The effect of various cleaning methods on coating morphology and their effectiveness in removing organic contaminants has been studied in this research. Bioactive coatings containing titanium oxides and hydroxyapatite (HAP) were obtained through plasma electrolytic oxidation in aqueous electrolytes and molten salts. The cleaning procedure for the coated surface was performed using autoclave (A), ultraviolet light (UV), radio frequency (RF), air plasma (P), and UV-ozone cleaner (O). The samples were characterized using scanning electron microscopy (SEM) with an EDS detector, X-ray photoelectron spectroscopy (XPS), X-ray phase analysis (XRD), and contact angle (CA) measurements. The conducted studies revealed that the samples obtained from molten salt exhibited a finer crystalline structure morphology (275 nm) compared to those obtained from aqueous electrolytes (350 nm). After applying surface cleaning methods, the carbon content decreased from 5.21 at.% to 0.11 at.% (XPS), which directly corresponds to a reduction in organic contaminations and a decrease in the contact angle as follows: A > UV > P > O. This holds true for both coatings obtained in molten salt (25.3° > 19.5° > 10.5° > 7.5°) and coatings obtained in aqueous electrolytes (35.2° > 28.3° > 26.1° > 16.6°). The most effective and moderate cleaning method is ozone treatment.

Titanium alloys have good biocompatibility and good mechanical properties, making them particularly suitable for dental and orthopedic implants. Improving their osseointegration with human bones is one of the most essential tasks. This can be achieved by developing hydroxyapatite (HA) on the treating surface using the plasma electrolytic oxidation (PEO) method in molten salt. In this study, a coating of titanium oxide-containing HA nanoparticles was formed on Ti-6Al-7Nb alloy by PEO in molten salt. Then, samples were subjected to hydrothermal treatment (HTT) to form HA crystals sized 0.5 to 1 μm. The effect of the current and voltage frequency for the creation of the coating on the morphology, chemical, and phase composition was studied. The anti-corrosion properties of the samples were studied using the potentiodynamic polarization test (PPT) and electrochemical impedance spectroscopy (EIS). An assessment of the morphology of the sample formed at a frequency of 100 Hz shows that the structure of this coating has a uniform submicron porosity, and its surface shows high hydrophilicity and anti-corrosion properties (4.90 × 10⁶ Ohm·cm²). In this work, for the first time, the process of formation of a bioactive coating consisting of titanium oxides and HA was studied by the PEO method in molten salts.