This experimental study investigates the damage effects of nanosecond pulse laser irradiation on silicon solar cells. It encompasses the analysis of transient pulse signal waveform characteristics at the cells’ output and changes in electrical parameters, such as I–V curves before and after laser irradiation under varying laser fluence and background light intensities, and explores the underlying action mechanisms of laser irradiation. The study reveals that as the laser fluence increases up to 4.0 J/cm², the peak value of the transient pulse signal increases by 47.5%, while the pulse width augments by 88.2% compared to the initial transient pulse signal. Furthermore, certain parameters, such as open-circuit voltage, short-circuit current, and peak power obtained, from the measured I–V curve indicate a threshold laser fluence for functional degradation of the solar cell at approximately 1.18 ± 0.42 J/cm². Results obtained from laser irradiation under different background light intensities underscore the significant influence of background light on laser irradiation of silicon cells, with the most severe damage occurring in the absence of light. Moreover, findings from laser irradiation at multiple locations on the silicon cell demonstrate a linear decrease in the output voltage of the silicon cell with an increase in the number of irradiation points.

Laser ablation has been extensively studied by researchers due to its high precision, high efficiency processing capabilities, and wide range of application potentials. However, in a vacuum environment, due to the complexity of experimental conditions, specific application scenarios, and interdisciplinary interferences, more in-depth research on the ablation behavior of high-intensity lasers in vacuum is still insufficient. In response to such issues, experiments were conducted on titanium alloy perforation using a nanosecond laser in a vacuum environment. The variations in ablation depth and volume as functions of pulse energy, pulse number, and defocus were investigated. Both the depth and volume ablation efficiencies were calculated, and the three-dimensional morphology of the ablation holes was captured. Additionally, the ablation plume was observed to support the research conclusions. The results indicate that within the number of high-intensity laser pulses, the ablation depth per pulse can be increased by more than four times, and the average ablation volume per pulse can reach 0.97 µm³/µJ. The enhanced sputtering of molten material during the multi-pulse laser ablation process in a vacuum environment is identified as the primary factor contributing to the increased ablation efficiency. With the advancement of science and technology and the growing demand for applications, this research is crucial for the further development of fields such as space exploration and technology, advanced manufacturing technology, and basic scientific research.

In the process of pulsed laser drilling, the material properties in the heat-affected zone will change due to the thermal effect of the laser. To study the effect of this change on the material tensile strength, two lasers were used to punch the standard 6061 aluminum alloy specimens with millisecond and nanosecond pulse widths, and then the tensile test was carried out on the standard specimens with a tensile tester to measure the ultimate tensile strength of the aluminum alloy. Finally, the micro-morphology of the fracture was photographed by scanning electron microscopy (SEM), and the fracture mechanism of the aluminum alloy was analyzed. The experimental results show that the relationship between the rate of intensity change induced by the millisecond laser and the ablation area ratio is more linear than that of the nanosecond laser; with the increase of ablation area ratio, the rate of intensity changes induced by the nanosecond and millisecond lasers becomes increasingly closer; three types of fractures are produced with two types of laser ablation; the plasticity of the material rapidly decreases with laser drilling, and the main reason for decrease in plasticity was stress concentration. This study provides an important point of reference for how to ensure the strength and plasticity of the components after laser drilling.

Laser propulsion is a new conceptual technology that drives spacecraft and possesses advantages such as high specific impulse, large payload ratio, and low launch cost. It has potential applications in diverse areas, such as space debris mitigation and removal, microsatellite attitude control, and orbital maneuvering. Liquid pulse laser propulsion has notable advantages among the various laser propulsion systems. We review the concept and the theory of liquid laser propulsion. Then, we categorize the current state of research based on three types of propellants—non-energetic liquids, energetic liquids, and liquid metals—and provide an analysis of the propulsion characteristics arising from the laser ablation of liquids such as water, glycidyl azide polymer (GAP), hydroxylammonium nitrate (HAN), and ammonium dinitramide (ADN). We also discuss future research directions and challenges of pulsed liquid laser propulsion. Although experiments have yielded encouraging outcomes due to the distinctive properties of liquid propellants, continued investigation is essential to ensure that this technology performs reliably in actual aerospace applications. Consistent results under both spatial and ground conditions remain a key research content for fully realizing its potential.

The Single-event Transient (SET) pulses triggered at the drain of NMOS with T-gate at various striking positions after heavy-ion striking are studied using Technical Computer Aided Design (TCAD) simulation based on the 130 nm Fully Depleted Silicon on insulator (SOI) technology. Based on this technology, we design Flip-Flop chain circuits with different gate widths and gate lengths. The heavy ion irradiation experiment of the device is carried out.