The paper describes the method for producing WC-10wt%Co hard alloy with 99.6% of the theoretical density and a Vickers hardness of ~1400 HV 0.5. Experimental data on densification dynamics, phase composition, morphology, mechanical properties, and grain size distribution of WC-10%wtCo using spark plasma sintering (SPS) within the range of 1000–1200 °C are presented. The high quality of the product is provided by the advanced method of high-speed powder mixture SPS-consolidation at achieving a high degree of densification with minimal calculated grain growth at 1200 °C.

The application of titanium and its alloys under friction conditions is severely restricted, owing to their poor wear resistance. The paper presents the results of studies of the composition, microstructure, and tribological properties of Ti-TiC-based composite coatings formed on titanium alloys by the electroarc treatment in an aqueous electrolyte using a graphite anode. It has been found that TiC grains have a different stoichiometry and do not contain oxygen. The grain size varies from hundreds of nanometers to tens of micrometers, and the micro-hardness of the treated surface reached the value of 29.5 GPa. The wear resistance of the treated surface increased approximately 40-fold, and the friction coefficient with steel decreased to 0.08–0.3 depending on the friction conditions. The formation of a composite material based on Ti-TiC will contribute to the effective protection of titanium alloys from frictional loads in engineering.

The paper presents a method of obtaining functionally graded material (FGM) of heterogeneous (layered) type based on joined metals Cr-Ti-Fe-Co-Ni-Cu using spark plasma sintering (SPS) technology. The structure, elemental and phase composition of FGM obtained on the basis of joined metals with different values of the temperature coefficient of linear expansion (CTLE) were studied by SEM, EDS and XRD methods with regard to the phase states of the alloy system. Based on the Vickers microhardness data, the evaluation of the mechanical characteristics of FGM in the whole sample body and locally at the contact boundaries of the joined metals was carried out. The results of the study are new and represent a potential for FGM, as well as functionally graded coatings (FGC), which have special physical, chemical and mechanical properties and are highly demanded for the manufacture of structures and products for industrial applications.