The objective of this study is to determine selected properties of thin-walled rotationally moulded composite parts. Linear low-density polyethylene (LLDPE) filled with quartz flour (QF, 5–35 wt.%) was tested. High-density polyethylene functionalized with maleic anhydride (HDPE-g-MA) was used as a compatibility agent. Polymer samples were prepared with and without the compatibility agent (2 wt.% in relation to the QF content). The study investigated the effect of QF content and HDPE-g-MA on the properties of rotationally moulded parts, including their melt flow rate (MFR), thermal properties (DSC and TGA), thermomechanical properties (VST), mechanical and physical properties, microstructure, and geometry. Results showed that the properties of LLDPE/QF with HDPE-g-MA were significantly higher than those of LLDPE/QF without HDPE-g-MA. It was also found that the compatibility agent improved the composite material’s thermal stability. This improvement was attributed to interactions occurring between the composite material components due to the use of the compatibility agent. In addition to that, microscopic examination demonstrated that the use of HDPE-g-MA improved miscibility of the composite material components. The composite samples containing HDPE-g-MA had better surface geometry.

The objectives of the research was to determine the causes of cracks in pipes made of high-density polyethylene (HDPE) regranulate during their storage. A visual assessment of the cracks was carried out and their fatigue nature was found. Due to the insufficient information on the composition and...

This paper presents the synthesis and physicochemical characterization of a new hybrid composite. Its main goals are evaluating the structure and studying the thermal and mechanical properties of the crosslinked polymeric materials based on varying chemical properties of the compounds. As an organic crosslinking monomer, bisphenol A glycerolate diacrylate (BPA.GDA) was used. Trimethoxyvinylsilane (TMVS) and N-vinyl-2-pyrrolidone (NVP) were used as comonomers and active diluents. The inorganic fraction was the silica in the form of nanoparticles (_NANOSiO₂). The hybrid composites were obtained by the bulk polymerization method using the UV initiator Irqacure 651 with a constant weight ratio of the tetrafunctional monomer BPA.GDA to TMVS or NVP (7:3 wt.%) and different wt.% of silica nanoparticles (0, 1, 3%). The proper course of polymerization was confirmed by the ATR/FTIR spectroscopy and SEM EDAX analysis. In the composites spectra the signals correspond to the C=O groups from NVP at 1672–1675 cm⁻¹, and the vibrations of Si–O–C and Si–O–Si groups at 1053–1100 cm⁻¹ from TMVS and _NANOSiO₂ are visible. Thermal stabilities of the obtained composites were studied by a differential scanning calorimetry DSC. Compared to NVP the samples with TMVS degraded in one stage (422.6–425.3 °C). The NVP-derived materials decomposed in three stages (three endothermic effects on the DSC curves). The addition of _NANOSiO₂ increases the temperature of composites maximum degradation insignificantly. Additionally, the Shore D hardness test was carried out with original metrological measurements of changes in diameter after indentation in relation to the type of material. The accuracy analysis of the obtained test results was based on a comparative analysis of graphical curves obtained from experimental tests. The values of the changes course of similarity in the examined factors, represented by those of characteristic coefficients were determined based on the Fréchet’s theory.

The article presents the results of flammability tests on polymer compositions with wheat bran (WB) as the applied filler, and polyethylene (PE) or poly(butylene succinate) (PBS) as the matrix material. Tests were conducted using samples of compositions containing 10, 30 and 50%wt wheat bran. The test samples were manufactured by injection moulding from compositions previously produced by extrusion pelleting. For comparative purposes, samples made only of the plastics used for the composition matrix were also examined. Flammability tests were carried out in accordance with the recommendations of EN 60695-11-10 Part 11–10 with horizontal and vertical positioning of the sample, using a universal flammability-test-stand. During the flammability tests, changes in the temperature field in the area of the burning sample were also recorded, using a thermal imaging camera. Sample residues after flammability tests were also examined with infrared spectroscopy (FTIR) to assess their thermal destruction. The results of the study showed a significant increase in flammability with bran content for both PE and PBS matrix compositions. Clear differences were also found in the combustion behaviour of the matrix materials alone. Both the burning rate and maximum flame temperature were lower in favour of PBS. PBS compositions with wheat bran also showed lower flammability, compared with their PE matrix counterparts.

The purpose of the article was to determine the influence of calcium carbonate and its modification (with stearic acid) on selected properties of composite polypropylene films and their processing. Polypropylene composites containing, respectively, 5, 10, 20 and 30 wt% filler, were made in twin-screw extrusion process with cold granulation. Films, on the other hand, were produced in single-screw extrusion process (an extruder with a screw with diameter d = 20 mm and ratio l/d = 24) using a flat head (so-called cast films) and a chill roll type cooling and pull-back device. The pull-back rotational speed was selected so as to obtain films of a thickness of approx. 120 µm, irrespectively of the composite being processed. The assessment of the effect of the addition of applied fillers on the magnitude of the melt volume-flow rate (MVR) of polypropylene and the processing characteristic of extrusion process was made (the flow resistance and the variations in volumetric flow rate were determined). It was demonstrated how variations in the processability of polymeric material determined the correction of extrusion process setup parameters (pull-back system speed). The processability of composite films under extensional flow conditions was also determined by evaluating the extensional viscosity (η_E) of the composites. The strength values of composite films were determined under static tension conditions and in puncture tests. The effect of the content and modification of CaCO₃ on the film haze and gloss was also assessed. The investigation carried out has demonstrated a direct effect of the addition of calcium carbonate and its modification on the processability and selected functional properties of composite films. The study has also proved that stearic acid is an effective modifier of processing properties, not only in shear flow conditions, but also under extensional flow conditions – smaller η_E values are exhibited by films containing modified calcium carbonate.

The effect of 10-40 wt% natural fillers (pumpkin husks, bean sorting waste, pine sawdust) on the mechanical properties and flammability of LDPE was examined. As the filler content increased, the hardness slightly increased and the tensile strength and relative elongation decreased. The tensile modulus more than doubled (pumpkin husks, pine sawdust). The linear combustion rate increased unfavorably, but the assumed flammability class HB40 was achieved, except for LDPE filled with 40 wt% pine sawdust (HB75). At the same time, the temperature in the combustion area decreased in the vertical flammability test.