In this study, the surface of commercially pure titanium (Cp-Ti) was covered by a 21–95 µm-thick aluminum oxide layer using plasma electrolytic oxidation. Coating characterization revealed the formation of nodular and granular α- and γ-Al₂O₃ phases with minor amounts of TiAl₂O₅ and Na₂Ti₄O₉ which yielded a maximum 49.0 GPa hardness and 50 N adhesive critical load. The corrosion resistance behavior in 3.5 wt.% NaCl solution of all plasma electrolytic oxidation (PEO) coatings was found to be two orders of magnitude higher compared to bare Ti substrate.

Magnetoresistive Fe–Co based thin film structures were produced using thermionic vacuum arc method. The purpose of this work was to obtain significant magnetic response on different granular combinatorial structures. The Giant Magnetoresistive (GMR) and combination between GMR and Tunneling Magnetoresistive (TMR) properties of the thin film structures were the aim of the work. The proposed method in order to obtain the desired granular structures is based on electron beam emitted by an externally heated cathode, accelerated by a high anodic potential.The work consisted in preparing two sets of samples, first being a combination between Fe–Co as magnetic materials embedded in a Cu matrix, with a total thickness of 200nm. The second structure was a combination between Fe–Co (50%–50%) alloy, embedded in a matrix of Cu combined with MgO with a thickness of 200nm. Both sets of samples were obtained by three simultaneous types of discharges. Because of the substrate positioning in respect with the three anode–cathode systems, different material concentrations were obtained, confirmed by Energy Dispersive Spectroscopy (EDS) measurement results. Structural and morphological properties were investigated using Scanning Electron Microscopy; Atomic Force Microscopy and EDS. Electrical properties of the obtained samples were studied using the 4 point measurement method. The magnetic properties were first studied using a non-destructive optical method called MOKE (Magneto-Optical Kerr Effect). Electrical resistance behavior of the granular type structures was studied for different values of the magnetic field, up to 0.3T, at different values of the sample temperature. The magnetoresistive effect obtained for the two sets of samples varied from 1.5% to 81% in respect with the substrate positioning and sample temperature for a constant magnetic field

Beryllium-deuterium co-deposited layers were obtained using DC magnetron sputtering technique by varying the Ar/D₂ gas mixture composition (10/1; 5/1; 2/1 and 1:1) at a constant deposition rate of 0.06 nm/s, 343 K substrate temperature and 2 Pa gas pressure. The surface morphology of the layers was analyzed using Scanning Electron Microscopy and the layer crystalline structure was analyzed by X-ray diffraction. Rutherford backscattering spectrometry was employed to determine the chemical composition of the layers. D trapping states and inventory quantification were performed using thermal desorption spectroscopy. The morphology of the layers is not influenced by the Ar/D₂ gas mixture composition but by the substrate type and roughness. The increase of the D₂ content during the deposition leads to the deposition of Be-D amorphous layers and also reduces the layer thickness by decreasing the sputtering yield due to the poisoning of the Be target. The D retention in the layers is dominated by the D trapping in low activation binding states and the increase of D₂ flow during deposition leads to a significant build-up of deuterium in these states. Increase of deuterium flow during deposition consequently leads to an increase of D retention in the beryllium layers up to 300%. The resulted Be-D layers release the majority of their D (above 99.99%) at temperatures lower than 700 K.

Reduced activation ferritic and martensitic steel like EUROFER (9Cr-1W) are considered as potential structural materials for the first wall of the future next-generation DEMOnstration Power Station (DEMO) fusion reactor and as a reference material for the International Thermonuclear Experimental Reactor (ITER) test blanket module. The primary motivation of this work is to study the re-deposition of the main constituent materials of EUROFER, namely tungsten (W), iron (Fe), and chromium (Cr), in a DEMO type reactor by producing and analyzing complex W_xCr_yFe_1−x−y layers. The composite layers were produced in laboratory using the thermionic vacuum arc (TVA) method, and the morphology, crystalline structure, elemental composition, and mechanical properties were studied using scanning electron microscopy (SEM), X-ray diffraction (XRD), micro-X-ray fluorescence (micro-XRF), and glow discharge optical emission spectrometry (GDOES), as well as nanoindentation and tribology measurements. The results show that the layer morphology is textured and is highly dependent on sample positioning during the deposition process. The formation of polycrystalline W_xCr_yFe_1−x−y was observed for all samples with the exception of the sample positioned closer to Fe anode during deposition. The crystalline grain size dimension varied between 10 and 20 nm. The composition and thickness of the layers were strongly influenced by the in-situ coating position, and the elemental depth profiles show a non-uniform distribution of Fe and Cr in the layers. The highest hardness was measured for the sample positioned near the Cr anode, 6.84 GPa, and the lowest was 4.84 GPa, measured for the sample positioned near the W anode. The tribology measurements showed an abrasive sliding wear behavior for most of the samples with a reduction of the friction coefficient with the increase of the normal load.