At the nanoscale, the synthesis of a random alloy (i.e. without phase segregation, whatever the composition) by chemical synthesis remains a difficult task, even for simple binary type systems. In this context, a unique approach based on the colloidal route is proposed enabling the synthesis of face-centred cubic and monodisperse bimetallic, trimetallic, tetrametallic and pentametallic nanoparticles with diameters around 5 nm as solid solutions. The Fe–Co–Ni–Pt–Ru alloy (and its subsets) is considered a challenging task as each element has fairly different physico-chemical properties. Particles are prepared by temperature-assisted co-reduction of metal acetylacetonate precursors in the presence of surfactants. It is highlighted how the correlation between precursors’ degradation temperatures and reduction potential values of the metal cations is the driving force to achieve a homogeneous distribution of all elements within the nanoparticles.

We report a new and versatile colloidal route towards the synthesis of nanoalloys with controlled size and chemical composition in the solid solution phase (without phase segregation such as core–shell structure or Janus structure) or chemical ordering. The principle of the procedure is based on the correlation between the oxidation–reduction potential of metal cations present in the precursors and the required synthesis temperature to nucleate particles without phase segregation. The procedure is demonstrated via the synthesis of Face Centered Cubic (FCC) Ni_xPt_1−x nanoparticles, which was elaborated by the co-reduction of nickel(II) acetylacetonate and platinum(II) acetylacetonate with 1,2-hexadecanediol in benzyl ether, using oleylamine and oleic acid as surfactants. The chemical composition and solid solution FCC structure of the nanoalloy are demonstrated by crosslinking imaging and chemical analysis using transmission electron microscopy and X-ray diffraction techniques. Whatever the chemical composition inspected, a systematic expansion of the lattice parameters is measured in relation to the respective bulk counterpart.

The aim of the present work is to valorise the brewing industry’s waste, i.e., brewer’s spent grain (BSG), into functional biocarbon for environmental catalysis applications. In this context, cost-effective and environmentally friendly biochar support coated with in-situ-generated Ag-Cu nanocrystals, was developed via the wet impregnation of BSG biomass powder with copper (II) nitrate trihydrate and silver nitrate aqueous solution prior to pyrolysis at moderate temperature (500 °C). Small-size homogenously distributed Ag-Cu nanocrystals (≤80 nm) on the surface of the biochar (Biochar@Ag-Cu) were observed by field emission scanning electron microscope (FESEM) and transmission electron microscope (TEM). Elemental compositions were determined by X-ray photoelectron spectroscopy (XPS) and energy dispersive X-ray analysis (EDX). The crystalline nature of the nanoparticles was confirmed by X-ray powder diffraction (XRD). Information about the thermal stability of the materials and quality were obtained by thermogravimetric analysis (TGA) and Raman, respectively. The potentiality of the Biochar@Ag-Cu catalyst in the field of pollutant removal is demonstrated by taking methyl orange and methylene blue as model dyes. A kinetics study was performed and analyzed by UV–vis spectroscopy. Its highly active catalytic nature is proved by the complete mineralization of the methyl orange dye (100%) through oxidative degradation. The reusability of the catalyst has shown 96% removal efficiency after 3 cycles. The linear plot of −Ln (C_A/C₀) vs. time (R² = 0.9892) reveals that the mineralization of the methyl orange dye follows pseudo-first-order kinetics (k = 0.603 × 10⁻² min⁻¹). A methyl orange + methylene blue dye mixture degradation study has revealed the faster kinetics of the present catalyst towards methylene blue degradation. The current study suggests that BSG Biochar@Ag-Cu can be a potential candidate in contribution towards SDG 6.

Chemical and physical synthesis methods were developed to fabricate high entropy nanoalloys containing up to five metals. TEM was exploited to reveal size and compositional effects on the nanophase diagram of these complex nanostructures.