Magnetoresistive (MR) sensors have been identified as promising candidates for the development of high-performance magnetometers due to their high sensitivity, low cost, low power consumption, and small size. The rapid advance of MR sensor technology has opened up a variety of MR sensor applications. These applications are in different areas that require MR sensors with different properties. Future MR sensor development in each of these areas requires an overview and a strategic guide. An MR sensor roadmap (non-recording applications) was therefore developed and made public by the Technical Committee of the IEEE Magnetics Society with the aim to provide an research and development (R&D) guide for MR sensors intended to be used by industry, government, and academia. The roadmap was developed over a three-year period and coordinated by an international effort of 22 taskforce members from ten countries and 17 organizations, including universities, research institutes, and sensor companies. In this paper, the current status of MR sensors for non-recording applications was identified by analyzing the patent and publication statistics. As a result, timescales for MR sensor development were established and critical milestones for sensor parameters were extracted in order to gain insight into potential MR sensor applications (non-recording). Five application areas were identified, and five MR sensor roadmaps were established. These include biomedical applications, flexible electronics, position sensing and human-computer interactions, non-destructive evaluation and monitoring, and navigation and transportation. Each roadmap was analyzed using a logistic growth model, and new opportunities were predicted based on the extrapolated curve, forecast milestones, and professional judgment of the taskforce members. This paper provides a framework for MR sensor technology (non-recording applications) to be used for public and private R&D planning, in order to provide guidance into likely MR sensor applications, products, and services expected in the next 15 years and beyond.

The lateral motion of a magnetic skyrmion, arising because of the skyrmion Hall effect, imposes a number of restrictions on the use of this spin state in the racetrack memory. A skyrmionium is a more promising spin texture for memory applications, since it has zero total topological charge and propagates strictly along a nanotrack. Here, the stability of the skyrmionium, as well as the dependence of its size on the magnetic parameters, such as the Dzyaloshinskii–Moriya interaction and perpendicular magnetic anisotropy, are studied by means of micromagnetic simulations. We propose an advanced method for the skyrmionium nucleation due to a local enhancement of the spin Hall effect. The stability of the skyrmionium being in motion under the action of the spin polarized current is analyzed.

An enhancement of the spin-orbit effects arising on an interface between a ferromagnet (FM) and a heavy metal (HM) is possible through the strong breaking of the structural inversion symmetry in the layered films. Here, we show that an introduction of an ultrathin W interlayer between Co and Ru in Ru/Co/Ru films enables to preserve perpendicular magnetic anisotropy (PMA) and simultaneously induce a large interfacial Dzyaloshinskii-Moriya interaction (iDMI). The study of the spin-wave propagation in the Damon-Eshbach geometry by Brillouin light scattering spectroscopy reveals the drastic increase in the iDMI value with the increase in W thickness (t_W). The maximum iDMI of −3.1 erg/cm² is observed for t_W = 0.24 nm, which is 10 times larger than for the quasi-symmetrical Ru/Co/Ru films. We demonstrate the evidence of the spontaneous field-driven nucleation of isolated skyrmions supported by micromagnetic simulations. Magnetic force microscopy measurements reveal the existence of sub-100-nm skyrmions in the zero magnetic field. The ability to simultaneously control the strength of PMA and iDMI in quasi-symmetrical HM/FM/HM trilayer systems through the interface engineered inversion asymmetry at the nanoscale excites new fundamental and practical interest in ultrathin ferromagnets, which are a potential host for stable magnetic skyrmions.

The interfacial Dzyaloshinskii-Moriya interaction (IDMI) generally arises in “heavy-metal–ferromagnet” (HM-FM) heterostructures due the strong spin-orbit coupling in HMs and plays a crucial role in the nucleation of Dzyaloshinskii domain walls and Skyrmions that can be efficiently moved by spin-orbit torques. We study the IDMI in $\mathrm{W}/\mathrm{Co}\text{−}\mathrm{Fe}\text{−}\mathrm{B}/\mathrm{MgO}/\mathrm{Ta}$ films with perpendicular magnetic anisotropy for different crystal structures and thicknesses of W layers treated by postsputtering annealing at $300°\mathrm{C}$ and $400°\mathrm{C}$. We employ Brillouin light scattering spectroscopy to precisely measure the energy density and sign of the IDMI. We reveal two peaks associated with the IDMI: one for the amorphouslike phase of W, and another for $\alpha \text{−}\mathrm{W}$. The samples with pure $\beta \text{−}\mathrm{W}$ underlayers show the smallest values of IDMI. The sign of the IDMI is positive for all samples with the observed maximum effective and surface values of $D_{\mathrm{eff}}=0.88\mathrm{erg}/{\mathrm{cm}}^2$ and $D_s=0.51\times {10}^{-7}\mathrm{erg}/\mathrm{cm}$, respectively. We report on the oscillating behavior of the IDMI as a function of thickness, which correlates with the surface anisotropy energy demonstrating common spin-orbit coupling and a robust dependence on the structural properties of the materials used. We ascribe the oscillations of the surface anisotropy and the IDMI mainly to the near inversely proportional dependence on the squared interatomic distance between the HM and FM atoms promoted by the thickness-driven crystal phase formation of W.