The additive manufacturing of titanium–niobium–tantalum alloys with nominal chemical compositions Ti–xNb–6Ta (x = 20, 27, 35) by means of laser beam powder bed fusion is reported, and their potential as implant materials is elaborated by mechanical and biological characterization. The properties of dense specimens manufactured in different build orientations and of open porous Ti–20Nb–6Ta specimens are evaluated. Compression tests indicate that strength and elasticity are influenced by the chemical composition and build orientation. The minimum elasticity is always observed in the 90° orientation. It is lowest for Ti–20Nb–6Ta (43.2 ± 2.7 GPa) and can be further reduced to 8.1 ± 1.0 GPa for open porous specimens (p < 0.001). Furthermore, human osteoblasts are cultivated for 7 and 14 days on as-printed specimens and their biological response is compared to that of Ti–6Al–4V. Build orientation and cultivation time significantly affect the gene expression profile of osteogenic differentiation markers. Incomplete cell spreading is observed in specimens manufactured in 0° build orientation, whereas widely stretched cells are observed in 90° build orientation, i.e., parallel to the build direction. Compared to Ti–6Al–4V, Ti–Nb–Ta specimens promote improved osteogenesis and reduce the induction of inflammation. Accordingly, Ti–xNb–6Ta alloys have favorable mechanical and biological properties with great potential for application in orthopedic implants.

Subject-specific finite element (FE) modeling of the mandible bone has recently gained attention for its higher accuracy. A critical modeling factor is including personalized material properties from medical images especially when bone quality has to be respected. However, there is no consensus on the material model for the mandible that realistically estimates the Young's modulus of the bone. Therefore, the present study aims to review FE studies employing heterogeneous material modeling of the human mandible bone, synthesizing these models, investigating their origins, and assessing their risk of bias.

Multifunctional materials have been described to meet the diverse requirements of implant materials for femoral components of uncemented total knee replacements. These materials aim to combine the high wear and corrosion resistance of oxide ceramics at the joint surfaces with the osteogenic potential of titanium alloys at the bone-implant interface. Our objective was to evaluate the biomechanical performance of hybrid material-based femoral components regarding mechanical stress within the implant during cementless implantation and stress shielding (evaluated by strain energy density) of the periprosthetic bone during two-legged squat motion using finite element modeling. The hybrid materials consisted of alumina-toughened zirconia (ATZ) ceramic joined with additively manufactured Ti-6Al-4V or Ti-35Nb-6Ta alloys. The titanium component was modeled with or without an open porous surface structure. Monolithic femoral components of ATZ ceramic or Co-28Cr-6Mo alloy were used as reference. The elasticity of the open porous surface structure was determined within experimental compression tests and was significantly higher for Ti-35Nb-6Ta compared to Ti-6Al-4V (5.2 ± 0.2 GPa vs. 8.8 ± 0.8 GPa, p < 0.001). During implantation, the maximum stress within the ATZ femoral component decreased from 1568.9 MPa (monolithic ATZ) to 367.6 MPa (Ti-6Al-4V/ATZ), 560.9 MPa (Ti-6Al-4V/ATZ with an open porous surface), 474.9 MPa (Ti-35Nb-6Ta/ATZ), and 648.4 MPa (Ti-35Nb-6Ta/ATZ with an open porous surface). The strain energy density increased at higher flexion angles for all models during the squat movement. At ∼90° knee flexion, the strain energy density in the anterior region of the distal femur increased by 25.7 % (Ti-6Al-4V/ATZ), 70.3 % (Ti-6Al-4V/ATZ with an open porous surface), 43.7 % (Ti-35Nb-6Ta/ATZ), and 82.5% (Ti-35Nb-6Ta/ATZ with an open porous surface) compared to monolithic ATZ. Thus, the hybrid material-based femoral component decreases the intraoperative fracture risk of the ATZ part and considerably reduces the risk of stress shielding of the periprosthetic bone.

In the field of dental technology, the length of ceramic pontics is limited to avoid mechanical failure. To reduce thermal-induced residual stress within the ceramic, using smaller subcomponents and subsequent bonding with silicate-based glass solder may be a favorable approach. Thus, the bending strength of zirconia compounds bonded with different silicate-based glass solders was investigated. For this purpose, rectangular specimens made of zirconia were bonded by glass solder. Parameters such as the scarf angle (45° and 90°), two different glass solders, as well as the soldering process (pressure and surface treatment) were varied. All specimens were subjected to quasi-static four-point bending tests according to DIN EN ISO 843-1. Additionally, the quality of the glass solder connection was evaluated using μCT and fractography. In the present study, zirconia compounds were sucessful bonded of zirconia compounds using silicate-based glass solder was. No significant differences in terms of bending strength were observed with respect to the different bonding parameters analyzed. The highest bending strength of 130.6 ± 50.5 MPa was achieved with a 90° scarf angle combined with ethanol treatment of the specimens before soldering and an additional application of a pressure of 2 bars in a dental pressure pot before subsequent soldering. Nevertheless, the bending strengths were highly decreased when compared to monolithic zirconia specimens (993.4 ± 125.5 MPa).

Proximal femur fracture risk depends on subject-specific factors such as bone mineral density and morphological parameters. Here, we aim to analyze the dependency of the femoral strength on sixteen morphological parameters. Therefore, finite-element analyses of 20 human femurs during stumbling and lateral falls on the hip were conducted. Pearson correlation coefficients were calculated and morphological parameters with significant correlations were examined in principal component analysis and linear regression analysis. The dependency of the fracture strength on morphological parameters was more pronounced during lateral falls on the hip compared to stumbling. Significant correlations were observed between the neck shaft angle (r = −0.474), neck diameter (r = 0.507), the true distance between the femoral head center and femoral shaft axis (r = 0.459), and its projected distance on the frontal plane (r = 0.511), greater trochanter height (r = 0.497), and distance between the femoral head center and a plane parallel to the frontal plane containing the projection of the femoral head center to the femoral neck axis (r = 0.669). Principal component analysis was strongly weighted by parameters defining the lever arm during a lateral fall as well as the loaded cross-section in the femoral neck.

Primary stability is crucial for implant osseointegration and the long-term stability of cementless total joint replacements. Biomechanical studies have shown the potential of femoral stems for total knee replacements to reduce micromotions at the bone-implant interface. However, approaches such as focusing on the structural elasticity of the femoral stems are rarely described. Three groups with different femoral stem designs were investigated: group 1: flexible surface stem, group 2: flexible surface stem with open-porous structured lamellas, and group 3: solid stem (reference). The stems were implanted into bone substitute material and dynamically loaded for 1000 cycles. Relative movement and subsidence were measured optically, and axial pull-out forces were determined after dynamic testing. Relative movements increased to 0.10 mm (groups 1 and 2) compared to 0.03 mm (group 3). Subsidence increased to 0.08 mm (group 1) and 0.11 mm (group 2) compared to 0.06 mm (group 3). For each group, subsidence mainly occurred during the first 500 cycles. A similar convergence was observed in the further course. Pull-out forces increased to 1815.0 N (group 1) and 1347.1 N (group 2) compared to 1306.4 N (group 3). The flexible surface stem design resulted in higher relative movements and subsidence, but also exhibited increased pull-out forces. The relative movements were below the critical limit of 0.15 mm and represent a superposition of the elastic deformations of the interacting implant components as well as the micromotion at the bone-implant interface. Therefore, the novel flexible surface stem design appears to offer promising primary implant fixation.