption of hardened SCC were also determined. The test results showed that fly ash can be used as an alternative to a VMA to produce cost-effective, self-compacting concrete. The slump flow of the various fresh-state concrete mixes ranged from 200 to 770 mm, with an L-box ratio of 0 to 1 and a flow time of 2.18 to 88 s. At 28 and 56 days, the compressive strengths of the concrete mixes with fly ash were found to be comparable to those of the control concrete mixes with VMA. The cost of ingredients for a specific SCC mix is 26.8% lower than the price of control concrete, according to a cost comparison assessment.

In this research study, environmentally friendly unburnt coal ash (CA) bricks were investigated as an alternative to conventional burnt clay bricks. In this research study, various physical and mechanical properties of unburnt CA bricks were investigated. The unburnt CA bricks were prepared by using 60% CA and 10% lime by weight. In these unburnt CA bricks, varying cement contents (5%, 10%, and 15%), sand contents (10% and 15%), and quarry dust contents (5% and 10%) by weight were used. A forming pressure of 29 MPa was applied through an automatic pressure control system either for 3 s or 6 s. The prepared bricks were moist cured for 28 days. The experimental results exhibited that unburnt CA bricks with 10% cement, 10% sand, and 10% quarry dust subjected to forming pressure for 3 s exhibited the highest compressive strength of 19 MPa and flexural strength of 2.1 MPa. The unburnt CA bricks exhibited reduced water absorption, reduced efflorescence, and lower weight per unit area than the conventional clay bricks. A cost comparison of unburnt CA bricks and clay bricks exhibited that unburnt CA bricks are cost-effective compared to clay bricks.

This study investigates the shear behavior of slender steel-reinforced geopolymer concrete (GPC) beams with the shear span to effective depth ratio ($a/d$) of 4.5 and 5.0. To investigate the effect of shear reinforcement, two ordinary Portland cement concrete (OPC) beams and two GPC beams without shear reinforcement, and two OPC beams and two GPC beams reinforced with shear stirrups were cast. All beams were 150 mm wide and 225 mm deep with lengths of 1770 mm ($a/d=4.5$) and 1950 mm ($a/d=5$). The beams were tested under a three-point bending test. The experimental results showed that OPC and GPC beams without and with shear reinforcements exhibited similar crack propagation and failure mechanism. The midspan deflections of GPC beams were greater than OPC beams. The normalized shear resistance of OPC and GPC beams with $a/d$ ratio 4.5 was greater than 4% and 30%, respectively, than beams with $a/d$ ratio 5. OPC beams showed a greater decrease in shear resistance with an increasing $a/d$ ratio compared to GPC beams. The shear resistances computed using empirical relationships available in various OPC design codes including AC1-318-14, AC1-318-19, fib-10 and JSCE-07 underestimated the experimental shear resistance of both OPC and GPC beams. In addition, the environmental assessment of OPC and GPC beams exhibited that GPC beams emit about 34% lower embodied CO₂ emissions than OPC beams.

While openings are an essential requirement in buildings as a source of access, fresh air and sunlight, these openings cause a reduction in the lateral stiffness and torsional resistance of masonry wall units. A detailed numerical investigation was carried out to explore the impact of the opening percentage on the in-plane stiffness and lateral strength of unconfined and confined masonry wall panels prepared using calcium silicate bricks, for sustainable masonry structures. A commercially available FEM package (ANSYS) was used to carry out comparative analysis of ten wall panels, five of each type (confined and unconfined masonry walls) with concentrically located openings of varying sizes (0% to 16.5%). A simplified micro-modeling technique following the Newton Raphson Algorithm was adopted. Results revealed that the confined masonry approach unveiled a more reliable anti-seismic response along with improved in-plane strength in the case of confined masonry walls. The failure type shifted from pure flexural to more of a blend of shear and flexure after the opening percentage increased to 10.09% in unconfined masonry walls, which was not the case where confinement was provided. Based on the outcomes, it is strongly recommended to adopt confined masonry in highly seismic-prone areas to avoid catastrophic damage caused by earthquakes.